A 218 V15 BK 21N-XH
Forever
A 218 V15 BK 21N-XH is a heat-stabilized polyamide 66 material with 15% glass fiber reinforcement, designed specifically for injection molding. This grade showcases a remarkable balance of thermal and mechanical properties, making it highly versatile and reliable for various applications.
General | |||
Form | |||
Filler | |||
Feature | |||
Usage |
|
| |
Physical Nominal Value Test Method | |||
Density / Specific Gravity 1.24 g/cm³ ISO 1183 | |||
Water Absorption(24 hr, 23°C) 1.1 % ISO 62 | |||
Molding shrinkage, parallel(72 hr, 23°C, 50% RH) 0.5 % | ISO 294-4, ISO 2577 | ||
Molding shrinkage, normal(72 hr, 23°C, 50% RH) 1.4 % | ISO 294-4, ISO 2577 | ||
Mechanical | Nominal Value | Test Method |
Tensile Modulus 1 mm/min;dry 1 mm/min;conditioned |
6200 MPa 4300 MPa | ISO 527-1/-2 |
Stress at break dry conditioned |
125 MPa 90 MPa | ISO 527-1/-2 |
Strain at break dry conditioned |
3 % 8 % | ISO 527-1/-2 |
Flexural Modulus 2 mm/min;dry 2 mm/min;conditioned |
5300 MPa 3500 MPa | ISO 178 |
Flexural Strength(2 mm/min;conditioned) | 115 MPa | ISO 178 |
C harpy Impact Strength, Unnotched 23 °C;dry 23 °C;conditioned |
40 kJ/m² 65 kJ/m² | ISO 179 1eU |
C harpy Notched Impact Strength 23 °C;dry 23 °C;conditioned |
5 kJ/m² 6.5 kJ/m² | ISO 179 1eA |
Izod impact strength, Notched 23 °C;dry 23 °C;conditioned |
40 kJ/m² 65 kJ/m² | ISO 180/1U |
Notched Izod Impact Strength 23 °C;dry 23 °C;conditioned |
5 kJ/m² 10 kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Test Method |
Melting Temperature(10°C/min) | 263 °C | ISO 11357-1 |
Temp. of deflection under load(1.8 MPa) | 245 °C | ISO 75 |
Flammability(3 mm) | HB | UL 94 |
Oxygen Index | 24 % |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1E+11 ohms ·cm | IEC 62631-3-1 |
Surface Resistivity | 6E+015 Ohms | IEC 62631-3-1 |
Comparative Tracking Index(Solution A) | 400 V | IEC 60112 |
Dielectric Strength(1 mm) | 31 kV/mm | IEC 60243-1 |
Processing | Nominal Value | |
Drying Temperature(除湿干燥机) | 80 °C | |
Drying Time(除湿干燥机) | 2 - 4 h | |
Suggested Max Moisture | 0.2 % | |
Rear Temperature | 270 - 280 °C | |
Middle Temperature | 275 - 285 °C | |
Front Temperature | 280 - 290 °C | |
Blow Molding Mold Temperature | 70 - 100 °C |
A 218 V15 BK 21N-XH is a heat-stabilized polyamide 66 material with 15% glass fiber reinforcement, designed specifically for injection molding. This grade showcases a remarkable balance of thermal and mechanical properties, making it highly versatile and reliable for various applications.
General | |||
Form | |||
Filler | |||
Feature | |||
Usage |
|
| |
Physical Nominal Value Test Method | |||
Density / Specific Gravity 1.24 g/cm³ ISO 1183 | |||
Water Absorption(24 hr, 23°C) 1.1 % ISO 62 | |||
Molding shrinkage, parallel(72 hr, 23°C, 50% RH) 0.5 % | ISO 294-4, ISO 2577 | ||
Molding shrinkage, normal(72 hr, 23°C, 50% RH) 1.4 % | ISO 294-4, ISO 2577 | ||
Mechanical | Nominal Value | Test Method |
Tensile Modulus 1 mm/min;dry 1 mm/min;conditioned |
6200 MPa 4300 MPa | ISO 527-1/-2 |
Stress at break dry conditioned |
125 MPa 90 MPa | ISO 527-1/-2 |
Strain at break dry conditioned |
3 % 8 % | ISO 527-1/-2 |
Flexural Modulus 2 mm/min;dry 2 mm/min;conditioned |
5300 MPa 3500 MPa | ISO 178 |
Flexural Strength(2 mm/min;conditioned) | 115 MPa | ISO 178 |
C harpy Impact Strength, Unnotched 23 °C;dry 23 °C;conditioned |
40 kJ/m² 65 kJ/m² | ISO 179 1eU |
C harpy Notched Impact Strength 23 °C;dry 23 °C;conditioned |
5 kJ/m² 6.5 kJ/m² | ISO 179 1eA |
Izod impact strength, Notched 23 °C;dry 23 °C;conditioned |
40 kJ/m² 65 kJ/m² | ISO 180/1U |
Notched Izod Impact Strength 23 °C;dry 23 °C;conditioned |
5 kJ/m² 10 kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Test Method |
Melting Temperature(10°C/min) | 263 °C | ISO 11357-1 |
Temp. of deflection under load(1.8 MPa) | 245 °C | ISO 75 |
Flammability(3 mm) | HB | UL 94 |
Oxygen Index | 24 % |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1E+11 ohms ·cm | IEC 62631-3-1 |
Surface Resistivity | 6E+015 Ohms | IEC 62631-3-1 |
Comparative Tracking Index(Solution A) | 400 V | IEC 60112 |
Dielectric Strength(1 mm) | 31 kV/mm | IEC 60243-1 |
Processing | Nominal Value | |
Drying Temperature(除湿干燥机) | 80 °C | |
Drying Time(除湿干燥机) | 2 - 4 h | |
Suggested Max Moisture | 0.2 % | |
Rear Temperature | 270 - 280 °C | |
Middle Temperature | 275 - 285 °C | |
Front Temperature | 280 - 290 °C | |
Blow Molding Mold Temperature | 70 - 100 °C |