Polycarbonate+ABS ( PC/ABS) Pellet Alloy Material Virgin Plastic Granules

Form

 Resin Pellets

Feature

Low Temperature Impact

Good Paintability

 Escr

Chemical Resistant

Excellent Processability

Good Dimensional

Good Thermal

Physical

Nominal Value

Test Method

Density / Specific Gravity(23 °C)

1.19 g/cm³

ISO 1183

Melt Volume-Flow Rate, MVR(260 °C;5 kg)

18 cm³/10 min

ISO 1133

Molding Shrinkage, Across Flow(260 °C;MT 80 °C;3 mm;150x105x3mm)

0.50 - 0.70 %

ISO 2577

Molding Shrinkage, Flow(260 °C;MT 80 °C;3 mm;150x105x3mm)

0.50 - 0.70 %

ISO 2577

Water Absorption, Saturation(23 °C)

0.50 %

ISO 62

Water Absorption, Equilibrium(50% RH;23 °C)

0.20 %

ISO 62

Melt Viscosity(260 °C;1000s-1)

480 Pa · s

ISO 11443-A

Mechanical

Nominal Value

Test Method

Tensile Modulus(23 °C)

2400 MPa

ISO 527-2/1

Tensile Stress, Yield(23 °C)

65.0 MPa

ISO 527-2/50

Tensile Stress, Break(23 °C)

60.0 MPa

ISO 527-2/50

Tensile Strain, Yield(23 °C)

5.0 %

ISO 527-2/50

Tensile Strain, Break(23 °C)

> 50 %

ISO 527-2/50

Notched Izod Impact Strength

-30 °C

23 °C

15 kJ/m²

55 kJ/m²

ISO 180/1A

Unnotched Izod Impact Strength(23 °C)

No Break

ISO 180

Heat Deflection Temperature, Unannealed

0.45 MPa

1.8 MPa

126 °C

115 °C

ISO 75-2/B

ISO 75-2/A

Vicat Softening Temperature

134 °C

136 °C

ISO 306/B50   ISO 306/B120

CLTE, Flow(23 - 55 °C)

6.8E-5 cm/cm/°C

ISO 11359-2

CLTE, Transverse(23 - 55 °C)

6.8E-5 cm/cm/°C

ISO 11359-2

Flame Rating

1 mm

1.5 mm

2 mm

3 mm

V-1

V-0

5VB

5VA

UL 94

Electrical

Nominal Value

Test Method

Surface Resistivity

1.0E+17 ohms

IEC 60093

Volume Resistivity(23 °C)

1.0E+17 ohms ·cm

IEC 60093

Electric Strength(23 °C;1 mm)

35 kV/mm

IEC 60243-1

Relative Permittivity

100 Hz;23 °C

23 °C;1.0e+6 Hz

3.20

3.10

IEC 60250

Dissipation Factor

100 Hz;23 °C

23 °C;1.0e+6 Hz

2.0E-3

8.0E-3

IEC 60250

Comparative Tracking Index, Solution A

300 V

IEC 60112

Drying Temperature - Dry Air Dryer<Injection>

80 °C

Drying Time - Dry Air Dryer<Injection>

4.0 hr

Suggested Max Moisture<Injection>

< 0.020 %

Suggested Shot Size<Injection>

30 - 70 %

Rear Temperature<Injection>

220 - 230 °C

Middle Temperature<injection>

225 - 235 °C

Front Temperature<Injection>

230 - 240 °C

Nozzle Temperature<Injection>

255 - 265 °C

Processing Temp, Melt<Injection>

240 - 270 °C

Mold Temperature<Injection>

60 - 90 °C

Back Pressure<Injection>

5.00 - 15.0 MPa

Vent Depth <Injection>

0.025 - 0.075 mm

Hold Pressure<Injection>

50 - 75 %

Standard Melt Temperature<Injection>

260 °C

Peripheral Screw Speed <Injection>

0.05 - 0.2 m/s