Transparent PC/ABS Plastics Raw Material Granules PC/ABS Compound Resin Pellets

Form

      Resin Pellets

Feature

Chemical Resistant

Non-Chlorinated

 Hydrolysis Resistance

 Thin Wall

Non-Brominated & Non- Chlorinated Flame

 Retardant

Usage                                        Healthcare

 Electrical

 Building and Construction

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.19

1.19 g/cm³

ASTM D792

ISO 1183

Melt Flow Rate[MFR](260 °C;2.16 kgf)

22.5 g/10min

ASTM D1238

Water Absorption(23 °C;saturated)

0.2 %

ISO 62-1

Moisture Absorption(50% RH;23 °C)

0.1 %

ISO 62

Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C)

21 cm³/10 min

ISO 1133

Izod Impact, Notched

23 °C

-30 °C

600 J/m

120 J/m

ASTM D256

Instrumented Dart Impact, Total Energy(23 °C)

63 J

ASTM D3763

Notched Izod Impact Strength

notched;80*10*3;23 °C 0

notched;80*10*3;-30 °C 0

15 kJ/m²

10 kJ/m²

ISO 180/1A

C harpy Impact, V-Notched

23 °C;Edgew;80*10*3;sp =62mm 0

-30 °C;Edgew;80*10*3;sp =62mm 0

15 kJ/m²

10 kJ/m²

ISO 179 1eA

Tensile Stress, Yield

50 mm/min;Type I

64 MPa

ASTM D638

50 mm/min

61 MPa

ISO 527

Tensile Stress, Break

50 mm/min;Type I

54 MPa

ASTM D638

50 mm/min

51 MPa

ISO 527

Tensile Strain, Yield

50 mm/min;Type I

4 %

ASTM D638

50 mm/min

4 %

ISO 527

Tensile Strain, Break

50 mm/min;Type I

90 %

ASTM D638

50 mm/min

90 %

ISO 527

Tensile Modulus

50 mm/min

2900 MPa

ASTM D638

1 mm/min

2700 MPa

ISO 527

Flexural Stress, Yield

1.3 mm/min;50 mm;span

100 MPa

ASTM D790

2 mm/min

100 MPa

ISO 178

Flexural Modulus

1.3 mm/min;50 mm;span

2700 MPa

ASTM D790

2 mm/min

2500 MPa

ISO 178

UL Recognized

≥ 3 mm

≥ 2 mm

≥ 1.2 mm

5VA

5VB

V-0

UL 94

Vicat Softening Temperature

Rate B/50

102 °C

ASTM D1525

Rate B/50

102 °C

ISO 306

Rate B/120

102 °C

ISO 306

Heat Deflection Temperature[HDT], Unannealed

0.45 MPa;3.2 mm

3.2 mm;1.82 MPa 0.45 MPa;6.4 mm

1.82 MPa;6.4 mm

94 °C

84 °C

98 °C

90 °C

ASTM D648

CTE, Flow

-40 - 40 °C

7.5e-05 1/°C

ASTM E831

-40 - 40 °C

7.5e-05 1/°C

ISO 11359-2

CTE, XFlow

-40 - 40 °C

7.5e-05 1/°C

ASTM E831

-40 - 40 °C

7.5e-05 1/°C

ISO 11359-2

Thermal Conductivity

0.2 W/m-K

ISO 8302

Ball Pressure Test(75°C +/- 2°C)

Pass

IEC 60695-10-2

HDT/Af(1.8)

84 °C

ISO 75/Af

Relative Temp Index, Elec

90 °C

UL 746B

Relative Temp Index, Mechanical with Impact

90 °C

UL 746B

Relative Temp Index, Mechanical without Impact

90 °C

UL 746B

Drying Temperature<Injection>

80 - 90 °C

Drying Time<Injection>

3 - 4 hrs

Drying Time, Cumulative<Injection>

8 hrs

Maximum Moisture Content<Injection>

0.04 %

Melt Temperature<Injection>

245 - 275 °C

Nozzle Temperature<Injection>

245 - 275 °C

Front, Zone 3 Temperature<Injection>

245 - 275 °C

Middle, Zone 2 Temperature<Injection>

220 - 265 °C

Rear, Zone 1 Temperature<Injection>

220 - 255 °C

Mold Temperature<Injection>

60 - 80 °C

Back Pressure<Injection>

0.3 - 0.7 MPa

Screw Speed <Injection>

40 - 70 rpm

Shot To Cylinder Size<Injection>

30 - 80 %

Vent Depth <Injection>

0.038 - 0.076 mm