Polycarbonate Polymers Light Diffusion for Lamp PC Fr V0 Granules Transparent PC Pellets PC Resin

Form                                        Resin Pellets

Filler                                        30 % Glass Fiber

Feature

 High Impact  Lds

 Enhanced Ductility            Circuit Solution

 Good Surface Appearance

Uses

 Automotive

 Electrical

 Consumer                          Laser Direct Structuring

Physical                                                                                 Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.47                                                        ASTM D792

Melt Flow Rate[MFR]                                                                                                                           ASTM D1238

280 °C;2.16 kgf                                                                    10 g/10min

280 °C;5 kgf                                                                        27 g/10min

300 °C;1.2 kgf                                                                      16 g/10min

Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C)                 13 cm³/10 min                                        ASTM D1238

C harpy Impact, Unnotched(23 °C)

50 kJ/m²

ISO 179/2C

Izod Impact, Unnotched

23 °C

700 J/m

ASTM D4812

80*10*4;23 °C

40 kJ/m²

ISO 180/1U

Izod Impact, Notched

23 °C

150 J/m

ASTM D256

80*10*4;23 °C

14 kJ/m²

ISO 180/1A

C harpy Impact, Notched(23 °C)

14 kJ/m²

ISO 179/2C

Tensile Stress, Break

5 mm/min;Type I

120 MPa

ASTM D638

50 mm/min

120 MPa

ISO 527

Tensile Strain, Break

5 mm/min;Type I

2.4 %

ASTM D638

50 mm/min

2.4 %

ISO 527

Tensile Modulus

5 mm/min

8760 MPa

ASTM D638

1 mm/min

8840 MPa

ISO 527

Flexural Stress

170 MPa

ASTM D790

180 MPa

ISO 178

Flexural Modulus

8020 MPa

ASTM D790

8450 MPa

ISO 178

Heat Deflection Temperature[HDT]

0.45 MPa;3.2 mm

3.2 mm;1.82 MPa

126 °C

122 °C

ASTM D648

CTE, Flow

-40 - 40 °C

-40 - 40 °C

2.1e-05 1/°C

2.1e-05 1/°C

ASTM E831

ISO 11359-2

CTE, XFlow

-40 - 40 °C

-40 - 40 °C

6.9e-05 1/°C

7.1e-05 1/°C

ASTM E831

ISO 11359-2

HDT/Bf(0.45)

127 °C

ISO 75/Bf

HDT/Af(1.8)

124 °C

ISO 75/Af

Processing

Nominal Value

Drying Temperature<Injection>

110 °C

Drying Time<Injection>

3 - 4 hrs

Melt Temperature<Injection>

270 - 295 °C

Nozzle Temperature<Injection>

270 - 295 °C

Front, Zone 3 Temperature<Injection>

270 - 295 °C

Middle, Zone 2 Temperature<Injection>

270 - 295 °C

Rear, Zone 1 Temperature<Injection>

270 - 295 °C

Mold Temperature<Injection>

100 - 120 °C