PR0G4-XH is a Polypropylene material that contains a 20% glass fiber filler. This material is specifically designed for use in Asia Pacific. Key characteristics of PR0G4 include its flame rating and flame retardant properties.
General | ||
Form | ||
Filler | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.13 g/cm³ | ISO 1183 |
Molding Shrinkage | 0.70 - 1.0 % | ISO 294-4 |
Rockwell Hardness, R-Scale | 102 | ISO 2039-2 |
Mechanical | Nominal Value | Test Method |
Tensile Stress, Yield | 48.0 MPa | ISO 527-2 |
Tensile Strain, Break | 4.0 % | ISO 527-2 |
Flexural Stress | 75.0 MPa | ISO 178 |
Notched Izod Impact Strength | 6.0 kJ/m² | ISO 180 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(0.45 MPa) | 130 °C | ISO 75-2/B |
Melting Temperature, DSC | 167 °C | ISO 3146 |
Flame Rating | V-0 | UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
PR0G4-XH is a Polypropylene material that contains a 20% glass fiber filler. This material is specifically designed for use in Asia Pacific. Key characteristics of PR0G4 include its flame rating and flame retardant properties.
General | ||
Form | ||
Filler | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.13 g/cm³ | ISO 1183 |
Molding Shrinkage | 0.70 - 1.0 % | ISO 294-4 |
Rockwell Hardness, R-Scale | 102 | ISO 2039-2 |
Mechanical | Nominal Value | Test Method |
Tensile Stress, Yield | 48.0 MPa | ISO 527-2 |
Tensile Strain, Break | 4.0 % | ISO 527-2 |
Flexural Stress | 75.0 MPa | ISO 178 |
Notched Izod Impact Strength | 6.0 kJ/m² | ISO 180 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed(0.45 MPa) | 130 °C | ISO 75-2/B |
Melting Temperature, DSC | 167 °C | ISO 3146 |
Flame Rating | V-0 | UL 94 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |