Raw PA6 Material Nylon PA6 Plastic Resin for Injection Raw Material PA6 Polyamide PA6 Price

Form                                        Resin Pellets

Filler                                        30 % Glass Fiber

Feature                                    Flame Retardant

Uses                                          Automotive                      Engineered                        Electron & electric parts

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.41 g/cm³                                             ISO 1183

Mold Shrinkage, MD                                                            0.3 %                                                       ISO 294-4

Mold Shrinkage, TD                                                             0.7 %                                                       ISO 294-4

Mechanical                                                                            Nominal Value                                      Test Method

Tensile Strength(20 mm/min)                                             135 MPa                                                 ISO 527-2

Elongation at Break(20 mm/min)                                        2.6 %                                                       ISO 527-2

Flexural Strength(2 mm/min)                                              185 MPa                                                 ISO 178

Flexural Modulus(2 mm/min)                                              7800 MPa                                               ISO 178

Notched Izod Impact Strength                                            10 kJ/m²                                                 ISO 180

Thermal                                                                                 Nominal Value                                      Test Method

Heat Deflection Temperature                                                                                                            ISO 75

0.45 MPa                                                                              210 °C

1.82 MPa                                                                              200 °C

Flammability(1.6 mm)                                                         V-0                                                          UL94

Processing                                                                                                                                           Nominal Value

Drying Temperature                                                                                                                            95 - 110 °C

Drying Time                                                                                                                                       2 - 4 h

Mold Temperature                                                                                                                               65 - 100 °C

Melt Temperature                                                                                                                                230 - 265 °C