LEXAN923X-XH
FOREVER
Product Description | |||
LEXAN923X-XH, an impressive injection molding grade designed with high UV stabilization and excellent impact resistance. Its unique composition comprises non-bromine and non-chlorine flame-retardant systems that offer UL94 V0 @ 1.5mm flame retardancy. Moreover, it exhibits low temperature ductility and impressive processing properties that translate to shorter injection molding cycle times in comparison to standard PC resins. Available in a wide selection of opaque colors, LEXAN923X-XH is a versatile product fit for numerous applications. With its outstanding properties and durability, it is set to revolutionize the world of injection molding. | |||
General | |||
Form |
| ||
| |||
Feature | |||
| |||
| |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 16 g/10min ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.80 % Internal Method | |||
Mechanical | Nominal Value | Test Method | |
Tensile Modulus(5 mm/min) | 2100 MPa | ASTM D638 | |
Tensile Strength, Yield(50 mm/min;Type I) 58.0 MPa ASTM D638 | |||
Tensile Strength, Break(50 mm/min;Type I) 60.0 MPa ASTM D638 | |||
Tensile Elongation, Yield(50 mm/min;Type I) 6.0 % ASTM D638 | |||
Tensile Elongation, Break(50 mm/min;Type I) 110 % ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) 2400 MPa ASTM D790 | |||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 90.0 MPa ASTM D790 | |||
Notched Izod Impact | ASTM D256 | ||
-30 °C | 650 J/m | ||
23 °C | 780 J/m | ||
Instrumented Dart Impact, Total Energy(23 °C) 65.0 J ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed(1.8 MPa;3 2 mm) | 123 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 140 °C | ASTM D1525 |
CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 6.2E-5 cm/cm/°C | ASTM E831 |
RTI Elec | 125 °C | UL 746 |
RTI Imp | 115 °C | UL 746 |
RTI Str | 120 °C | UL 746 |
Flame Rating 1.5 mm 3 mm |
V-0 5VA | UL 94 |
Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1.5 mm 3 mm |
825 °C 825 °C | IEC 60695-2-13 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 270 - 295 °C | |
Middle Temperature<injection> | 280 - 305 °C | |
Front Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Processing Temp, Melt<Injection> | 295 - 315 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
Product Description | |||
LEXAN923X-XH, an impressive injection molding grade designed with high UV stabilization and excellent impact resistance. Its unique composition comprises non-bromine and non-chlorine flame-retardant systems that offer UL94 V0 @ 1.5mm flame retardancy. Moreover, it exhibits low temperature ductility and impressive processing properties that translate to shorter injection molding cycle times in comparison to standard PC resins. Available in a wide selection of opaque colors, LEXAN923X-XH is a versatile product fit for numerous applications. With its outstanding properties and durability, it is set to revolutionize the world of injection molding. | |||
General | |||
Form |
| ||
| |||
Feature | |||
| |||
| |||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) 16 g/10min ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.80 % Internal Method | |||
Mechanical | Nominal Value | Test Method | |
Tensile Modulus(5 mm/min) | 2100 MPa | ASTM D638 | |
Tensile Strength, Yield(50 mm/min;Type I) 58.0 MPa ASTM D638 | |||
Tensile Strength, Break(50 mm/min;Type I) 60.0 MPa ASTM D638 | |||
Tensile Elongation, Yield(50 mm/min;Type I) 6.0 % ASTM D638 | |||
Tensile Elongation, Break(50 mm/min;Type I) 110 % ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) 2400 MPa ASTM D790 | |||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) 90.0 MPa ASTM D790 | |||
Notched Izod Impact | ASTM D256 | ||
-30 °C | 650 J/m | ||
23 °C | 780 J/m | ||
Instrumented Dart Impact, Total Energy(23 °C) 65.0 J ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed(1.8 MPa;3 2 mm) | 123 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 140 °C | ASTM D1525 |
CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 6.2E-5 cm/cm/°C | ASTM E831 |
RTI Elec | 125 °C | UL 746 |
RTI Imp | 115 °C | UL 746 |
RTI Str | 120 °C | UL 746 |
Flame Rating 1.5 mm 3 mm |
V-0 5VA | UL 94 |
Glow Wire Flammability Index(1.5 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1.5 mm 3 mm |
825 °C 825 °C | IEC 60695-2-13 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 270 - 295 °C | |
Middle Temperature<injection> | 280 - 305 °C | |
Front Temperature<Injection> | 295 - 315 °C | |
Nozzle Temperature<Injection> | 290 - 310 °C | |
Processing Temp, Melt<Injection> | 295 - 315 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Vent Depth<Injection> | 0.025 - 0.076 mm |