PPcompound 9713-XH
Forever
PPcompound 9713-XH is a specially formulated mineral-filled Polypropylene that is modified with elastomers for automotive interior applications. This material is designed to provide an exceptional impact performance while maintaining good processing capabilities.
General | ||
Form | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.05 g/cm³ | ISO 1183 |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 20 g/10min | ISO 1133 |
Molding Shrinkage(24 hr;3.2 mm;65x65x3.2 mm) | 0.70 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Modulus, injection molded | 1800 MPa | ISO 527-1/1A |
Tensile Stress, Yield, Injection Molded | 16.0 MPa | ISO 527-2/1A |
Tensile Stress, Break, Injection Molded | 10.0 MPa | ISO 527-2/1A |
Tensile Strain, Break, Injection molded | 50 % | ISO 527-2/1A |
Flexural Modulus, Injection Molded(Type 1A) | 1900 MPa | ISO 178 |
Notched Izod Impact Strength, Injection Molded | ISO 180/1A | |
-20 °C | 10 kJ/m² | |
23 °C | No Break | |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa) | 55.0 °C | ISO 75-2/A |
CLTE, Flow(-30 - 100 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 |
PPcompound 9713-XH is a specially formulated mineral-filled Polypropylene that is modified with elastomers for automotive interior applications. This material is designed to provide an exceptional impact performance while maintaining good processing capabilities.
General | ||
Form | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.05 g/cm³ | ISO 1183 |
Melt Mass-Flow Rate, MFR(230 °C;2.16 kg) | 20 g/10min | ISO 1133 |
Molding Shrinkage(24 hr;3.2 mm;65x65x3.2 mm) | 0.70 % | Internal Method |
Mechanical | Nominal Value | Test Method |
Tensile Modulus, injection molded | 1800 MPa | ISO 527-1/1A |
Tensile Stress, Yield, Injection Molded | 16.0 MPa | ISO 527-2/1A |
Tensile Stress, Break, Injection Molded | 10.0 MPa | ISO 527-2/1A |
Tensile Strain, Break, Injection molded | 50 % | ISO 527-2/1A |
Flexural Modulus, Injection Molded(Type 1A) | 1900 MPa | ISO 178 |
Notched Izod Impact Strength, Injection Molded | ISO 180/1A | |
-20 °C | 10 kJ/m² | |
23 °C | No Break | |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed, Injection Molded(1.8 MPa) | 55.0 °C | ISO 75-2/A |
CLTE, Flow(-30 - 100 °C) | 6.5E-5 cm/cm/°C | ISO 11359-2 |
Resin Pellets