HR5007A-XH
Forever
HR5007A-XH is a thermoplastic plastic made of PC and ABS alloys. Combining the excellent properties of two materials. It can be widely used in automotive accessories, lampshades, handles, and other components. Its comprehensive performance is good, with high impact strength, chemical stability, and good electrical properties.
General | ||||
Form |
| |||
Feature |
|
| ||
Usage |
|
|
| |
Physical Nominal Value | Test Method | |||
Density / Specific Gravity 1.14 g/cm³ | ASTM D792 | |||
Melt Mass-Flow Rate, MFR(250 °C;2.16 kg) 5.3 g/10min | ASTM D1238 | |||
Molding Shrinkage - Flow, Injection Molded(23 °C;3.2 mm) | 0.50 - 0.80 % | ASTM D955 | ||
Mechanical Nominal Value | Test Method | |||
Tensile Strength, Yield, Injection molded(50 mm/min;23 56.9 MPa °C;3.2 mm) | ASTM D638 | |||
Tensile Elongation, Break, Injection Molded(50 mm/min;23 °C;3.2 mm) | > 100 % | ASTM D638 | ||
Flexural Modulus, Injection Molded(10 mm/min;23 °C;3.22110 MPa mm) | ASTM D790 | |||
Flexural Strength, Injection Molded(10 mm/min;23 °C;3.277.5 MPa mm;Span) | ASTM D790 | |||
Notched Izod Impact, Injection Molded -30 °C;3.2 mm 23 °C;3.2 mm |
490 J/m 640 J/m | ASTM D256 | ||
Thermal Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa;6.4 mm) | 113 °C | ASTM D648 | ||
RTI Elec 60.0 °C | UL 746 | |||
RTI Imp 60.0 °C | UL 746 | |||
RTI Str 60.0 °C | UL 746 | |||
Flame Rating 1.6 mm 3 mm |
HB HB | UL 94 | ||
Processing | Nominal Value |
Drying Temperature<Injection> | 80 - 100 °C |
Drying Time<Injection> | 4.0 - 6.0 hr |
Suggested Max Moisture<Injection> | 0.020 % |
Rear Temperature<Injection> | 240 - 270 °C |
Middle Temperature<injection> | 245 - 275 °C |
Front Temperature<Injection> | 245 - 275 °C |
Nozzle Temperature<Injection> | 245 - 275 °C |
Processing Temp, Melt<Injection> | 250 - 275 °C |
Mold Temperature<Injection> | 50 - 70 °C |
Screw Speed <Injection> | 40 - 70 rpm |
HR5007A-XH is a thermoplastic plastic made of PC and ABS alloys. Combining the excellent properties of two materials. It can be widely used in automotive accessories, lampshades, handles, and other components. Its comprehensive performance is good, with high impact strength, chemical stability, and good electrical properties.
General | ||||
Form |
| |||
Feature |
|
| ||
Usage |
|
|
| |
Physical Nominal Value | Test Method | |||
Density / Specific Gravity 1.14 g/cm³ | ASTM D792 | |||
Melt Mass-Flow Rate, MFR(250 °C;2.16 kg) 5.3 g/10min | ASTM D1238 | |||
Molding Shrinkage - Flow, Injection Molded(23 °C;3.2 mm) | 0.50 - 0.80 % | ASTM D955 | ||
Mechanical Nominal Value | Test Method | |||
Tensile Strength, Yield, Injection molded(50 mm/min;23 56.9 MPa °C;3.2 mm) | ASTM D638 | |||
Tensile Elongation, Break, Injection Molded(50 mm/min;23 °C;3.2 mm) | > 100 % | ASTM D638 | ||
Flexural Modulus, Injection Molded(10 mm/min;23 °C;3.22110 MPa mm) | ASTM D790 | |||
Flexural Strength, Injection Molded(10 mm/min;23 °C;3.277.5 MPa mm;Span) | ASTM D790 | |||
Notched Izod Impact, Injection Molded -30 °C;3.2 mm 23 °C;3.2 mm |
490 J/m 640 J/m | ASTM D256 | ||
Thermal Nominal Value | Test Method | |||
Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa;6.4 mm) | 113 °C | ASTM D648 | ||
RTI Elec 60.0 °C | UL 746 | |||
RTI Imp 60.0 °C | UL 746 | |||
RTI Str 60.0 °C | UL 746 | |||
Flame Rating 1.6 mm 3 mm |
HB HB | UL 94 | ||
Processing | Nominal Value |
Drying Temperature<Injection> | 80 - 100 °C |
Drying Time<Injection> | 4.0 - 6.0 hr |
Suggested Max Moisture<Injection> | 0.020 % |
Rear Temperature<Injection> | 240 - 270 °C |
Middle Temperature<injection> | 245 - 275 °C |
Front Temperature<Injection> | 245 - 275 °C |
Nozzle Temperature<Injection> | 245 - 275 °C |
Processing Temp, Melt<Injection> | 250 - 275 °C |
Mold Temperature<Injection> | 50 - 70 °C |
Screw Speed <Injection> | 40 - 70 rpm |
Resin Pellets