511CPE NC010-XH
Forever
Re describe the following paragraph 511CPE NC010-XH is a medium viscosity acetal homopolymer with enhanced crystallinity, reduced cycle time, excellent creep and fatigue resistance, and extremely low VOC emissions. 511CPE NC010-XH offers improved thermal stability, dimensional stability, reduced warpage, fewer voids, and increased efficiency in injection molding. Acetal resins are known for their mechanical properties, such as high strength and stiffness, exceptional resistance to fatigue and impact, as well as their ability to withstand moisture, gasoline, lubricants, solvents, and other neutral chemicals. Additionally, acetal resin provides excellent dimensional stability and electrical insulation. They possess natural resilience, self-lubrication, and are available in various colors and special grades. Acetal resins are widely used in demanding applications across industries such as automotive, household appliances, sports, industrial engineering, electronics, and consumer goods.
General | ||
Form | ||
Feature | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.42 g/cm³ | ISO 1183 |
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) | 14 g/10min | ISO 1133 |
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 13 cm³/10 min | ISO 1133 |
Molding Shrinkage, Across Flow | 1.8 % | ISO 294-4 |
Molding Shrinkage, Flow | 1.8 % | ISO 294-4 |
Rockwell Hardness, M-Scale | 95 | ISO 2039-2 |
Rockwell Hardness, R-Scale | 122 | ISO 2039-2 |
Emission | < 2.00 mg/kg | VDA 275 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 3400 MPa | ISO 527-2 |
Tensile Stress, Yield | 77.0 MPa | ISO 527-2 |
Tensile Strain, Yield | 13 % | ISO 527-2 |
Nominal Tensile Strain at Break | 25 % | ISO 527-2 |
Flexural Modulus | 3200 MPa | ISO 178 |
Flexural Stress(3.5% Strain) | 89.0 MPa | ISO 178 |
Poisson's Ratio | 0.37 | No Standard |
C harpy Notched Impact Strength | ISO 179 1eA | |
-30 °C | 6.5 kJ/m² | |
23 °C | 7.0 kJ/m² | |
C harpy Unnotched Impact Strength(23 °C) | 240 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
165 °C 115 °C |
ISO 75-2/B ISO 75-2/A |
Melting Point(10 °C/min) | 178 °C | ISO 11357-3 |
Annealing Temperature | 160 °C | |
Annealing Time - Optional | 30.0 min/mm | |
Burning rate(1 mm;FMVSS 302) | 30 mm/min | ISO 3795 |
Flame Rating
0.8 mm 1.5 mm |
HB HB | IEC 60695-11- 10;UL 94;IEC 60695-11-20 |
FMVSS Flammability | B | FMVSS 302 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 62631-3-2 |
Volume Resistivity | > 1E+11 ohms ·cm | IEC 62631-3-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
3.90 3.90 | IEC 62631-2-1 |
Dissipation Factor 100 Hz 1.0e+6 Hz |
4.0E-3 4.5E-3 | IEC 62631-2-1 |
Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Time - Desiccant Dryer<Injection> | 2.0 - 4.0 hr | |
Processing Temp, Melt<Injection> | 200 - 210 °C | |
Melt Temperature, Optimum<Injection> | 205 °C | |
Mold Temperature<Injection> | 80 - 100 °C | |
Mold Temperature, Optimum<Injection> | 90 °C | |
Holding Pressure<Injection> | 80.0 - 100 MPa | |
Drying Recommended <Injection> | YES | |
Hold Pressure Time<Injection> | 8.00 s/mm | |
Maximum Screw Tangential Speed <Injection> | 18 m/min |
Re describe the following paragraph 511CPE NC010-XH is a medium viscosity acetal homopolymer with enhanced crystallinity, reduced cycle time, excellent creep and fatigue resistance, and extremely low VOC emissions. 511CPE NC010-XH offers improved thermal stability, dimensional stability, reduced warpage, fewer voids, and increased efficiency in injection molding. Acetal resins are known for their mechanical properties, such as high strength and stiffness, exceptional resistance to fatigue and impact, as well as their ability to withstand moisture, gasoline, lubricants, solvents, and other neutral chemicals. Additionally, acetal resin provides excellent dimensional stability and electrical insulation. They possess natural resilience, self-lubrication, and are available in various colors and special grades. Acetal resins are widely used in demanding applications across industries such as automotive, household appliances, sports, industrial engineering, electronics, and consumer goods.
General | ||
Form | ||
Feature | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.42 g/cm³ | ISO 1183 |
Melt Mass-Flow Rate, MFR(190 °C;2.16 kg) | 14 g/10min | ISO 1133 |
Melt Volume-Flow Rate, MVR(190 °C;2.16 kg) | 13 cm³/10 min | ISO 1133 |
Molding Shrinkage, Across Flow | 1.8 % | ISO 294-4 |
Molding Shrinkage, Flow | 1.8 % | ISO 294-4 |
Rockwell Hardness, M-Scale | 95 | ISO 2039-2 |
Rockwell Hardness, R-Scale | 122 | ISO 2039-2 |
Emission | < 2.00 mg/kg | VDA 275 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | 3400 MPa | ISO 527-2 |
Tensile Stress, Yield | 77.0 MPa | ISO 527-2 |
Tensile Strain, Yield | 13 % | ISO 527-2 |
Nominal Tensile Strain at Break | 25 % | ISO 527-2 |
Flexural Modulus | 3200 MPa | ISO 178 |
Flexural Stress(3.5% Strain) | 89.0 MPa | ISO 178 |
Poisson's Ratio | 0.37 | No Standard |
C harpy Notched Impact Strength | ISO 179 1eA | |
-30 °C | 6.5 kJ/m² | |
23 °C | 7.0 kJ/m² | |
C harpy Unnotched Impact Strength(23 °C) | 240 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
165 °C 115 °C |
ISO 75-2/B ISO 75-2/A |
Melting Point(10 °C/min) | 178 °C | ISO 11357-3 |
Annealing Temperature | 160 °C | |
Annealing Time - Optional | 30.0 min/mm | |
Burning rate(1 mm;FMVSS 302) | 30 mm/min | ISO 3795 |
Flame Rating
0.8 mm 1.5 mm |
HB HB | IEC 60695-11- 10;UL 94;IEC 60695-11-20 |
FMVSS Flammability | B | FMVSS 302 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 62631-3-2 |
Volume Resistivity | > 1E+11 ohms ·cm | IEC 62631-3-1 |
Relative Permittivity 100 Hz 1.0e+6 Hz |
3.90 3.90 | IEC 62631-2-1 |
Dissipation Factor 100 Hz 1.0e+6 Hz |
4.0E-3 4.5E-3 | IEC 62631-2-1 |
Comparative Tracking Index | 600 V | IEC 60112 |
Processing | Nominal Value | |
Drying Time - Desiccant Dryer<Injection> | 2.0 - 4.0 hr | |
Processing Temp, Melt<Injection> | 200 - 210 °C | |
Melt Temperature, Optimum<Injection> | 205 °C | |
Mold Temperature<Injection> | 80 - 100 °C | |
Mold Temperature, Optimum<Injection> | 90 °C | |
Holding Pressure<Injection> | 80.0 - 100 MPa | |
Drying Recommended <Injection> | YES | |
Hold Pressure Time<Injection> | 8.00 s/mm | |
Maximum Screw Tangential Speed <Injection> | 18 m/min |