Rubber Raw Material Polypropylene Plastic Raw Material PA6 Particle Native Polycarbonate Resin

Form

Resin Pellets

Usage

Furniture

Electrical

White Goods & Small  Appliances

 Wire & Cable Applications

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.38 g/cm³

ISO 1183

Water Absorption(24 hr, 23°C)

0.9 %

ISO 62

Tensile Modulus

1 mm/min/dry

1 mm/min/conditioned

11000 MPa

6500 MPa

ISO 527-1/-2

Stress at break

dry

conditioned

175 MPa

110 MPa

ISO 527-1/-2

Strain at break

dry

conditioned

3.2 %

7 %

ISO 527-1/-2

Flexural Modulus

2 mm/min/dry

2 mm/min/conditioned

10000 MPa

6500 MPa

ISO 178

Flexural Strength

2 mm/min/dry

2 mm/min/conditioned

300 MPa

155 MPa

ISO 178

C harpy Impact Strength, Unnotched

dry; 23 ℃

conditioned; 23

90 kJ/m²

95 kJ/m²

ISO 179 1eU

C harpy Notched Impact Strength

dry; 23 ℃

conditioned; 23

12 kJ/m²

20 kJ/m²

ISO 179 1eA

Notched Izod Impact Strength

dry; 23 ℃

conditioned; 23

15 kJ/m²

28 kJ/m²

ISO 180/1A

Thermal

Nominal Value

Test Method

Melting Temperature(10°C/min)

222 °C

ISO 11357-1

Temp. of deflection under load(1.8 MPa)

210 °C

ISO 75

Flammability

0.75 mm

1.5 mm

3 mm

HB

HB

HB

UL 94

Glow-Wire Flammability, GWFI(1.5 mm)

650 °C

IEC 60695-2-12

Volume Resistivity

1E+11 ohms ·cm

IEC 62631-3-1

Surface Resistivity

1E+014 Ohms

IEC 62631-3-1

Comparative Tracking Index(Solution A)

400 V

IEC 60112

Processing

Nominal Value

Drying Temperature(除湿干燥机)

80 °C

Drying Time(除湿干燥机)

2 - 4 h

Suggested Max Moisture

0.2 %

Rear Temperature

230 - 235 °C

Middle Temperature

235 - 240 °C

Front Temperature

240 - 250 °C

Blow Molding Mold Temperature

60 - 90 °C