62 CPG/500-XH
Forever
62 CPG/500-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.
General | |
Form | |
Filler | Glass Fiber/Thermally Conductive Proprietary
|
Feature | |
Physical Nominal Value Test Method | |
Density / Specific Gravity 1.91 g/cm³ ISO 1183 | |
Molding Shrinkage, Across Flow(2 mm;60 MPa) 0.45 - 0.70 % ISO 294-4 | |
Molding Shrinkage, Flow(2 mm;60 MPa) 0.35 - 0.60 % ISO 294-4 | |
Mechanical Nominal Value Test Method | |
Tensile Modulus(23 °C) 8500 MPa ISO 527-1/2 | |
Tensile Stress, Break(23 °C) 120 MPa ISO 527-2/5 | |
Elongation at Break(23 °C) 2.0 % ISO 527-2/5 | |
C harpy Notched Impact Strength(23 °C) 4.0 kJ/m² ISO 179 1eA | |
C harpy Unnotched Impact Strength(23 °C) 40 kJ/m² ISO 179 1eU | |
Thermal Nominal Value Test Method | |
Heat Deflection Temperature | |
Unannealed;0.45 MPa 215 °C ISO 75-2/B | |
Unannealed;1.8 MPa 195 °C ISO 75-2/A | |
Vicat Softening Temperature 205 °C ISO 306/B50 | |
Thermal Conductivity, Through Plane(Longitudinal) 1.2 W/m-K Internal Method | |
Electrical Nominal Value Test Method | |
Surface Resistivity 1.0E+14 ohms ASTM D257 | |
Processing Nominal Value | |
Melt Temperature 250 - 270 °C | |
Mold Temperature 80.0 - 100 °C | |
Drying Temperature 90.0 - 100 °C | |
Dry Time 3 hr | |
62 CPG/500-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.
General | |
Form | |
Filler | Glass Fiber/Thermally Conductive Proprietary
|
Feature | |
Physical Nominal Value Test Method | |
Density / Specific Gravity 1.91 g/cm³ ISO 1183 | |
Molding Shrinkage, Across Flow(2 mm;60 MPa) 0.45 - 0.70 % ISO 294-4 | |
Molding Shrinkage, Flow(2 mm;60 MPa) 0.35 - 0.60 % ISO 294-4 | |
Mechanical Nominal Value Test Method | |
Tensile Modulus(23 °C) 8500 MPa ISO 527-1/2 | |
Tensile Stress, Break(23 °C) 120 MPa ISO 527-2/5 | |
Elongation at Break(23 °C) 2.0 % ISO 527-2/5 | |
C harpy Notched Impact Strength(23 °C) 4.0 kJ/m² ISO 179 1eA | |
C harpy Unnotched Impact Strength(23 °C) 40 kJ/m² ISO 179 1eU | |
Thermal Nominal Value Test Method | |
Heat Deflection Temperature | |
Unannealed;0.45 MPa 215 °C ISO 75-2/B | |
Unannealed;1.8 MPa 195 °C ISO 75-2/A | |
Vicat Softening Temperature 205 °C ISO 306/B50 | |
Thermal Conductivity, Through Plane(Longitudinal) 1.2 W/m-K Internal Method | |
Electrical Nominal Value Test Method | |
Surface Resistivity 1.0E+14 ohms ASTM D257 | |
Processing Nominal Value | |
Melt Temperature 250 - 270 °C | |
Mold Temperature 80.0 - 100 °C | |
Drying Temperature 90.0 - 100 °C | |
Dry Time 3 hr | |
Resin Pellets