PPcompound 1200-XH
Forever
PPcompound 1200-XH is a mineral reinforced polypropylene material known for its excellent flowability and stiffness. With its high modulus and melt flow, this grade is specifically designed for the production of large parts, making it ideal for applications like e-Commerce base or lid components.
General | ||
Form | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 0.970 g/cm³ | ISO 1183 |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 23 g/10min | ISO 1133 |
Molding Shrinkage(24 hr;3.2 mm;65x65x3.2 mm) | 1.2 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Modulus, injection molded | 1400 MPa | ISO 527-1/1A |
Tensile Stress, Yield, Injection Molded | 20.0 MPa | ISO 527-2/1A |
Tensile Stress, Break, Injection Molded | 16.0 MPa | ISO 527-2/1A |
Tensile Strain, Break, Injection molded | 18 % | ISO 527-2/1A |
Flexural Modulus, Injection Molded(Type 1A) | 1450 MPa | ISO 178 |
Notched Izod Impact Strength, Injection Molded | ISO 180/1A | |
-20 °C | 4.5 kJ/m² | |
0 °C | 6.0 kJ/m² | |
23 °C | 10 kJ/m² | |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed, | ||
Injection Molded | ||
0.45 MPa | 93.0 °C | ISO 75-2/B |
1.8 MPa | 54.0 °C | ISO 75-2/A |
CLTE, Flow(-30 - 100 °C) | 1.2E-4 cm/cm/°C | ISO 11359-2 |
PPcompound 1200-XH is a mineral reinforced polypropylene material known for its excellent flowability and stiffness. With its high modulus and melt flow, this grade is specifically designed for the production of large parts, making it ideal for applications like e-Commerce base or lid components.
General | ||
Form | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 0.970 g/cm³ | ISO 1183 |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 23 g/10min | ISO 1133 |
Molding Shrinkage(24 hr;3.2 mm;65x65x3.2 mm) | 1.2 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Modulus, injection molded | 1400 MPa | ISO 527-1/1A |
Tensile Stress, Yield, Injection Molded | 20.0 MPa | ISO 527-2/1A |
Tensile Stress, Break, Injection Molded | 16.0 MPa | ISO 527-2/1A |
Tensile Strain, Break, Injection molded | 18 % | ISO 527-2/1A |
Flexural Modulus, Injection Molded(Type 1A) | 1450 MPa | ISO 178 |
Notched Izod Impact Strength, Injection Molded | ISO 180/1A | |
-20 °C | 4.5 kJ/m² | |
0 °C | 6.0 kJ/m² | |
23 °C | 10 kJ/m² | |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed, | ||
Injection Molded | ||
0.45 MPa | 93.0 °C | ISO 75-2/B |
1.8 MPa | 54.0 °C | ISO 75-2/A |
CLTE, Flow(-30 - 100 °C) | 1.2E-4 cm/cm/°C | ISO 11359-2 |
Resin Pellets