Availability: | |
---|---|
Quantity: | |
CX2244ME-XH
Forever
CX2244ME-XH is a type of plastic material that can be easily molded through injection. It has a medium flow and is treated with non-chlorinated/brominated flame retardants. It has achieved UL94 V0@0.75mm and 5VB@1.5mm ratings for its flame resistance. This particular grade offers better chemical resistance than regular PC/ABS blends and is highly suitable for applications that require thin walls, such as in the medical field.
General | |||||
Form |
| ||||
Feature | Chemical Resistant
Non-Brominated & Non- Chlorinated Flame retardant | Excellent Processability
Non-Chlorinated | Hydrolysis Resistance
Thin Wall | ||
Uses |
|
| |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity |
1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 18 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.2 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | |||
Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C) | 15 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched 23 °C -30 °C |
700 J/m 175 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
40 kJ/m² 10 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
40 kJ/m² 10 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 65 MPa | ASTM D638 |
50 mm/min | 65 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 58 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 4.1 % | ASTM D638 |
50 mm/min | 4 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 100 % | ASTM D638 |
50 mm/min | 90 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 2600 MPa | ASTM D638 |
1 mm/min | 2600 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 104 MPa | ASTM D790 |
2 mm/min | 96 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2500 MPa | ASTM D790 |
2 mm/min | 2500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 3 mm ≥ 1.5 mm ≥ 0.75 mm |
5VA 5VB V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT](3 mm) | 800 °C | IEC 60695-2-13 |
Glow Wire Flammability Index(3 mm) | 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature | ||
Rate B/50 | 110 °C | ASTM D1525 |
Rate B/50 | 110 °C | ISO 306 |
Rate B/120 | 113 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 89 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.5e-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.5e-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 7.5e-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.5e-05 1/°C | ISO 11359-2 |
Ball Pressure Test(75°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Af(1.8) | 93 °C | ISO 75/Af |
Relative Temp Index, Elec | 90 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 90 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 90 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Volume Resistivity | > 1E+15 ohms ·cm | IEC 60093 |
Surface Resistivity, ROA | > 1.E+15 ohms | IEC 60093 |
Dielectric Strength, in Oil 0.8 mm 1.6 mm 3.2 mm |
35 kV/mm 25 kV/mm 17 kV/mm | IEC 60243-1 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI(0.75 mm) | PLC 3 | UL 746A |
High Amp Arc Ignition, HAI(0.75 mm) | PLC 0 | UL 746A |
High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746A |
Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 2 - 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 250 - 300 °C | |
Nozzle Temperature<Injection> | 250 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 250 - 300 °C | |
Middle, Zone 2 Temperature<Injection> | 240 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 280 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 85 °C | |
Vent Depth <Injection> | 0.03 - 0.075 mm |
CX2244ME-XH is a type of plastic material that can be easily molded through injection. It has a medium flow and is treated with non-chlorinated/brominated flame retardants. It has achieved UL94 V0@0.75mm and 5VB@1.5mm ratings for its flame resistance. This particular grade offers better chemical resistance than regular PC/ABS blends and is highly suitable for applications that require thin walls, such as in the medical field.
General | |||||
Form |
| ||||
Feature | Chemical Resistant
Non-Brominated & Non- Chlorinated Flame retardant | Excellent Processability
Non-Chlorinated | Hydrolysis Resistance
Thin Wall | ||
Uses |
|
| |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity |
1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](260 °C;2.16 kgf) | 18 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.2 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | |||
Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C) | 15 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched 23 °C -30 °C |
700 J/m 175 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
40 kJ/m² 10 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
40 kJ/m² 10 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 65 MPa | ASTM D638 |
50 mm/min | 65 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 58 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 4.1 % | ASTM D638 |
50 mm/min | 4 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 100 % | ASTM D638 |
50 mm/min | 90 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 2600 MPa | ASTM D638 |
1 mm/min | 2600 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 104 MPa | ASTM D790 |
2 mm/min | 96 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2500 MPa | ASTM D790 |
2 mm/min | 2500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 3 mm ≥ 1.5 mm ≥ 0.75 mm |
5VA 5VB V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT](3 mm) | 800 °C | IEC 60695-2-13 |
Glow Wire Flammability Index(3 mm) | 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature | ||
Rate B/50 | 110 °C | ASTM D1525 |
Rate B/50 | 110 °C | ISO 306 |
Rate B/120 | 113 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 89 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.5e-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.5e-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 7.5e-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.5e-05 1/°C | ISO 11359-2 |
Ball Pressure Test(75°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Af(1.8) | 93 °C | ISO 75/Af |
Relative Temp Index, Elec | 90 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 90 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 90 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Volume Resistivity | > 1E+15 ohms ·cm | IEC 60093 |
Surface Resistivity, ROA | > 1.E+15 ohms | IEC 60093 |
Dielectric Strength, in Oil 0.8 mm 1.6 mm 3.2 mm |
35 kV/mm 25 kV/mm 17 kV/mm | IEC 60243-1 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI(0.75 mm) | PLC 3 | UL 746A |
High Amp Arc Ignition, HAI(0.75 mm) | PLC 0 | UL 746A |
High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746A |
Arc Resistance, Tungsten Electrode | PLC 6 | ASTM D495 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 2 - 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 250 - 300 °C | |
Nozzle Temperature<Injection> | 250 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 250 - 300 °C | |
Middle, Zone 2 Temperature<Injection> | 240 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 280 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 85 °C | |
Vent Depth <Injection> | 0.03 - 0.075 mm |