C6600-XH
FOREVER
C6600-XH is an exceptional polycarbonate and acrylonitrile butadiene styrene (PC/ABS) blend produced using the latest technology.
It is a non-chlorinated/brominated flame retardant grade engineered to have good hydrolytic stability, impact strength, balanced flow, and excellent chemical resistance.
C6600-XH can be easily injection-molded and molded into a range of products in opaque colors. It is also UL94 V0@1.5mm and 5VB@2.0mm flame rated, making it a safer product. With its outstanding properties, C6600-XH is an ideal choice for a range of applications in the electronic, lighting, and automotive industries.
General | |||||||
Form |
| ||||||
Feature | Non-Brominated Ductile | Non-Chlorinated Hydrolysis Resistance | Excellent Processability | ||||
| |||||||
Automotive Under The | Industrial Applications | Electronic Displays | |||||
Hood |
| Lawn And Garden | |||||
Uses | Equipment | ||||||
Nuclear Power
|
| Aerospace Automotive Interior | |||||
|
| Outdoor | |||||
Physical | Nominal Value | Test Method | |||||
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |||||
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) | 22 g/10min | ASTM D1238 | |||||
Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.60 % | Internal Method | |||||
Water Absorption(24 hr) | 0.11 % | ASTM D570 | |||||
Mechanical | Nominal Value | Test Method | |||||
Tensile Modulus(50 mm/min) | 3000 MPa | ASTM D638 | |||||
Tensile Strength, Yield(50 mm/min;Type I) | 63.0 MPa | ASTM D638 | |||||
Tensile Strength, Break(50 mm/min;Type I) | 49.0 MPa | ASTM D638 | |||||
Tensile Elongation, Yield(50 mm/min;Type I) | 4.0 % | ASTM D638 | |||||
Tensile Elongation, Break(50 mm/min;Type I) | 80 % | ASTM D638 | |||||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2620 MPa | ASTM D790 | |||||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 94.0 MPa | ASTM D790 | |||||
Notched Izod Impact(23 °C) | 550 J/m | ASTM D256 | |||||
Instrumented Dart Impact, Total Energy | ASTM D3763 | ||||||
-30 °C | 51.0 J | ||||||
23 °C | 51.0 J | ||||||
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm |
98.0 °C 83.0 °C 90.0 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 99.0 °C | ASTM D1525 |
RTI Elec | 80.0 °C | UL 746 |
RTI Imp | 70.0 °C | UL 746 |
RTI Str | 80.0 °C | UL 746 |
Flame Rating 0.75 mm 1.5 mm 2 mm |
V-2 V-0 5VB | UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 Ohms·cm | IEC 60093 |
Electric Strength, in Oil(3.2 mm) | 17 kV/mm | IEC 60243-1 |
Relative Permittivity 50 Hz 60 Hz 1.0e+6 Hz |
2.70 2.70 2.70 | IEC 60250 |
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
4.0E-3 4.0E-3 6.0E-3 | IEC 60250 |
Processing | Nominal Value |
Drying Temperature<Injection> | 80 - 90 °C |
Drying Time<Injection> | 3.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.040 % |
Suggested Shot Size<Injection> | 30 - 80 % |
Rear Temperature<Injection> | 220 - 255 °C |
Middle Temperature<injection> | 220 - 275 °C |
Front Temperature<Injection> | 245 - 275 °C |
Nozzle Temperature<Injection> | 245 - 275 °C |
Processing Temp, Melt<Injection> | 245 - 275 °C |
Mold Temperature<Injection> | 60 - 80 °C |
Back Pressure<Injection> | 0.300 - 0.700 MPa |
Screw Speed<Injection> | 40 - 70 rpm |
Vent Depth<Injection> | 0.038 - 0.076 mm |
Drying Time, Cumulative<Injection> | 8 hrs |
C6600-XH is an exceptional polycarbonate and acrylonitrile butadiene styrene (PC/ABS) blend produced using the latest technology.
It is a non-chlorinated/brominated flame retardant grade engineered to have good hydrolytic stability, impact strength, balanced flow, and excellent chemical resistance.
C6600-XH can be easily injection-molded and molded into a range of products in opaque colors. It is also UL94 V0@1.5mm and 5VB@2.0mm flame rated, making it a safer product. With its outstanding properties, C6600-XH is an ideal choice for a range of applications in the electronic, lighting, and automotive industries.
General | |||||||
Form |
| ||||||
Feature | Non-Brominated Ductile | Non-Chlorinated Hydrolysis Resistance | Excellent Processability | ||||
| |||||||
Automotive Under The | Industrial Applications | Electronic Displays | |||||
Hood |
| Lawn And Garden | |||||
Uses | Equipment | ||||||
Nuclear Power
|
| Aerospace Automotive Interior | |||||
|
| Outdoor | |||||
Physical | Nominal Value | Test Method | |||||
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |||||
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) | 22 g/10min | ASTM D1238 | |||||
Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.60 % | Internal Method | |||||
Water Absorption(24 hr) | 0.11 % | ASTM D570 | |||||
Mechanical | Nominal Value | Test Method | |||||
Tensile Modulus(50 mm/min) | 3000 MPa | ASTM D638 | |||||
Tensile Strength, Yield(50 mm/min;Type I) | 63.0 MPa | ASTM D638 | |||||
Tensile Strength, Break(50 mm/min;Type I) | 49.0 MPa | ASTM D638 | |||||
Tensile Elongation, Yield(50 mm/min;Type I) | 4.0 % | ASTM D638 | |||||
Tensile Elongation, Break(50 mm/min;Type I) | 80 % | ASTM D638 | |||||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2620 MPa | ASTM D790 | |||||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 94.0 MPa | ASTM D790 | |||||
Notched Izod Impact(23 °C) | 550 J/m | ASTM D256 | |||||
Instrumented Dart Impact, Total Energy | ASTM D3763 | ||||||
-30 °C | 51.0 J | ||||||
23 °C | 51.0 J | ||||||
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm |
98.0 °C 83.0 °C 90.0 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 99.0 °C | ASTM D1525 |
RTI Elec | 80.0 °C | UL 746 |
RTI Imp | 70.0 °C | UL 746 |
RTI Str | 80.0 °C | UL 746 |
Flame Rating 0.75 mm 1.5 mm 2 mm |
V-2 V-0 5VB | UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 Ohms·cm | IEC 60093 |
Electric Strength, in Oil(3.2 mm) | 17 kV/mm | IEC 60243-1 |
Relative Permittivity 50 Hz 60 Hz 1.0e+6 Hz |
2.70 2.70 2.70 | IEC 60250 |
Dissipation Factor 50 Hz 60 Hz 1.0e+6 Hz |
4.0E-3 4.0E-3 6.0E-3 | IEC 60250 |
Processing | Nominal Value |
Drying Temperature<Injection> | 80 - 90 °C |
Drying Time<Injection> | 3.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.040 % |
Suggested Shot Size<Injection> | 30 - 80 % |
Rear Temperature<Injection> | 220 - 255 °C |
Middle Temperature<injection> | 220 - 275 °C |
Front Temperature<Injection> | 245 - 275 °C |
Nozzle Temperature<Injection> | 245 - 275 °C |
Processing Temp, Melt<Injection> | 245 - 275 °C |
Mold Temperature<Injection> | 60 - 80 °C |
Back Pressure<Injection> | 0.300 - 0.700 MPa |
Screw Speed<Injection> | 40 - 70 rpm |
Vent Depth<Injection> | 0.038 - 0.076 mm |
Drying Time, Cumulative<Injection> | 8 hrs |