527UV NC010-XH
Forever
527UV NC010-XH is a linear polymer with no side chains, high density, and high crystallinity. It is an engineering plastic with excellent comprehensive performance. It has good physical, mechanical, and chemical properties, especially excellent friction resistance.
General | ||||
Form |
| |||
Feature |
|
|
| |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.42 g/cm³ | ISO 1183 | ||
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) | 15 g/10min | ISO 1133 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 13 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | 1.9 % | ISO 294-4 | ||
Molding Shrinkage, Flow | 2.0 % | ISO 294-4 | ||
Water Absorption(24 hr;23 °C) | 0.50 % | ISO 62 | ||
Water Absorption, Saturation(23 °C;2 mm) | 1.2 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C;2 mm) | 0.20 % | ISO 62 | ||
Rockwell Hardness, M-Scale | 92 | ISO 2039-2 | ||
Rockwell Hardness, R-Scale | 120 | ISO 2039-2 | ||
Emission | < 8.00 mg/kg | VDA 275 | ||
Fogging, G-value, condensate | 2.0E-4 g | ISO 6452 | ||
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 3100 MPa | ISO 527-2 |
Tensile Stress, Yield | 70.0 MPa | ISO 527-2 |
Tensile Strain, Yield | 17 % | ISO 527-2 |
Nominal Tensile Strain at Break | 30 % | ISO 527-2 |
Flexural Modulus | 3000 MPa | ISO 178 |
Flexural Stress 3.5% Strain |
77.0 MPa 78.0 MPa | ISO 178 |
Poisson's Ratio | 0.37 | No Standard |
C harpy Notched Impact Strength -30 °C 23 °C |
8.0 kJ/m² 9.0 kJ/m² | ISO 179 1eA |
C harpy Unnotched Impact Strength -30 °C 23 °C |
260 kJ/m² 260 kJ/m² | ISO 179 1eU |
Notched Izod Impact Strength -40 °C 23 °C |
8.0 kJ/m² 8.0 kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
163 °C 95.0 °C |
ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature |
160 °C 174 °C |
ISO 306/B50 ISO 306/A50 |
Melting Point(10 °C/min) | 178 °C | ISO 11357-3 |
CLTE, Flow | 1.1E-4 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse | 1.2E-4 cm/cm/°C | ISO 11359-2 |
Annealing Temperature | 160 °C | |
Annealing Time - Optional | 30.0 min/mm | |
Burning rate(1 mm;FMVSS 302) | 21 mm/min | ISO 3795 |
Flame Rating(0.8 mm) | HB | IEC 60695-11- 10;UL 94;IEC 60695-11-20 |
FMVSS Flammability | B | FMVSS 302 |
Fogging, F-value, refraction, Assessed, Min | 90 % | ISO 6452 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 2.0E+13 ohms | IEC 62631-3-2 |
Volume Resistivity | > 1E+11 ohms ·cm | IEC 62631-3-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
3.80 3.80 | IEC 62631-2-1 |
Dissipation Factor 100 Hz 1.0e+6 Hz |
2.1E-3 5.6E-3 | IEC 62631-2-1 |
Comparative Tracking Index | 600 V | IEC 60112 |
527UV NC010-XH is a linear polymer with no side chains, high density, and high crystallinity. It is an engineering plastic with excellent comprehensive performance. It has good physical, mechanical, and chemical properties, especially excellent friction resistance.
General | ||||
Form |
| |||
Feature |
|
|
| |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.42 g/cm³ | ISO 1183 | ||
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) | 15 g/10min | ISO 1133 | ||
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 13 cm³/10 min | ISO 1133 | ||
Molding Shrinkage, Across Flow | 1.9 % | ISO 294-4 | ||
Molding Shrinkage, Flow | 2.0 % | ISO 294-4 | ||
Water Absorption(24 hr;23 °C) | 0.50 % | ISO 62 | ||
Water Absorption, Saturation(23 °C;2 mm) | 1.2 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C;2 mm) | 0.20 % | ISO 62 | ||
Rockwell Hardness, M-Scale | 92 | ISO 2039-2 | ||
Rockwell Hardness, R-Scale | 120 | ISO 2039-2 | ||
Emission | < 8.00 mg/kg | VDA 275 | ||
Fogging, G-value, condensate | 2.0E-4 g | ISO 6452 | ||
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 3100 MPa | ISO 527-2 |
Tensile Stress, Yield | 70.0 MPa | ISO 527-2 |
Tensile Strain, Yield | 17 % | ISO 527-2 |
Nominal Tensile Strain at Break | 30 % | ISO 527-2 |
Flexural Modulus | 3000 MPa | ISO 178 |
Flexural Stress 3.5% Strain |
77.0 MPa 78.0 MPa | ISO 178 |
Poisson's Ratio | 0.37 | No Standard |
C harpy Notched Impact Strength -30 °C 23 °C |
8.0 kJ/m² 9.0 kJ/m² | ISO 179 1eA |
C harpy Unnotched Impact Strength -30 °C 23 °C |
260 kJ/m² 260 kJ/m² | ISO 179 1eU |
Notched Izod Impact Strength -40 °C 23 °C |
8.0 kJ/m² 8.0 kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
163 °C 95.0 °C |
ISO 75-2/B ISO 75-2/A |
Vicat Softening Temperature |
160 °C 174 °C |
ISO 306/B50 ISO 306/A50 |
Melting Point(10 °C/min) | 178 °C | ISO 11357-3 |
CLTE, Flow | 1.1E-4 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse | 1.2E-4 cm/cm/°C | ISO 11359-2 |
Annealing Temperature | 160 °C | |
Annealing Time - Optional | 30.0 min/mm | |
Burning rate(1 mm;FMVSS 302) | 21 mm/min | ISO 3795 |
Flame Rating(0.8 mm) | HB | IEC 60695-11- 10;UL 94;IEC 60695-11-20 |
FMVSS Flammability | B | FMVSS 302 |
Fogging, F-value, refraction, Assessed, Min | 90 % | ISO 6452 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 2.0E+13 ohms | IEC 62631-3-2 |
Volume Resistivity | > 1E+11 ohms ·cm | IEC 62631-3-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
3.80 3.80 | IEC 62631-2-1 |
Dissipation Factor 100 Hz 1.0e+6 Hz |
2.1E-3 5.6E-3 | IEC 62631-2-1 |
Comparative Tracking Index | 600 V | IEC 60112 |
Resin Pellets