Recycled Polycarbonate (PC) Resin with High Modulus, Low Warpage, And Good Ductility of Glass Fibers

Form

Resin Pellets

Filler

20 % Glass Fiber

Feature

35 % Pcr

Pcr

 Low Warpage                

Non-Brominated & Non-

Chlorinated Flame            

Retardant

Good Hardness

Non-Chlorinated

Structural

Enhanced Ductility

Usage

Consumer

 Electrical

 Building and Construction

Physical

Nominal Value

Test Method

Melt Flow Rate[MFR]

300 °C;1.2 kgf

300 °C;2.16 kgf

12 g/10min

25 g/10min

ASTM D1238

Density / Specific Gravity

1.35 g/cm³

ASTM D792

Mold Shrinkage, Flow(24 hrs)

0.2 - 0.4 %

ASTM D955

Mold Shrinkage, XFlow(24 hrs)

0.2 - 0.4 %

ASTM D955

Melt Volume Rate, MVR

1.2 kg;MVR at 300 °C

2.16 kg;MVR at 300 °C

10 cm³/10 min

21 cm³/10 min

ISO 1133

Water Absorption(24 hrs;23 °C

)

0.03 %

ISO 62-1

Izod Impact, Notched

23 °C

140 J/m

ASTM D256

-30 °C

90 J/m

ASTM D256

80*10*4;23 °C

13 kJ/m²

ISO 180/1A

80*10*4;-30 °C

9 kJ/m²

ISO 180/1A

Instrumented Dart Impact, Total Energy(23 °C)

22 J

ASTM D3763

Izod Impact, Unnotched

23 °C

680 J/m

ASTM D4812

80*10*4;23 °C

41 kJ/m²

ISO 180/1U

Tensile Modulus

5 mm/min

6700 MPa

ASTM D638

1 mm/min

6650 MPa

ISO 527

Tensile Strain, Break

5 mm/min;Type I

2.6 %

ASTM D638

5 mm/min

2.6 %

ISO 527

Tensile Stress, Break

5 mm/min;Type I

109 MPa

ASTM D638

5 mm/min

107 MPa

ISO 527

Flexural Modulus

1.3 mm/min;50 mm;span

6050 MPa

ASTM D790

2 mm/min

6150 MPa

ISO 178

Flexural Stress, break

1.3 mm/min;50 mm;span

158 MPa

ASTM D790

2 mm/min

160 MPa

ISO 178

Flexural Stress, Yield

1.3 mm/min;50 mm;span

161 MPa

ASTM D790

2 mm/min

161 MPa

ISO 178

UL Recognized

≥ 0.6 mm

≥ 0.5 mm

V-0

V-1

UL 94

Glow Wire Ignition Temperature [GWIT]

2 mm

1 mm

1.6 mm

850 °C

850 °C

850 °C

IEC 60695-2-13

Glow Wire Flammability Index

2 mm

1 mm

1.6 mm

960 °C

960 °C

960 °C

IEC 60695-2-12

Heat Deflection Temperature[HDT], Unannealed

0.45 MPa;3.2 mm

3.2 mm;1.82 MPa

120 °C

115 °C

ASTM D648

CTE, Flow

23°C to 80°C

-40 - 40 °C

2.6e-05 1/°C

2.5e-05 1/°C

ASTM E831

CTE, XFlow

23°C to 80°C

-40 - 40 °C

7.5e-05 1/°C

6.3e-05 1/°C

ASTM E831

Vicat Softening Temperature

Rate B/120

Rate B/50

125 °C

122 °C

ISO 306

HDT/Af(1.8)

116 °C

ISO 75/Af

HDT/Bf(0.45)

121 °C

ISO 75/Bf

Relative Temp Index, Elec

80 °C

UL 746B

Relative Temp Index, Mechanical with Impact

80 °C

UL 746B

Relative Temp Index, Mechanical without Impact

80 °C

UL 746B

Surface Resistivity

> 1.0E+16 ohms

ASTM D257

Volume Resistivity

> 1.0E+16 ohms ·cm

ASTM D257

Comparative Tracking Index, CTI

PLC 3

UL 746A

Processing

Nominal Value

Back Pressure<Injection>

0.1 - 0.3 MPa

Drying Temperature<Injection>

110 °C

Drying Time<Injection>

3 - 6 hrs

Front, Zone 3 Temperature<Injection>

280 - 300 °C

Maximum Moisture Content<Injection>

0.02 %

Melt Temperature<Injection>

285 - 310 °C

Middle, Zone 2 Temperature<Injection>

270 - 290 °C

Mold Temperature<Injection>

80 - 110 °C

Nozzle Temperature<Injection>

285 - 305 °C

Rear, Zone 1 Temperature<Injection>

260 - 280 °C

Screw Speed <Injection>

50 - 90 rpm