PP Plastic Resin for Polypropylene Non-woven Fabric Spunbonded Polypropylene Particles Polypropylene

Form                                        Resin Pellets

Filler                                        30 % Long Glass Fiber

Physical                                                                                Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.12 g/cm³                                             ISO 1183

Mechanical                                                                            Nominal Value                                     Test Method

Tensile Modulus                                                                  5800 MPa                                              ISO 527-2/1A

Tensile Stress, Break                                                            92.0 MPa                                                ISO 527-2/1A/5

Tensile Strain, Break                                                            2.5 %                                                       ISO 527-2/1A/5

Flexural Modulus(23 °C)                                                       6000 MPa                                               ISO 178

Flexural Stress(23 °C)                                                            155 MPa                                                 ISO 178

C harpy Notched Impact Strength(23 °C)                            20 kJ/m²                                                 ISO 179 1eA

Thermal                                                                                 Nominal Value                                      Test Method

Heat Deflection Temperature, Unannealed(1.8 MPa)        157 °C                                                     ISO 75-2/A

Flame Rating(1 mm)                                                             HB                                                            UL 94

Processing                                                                                                                                          Nominal Value

Drying Temperature<Injection>                                                                                                       90 - 100 °C

Drying Time<Injection>                                                                                                                    2.0 hr

Suggested Max Moisture<Injection>                                                                                              0.20 %

Rear Temperature<Injection>                                                                                                           200 - 210 °C

Middle Temperature<injection>                                                                                                       210 - 220 °C

Front Temperature<Injection>                                                                                                          220 - 230 °C

Nozzle Temperature<Injection>                                                                                                       230 - 240 °C

Processing Temp, Melt<Injection>                                                                                                   230 - 240 °C

Mold Temperature<Injection>                                                                                                          40 - 70 °C

Feeding Zone Temperature<Injection>                                                                                            20 - 50 °C

Zone4 temperature<Injection>                                                                                                        230 - 240 °C