DFL36-XH
Forever
DFL36-XH is a wear-resistant compound made of Polycarbonate (PC) resin with 30% glass fiber and 15% PTFE. This grade is specifically designed to provide enhanced wear resistance in various applications.
General | ||||||
Form |
| |||||
Filler | 30 % Glass Fiber | 15 % PTFE | ||||
Feature | Abrasion Resistant | Structural |
| |||
Usage | ||||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.54 g/cm³ | ASTM D792 | ||||
Mold Shrinkage, Flow(24 hrs) | 0.2 - 0.3 % | ASTM D955 | ||||
Mold Shrinkage, XFlow(24 hrs) | 0.5 % | ASTM D955 | ||||
Wear Factor Washer | 22 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual | ||||
Dynamic Cof | 0.46 | ASTM D3702 Modified: Manual | ||||
Static Cof | 0.41 | ASTM D3702 Modified: Manual |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 923 J/m | ASTM D4812 |
80*10*4;23 °C | 55 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 197 J/m | ASTM D256 |
80*10*4;23 °C | 16 kJ/m² | ISO 180/1A |
Tensile Stress, Yield | ||
123 MPa | ASTM D638 | |
118 MPa | ISO 527 | |
Tensile Stress, Break | ||
123 MPa | ASTM D638 | |
118 MPa | ISO 527 | |
Tensile Strain, Yield | ||
2.6 % | ASTM D638 | |
2.6 % | ISO 527 | |
Tensile Strain, Break | ||
2.8 % | ASTM D638 | |
2.7 % | ISO 527 | |
Tensile Modulus | ||
5 mm/min | 9580 MPa | ASTM D638 |
1 mm/min | 9080 MPa | ISO 527 |
Flexural Stress | ||
186 MPa | ASTM D790 | |
185 MPa | ISO 178 | |
Flexural Modulus | ||
8610 MPa | ASTM D790 | |
8340 MPa | ISO 178 | |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 3 mm) | V-1 | UL 94 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 143 °C | ASTM D648 |
Processing | Nominal Value |
Drying Temperature<Injection> | 120 °C |
Drying Time<Injection> | 4 hrs |
Maximum Moisture Content<Injection> | 0.02 % |
Melt Temperature<Injection> | 305 - 325 °C |
Front, Zone 3 Temperature<Injection> | 320 - 330 °C |
Middle, Zone 2 Temperature<Injection> | 310 - 320 °C |
Rear, Zone 1 Temperature<Injection> | 295 - 305 °C |
Mold Temperature<Injection> | 80 - 110 °C |
Back Pressure<Injection> | 0.2 - 0.3 MPa |
Screw Speed <Injection> | 30 - 60 rpm |
DFL36-XH is a wear-resistant compound made of Polycarbonate (PC) resin with 30% glass fiber and 15% PTFE. This grade is specifically designed to provide enhanced wear resistance in various applications.
General | ||||||
Form |
| |||||
Filler | 30 % Glass Fiber | 15 % PTFE | ||||
Feature | Abrasion Resistant | Structural |
| |||
Usage | ||||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.54 g/cm³ | ASTM D792 | ||||
Mold Shrinkage, Flow(24 hrs) | 0.2 - 0.3 % | ASTM D955 | ||||
Mold Shrinkage, XFlow(24 hrs) | 0.5 % | ASTM D955 | ||||
Wear Factor Washer | 22 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual | ||||
Dynamic Cof | 0.46 | ASTM D3702 Modified: Manual | ||||
Static Cof | 0.41 | ASTM D3702 Modified: Manual |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 923 J/m | ASTM D4812 |
80*10*4;23 °C | 55 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 197 J/m | ASTM D256 |
80*10*4;23 °C | 16 kJ/m² | ISO 180/1A |
Tensile Stress, Yield | ||
123 MPa | ASTM D638 | |
118 MPa | ISO 527 | |
Tensile Stress, Break | ||
123 MPa | ASTM D638 | |
118 MPa | ISO 527 | |
Tensile Strain, Yield | ||
2.6 % | ASTM D638 | |
2.6 % | ISO 527 | |
Tensile Strain, Break | ||
2.8 % | ASTM D638 | |
2.7 % | ISO 527 | |
Tensile Modulus | ||
5 mm/min | 9580 MPa | ASTM D638 |
1 mm/min | 9080 MPa | ISO 527 |
Flexural Stress | ||
186 MPa | ASTM D790 | |
185 MPa | ISO 178 | |
Flexural Modulus | ||
8610 MPa | ASTM D790 | |
8340 MPa | ISO 178 | |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 3 mm) | V-1 | UL 94 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 143 °C | ASTM D648 |
Processing | Nominal Value |
Drying Temperature<Injection> | 120 °C |
Drying Time<Injection> | 4 hrs |
Maximum Moisture Content<Injection> | 0.02 % |
Melt Temperature<Injection> | 305 - 325 °C |
Front, Zone 3 Temperature<Injection> | 320 - 330 °C |
Middle, Zone 2 Temperature<Injection> | 310 - 320 °C |
Rear, Zone 1 Temperature<Injection> | 295 - 305 °C |
Mold Temperature<Injection> | 80 - 110 °C |
Back Pressure<Injection> | 0.2 - 0.3 MPa |
Screw Speed <Injection> | 30 - 60 rpm |