RCY6113-XH
Forever
RCY6113-XH resin is a type of plastic that can be melted and shaped using injection molding. It is made by blending polycarbonate (PC) and acrylonitrile butadiene styrene (ABS), and it is made flame retardant without the use of bromine or chlorine. The resin also contains 30% recycled materials from consumer waste. It has been tested and received a UL-94 5VB rating at a thickness of 2.0mm, meaning it has good fire resistance, and a V0 rating at a thickness of 1.5mm, meaning it has even better fire resistance.
General | |||
Form |
| ||
Feature |
| ||
Usage |
| ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) | 20 g/10min | ASTM D1238 | |
Molding Shrinkage, Across Flow(3.2 mm) | 0.30 - 0.50 % | Internal Method | |
Molding Shrinkage, Flow(3.2 mm) | 0.30 - 0.50 % | Internal Method | |
Water Absorption(24 hr;23 °C) | 0.11 % | ASTM D570 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus(50 mm/min) | 2500 MPa | ASTM D638 | |
Tensile Strength, Yield(50 mm/min;Type I) | 60.0 MPa | ASTM D638 | |
Tensile Strength, Break(50 mm/min;Type I) | 47.0 MPa | ASTM D638 | |
Tensile Elongation, Yield(50 mm/min;Type I) | 4.0 % | ASTM D638 | |
Tensile Elongation, Break(50 mm/min;Type I) | 60 % | ASTM D638 | |
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2400 MPa | ASTM D790 | |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 90.0 MPa | ASTM D790 | |
Notched Izod Impact | |||
23 °C | 500 J/m | ASTM D256 | |
23 °C;80*10*3 mm | 55 kJ/m² | ISO 180/1A | |
Instrumented Dart Impact, Total Energy(23 °C) | 50.0 J | ASTM D3763 | |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm | 90.0 °C 75.0 °C 82.0 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 92.0 °C | ASTM D1525 |
CLTE, Flow(-40 - 60 °C) | 7.1E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 60 °C) | 7.6E-5 cm/cm/°C | ASTM E831 |
RTI Elec | 60.0 °C | UL 746B |
RTI Imp | 60.0 °C | UL 746B |
RTI Str | 60.0 °C | UL 746B |
Flame Rating > 1.5 mm > 2 mm | V-0 5VB | UL 94 |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI( > 3 mm) | PLC 2 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.040 % | |
Suggested Shot Size<Injection> | 30 - 80 % | |
Rear Temperature<Injection> | 220 - 255 °C | |
Middle Temperature<injection> | 220 - 265 °C | |
Front Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Processing Temp, Melt<Injection> | 245 - 275 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.038 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 8 hr |
RCY6113-XH resin is a type of plastic that can be melted and shaped using injection molding. It is made by blending polycarbonate (PC) and acrylonitrile butadiene styrene (ABS), and it is made flame retardant without the use of bromine or chlorine. The resin also contains 30% recycled materials from consumer waste. It has been tested and received a UL-94 5VB rating at a thickness of 2.0mm, meaning it has good fire resistance, and a V0 rating at a thickness of 1.5mm, meaning it has even better fire resistance.
General | |||
Form |
| ||
Feature |
| ||
Usage |
| ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ASTM D792 | |
Melt Mass-Flow Rate, MFR(260 °C;2.16 kg) | 20 g/10min | ASTM D1238 | |
Molding Shrinkage, Across Flow(3.2 mm) | 0.30 - 0.50 % | Internal Method | |
Molding Shrinkage, Flow(3.2 mm) | 0.30 - 0.50 % | Internal Method | |
Water Absorption(24 hr;23 °C) | 0.11 % | ASTM D570 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus(50 mm/min) | 2500 MPa | ASTM D638 | |
Tensile Strength, Yield(50 mm/min;Type I) | 60.0 MPa | ASTM D638 | |
Tensile Strength, Break(50 mm/min;Type I) | 47.0 MPa | ASTM D638 | |
Tensile Elongation, Yield(50 mm/min;Type I) | 4.0 % | ASTM D638 | |
Tensile Elongation, Break(50 mm/min;Type I) | 60 % | ASTM D638 | |
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2400 MPa | ASTM D790 | |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 90.0 MPa | ASTM D790 | |
Notched Izod Impact | |||
23 °C | 500 J/m | ASTM D256 | |
23 °C;80*10*3 mm | 55 kJ/m² | ISO 180/1A | |
Instrumented Dart Impact, Total Energy(23 °C) | 50.0 J | ASTM D3763 | |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;6.4 mm 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm | 90.0 °C 75.0 °C 82.0 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 92.0 °C | ASTM D1525 |
CLTE, Flow(-40 - 60 °C) | 7.1E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 60 °C) | 7.6E-5 cm/cm/°C | ASTM E831 |
RTI Elec | 60.0 °C | UL 746B |
RTI Imp | 60.0 °C | UL 746B |
RTI Str | 60.0 °C | UL 746B |
Flame Rating > 1.5 mm > 2 mm | V-0 5VB | UL 94 |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI( > 3 mm) | PLC 2 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.040 % | |
Suggested Shot Size<Injection> | 30 - 80 % | |
Rear Temperature<Injection> | 220 - 255 °C | |
Middle Temperature<injection> | 220 - 265 °C | |
Front Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Processing Temp, Melt<Injection> | 245 - 275 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.038 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 8 hr |
Resin Pellets