W1000XiQ-XH
Forever
W1000XiQ-XH compound is a Poly butylene terephthalate (PBT) resin that incorporates ELCRIN iQ upcycling technology, providing at least 56% Post-Consumer Recycling (PCR) weight content. This grade offers additional benefits such as enhanced processing capabilities.
General | ||
Form | ||
Feature |
| |
Usage |
|
|
Physical | Nominal Value | Test Method |
Density / Specific Gravity |
1.31 1.31 g/cm³ |
ASTM D792 ISO 1183 |
Melt Flow Rate[MFR](250 °C;2.16 kgf) | 23 g/10min | ASTM D1238 |
Water Absorption(23 °C;saturated) | 0.16 % | ISO 62-1 |
Moisture Absorption(50% RH;23 °C) | 0.07 % | ISO 62 |
Melt Volume Rate, MVR(2.16 kg;MVR at 250 °C) | 21 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 50 J/m | ASTM D256 |
-30 °C | 46 J/m | ASTM D256 |
80*10*4;23 °C | 4 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 2 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 61 J | ASTM D3763 |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 5 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 56 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 29 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 3.2 % | ASTM D638 |
50 mm/min | 3 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2550 MPa | ASTM D638 |
1 mm/min | 2550 MPa | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 140 % | ASTM D638 |
50 mm/min | 130 % | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 84 MPa | ASTM D790 |
2 mm/min | 80 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2560 MPa | ASTM D790 |
2 mm/min | 2430 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 48 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.8E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.8E-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 8.1e-05 1/°C | ASTM E831 |
-40 - 40 °C | 8.1e-05 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 133 °C | ISO 75/Bf |
Vicat Softening Temperature(Rate B/120) | 168 °C | ISO 306 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 12 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 245 - 260 °C | |
Nozzle Temperature<Injection> | 240 - 255 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 260 °C | |
Middle, Zone 2 Temperature<Injection> | 240 - 255 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 250 °C | |
Mold Temperature<Injection> | 50 - 75 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 50 - 100 rpm | |
Shot To Cylinder Size<Injection> | 40 - 80 % | |
Vent Depth <Injection> | 0.013 - 0.025 mm |
W1000XiQ-XH compound is a Poly butylene terephthalate (PBT) resin that incorporates ELCRIN iQ upcycling technology, providing at least 56% Post-Consumer Recycling (PCR) weight content. This grade offers additional benefits such as enhanced processing capabilities.
General | ||
Form | ||
Feature |
| |
Usage |
|
|
Physical | Nominal Value | Test Method |
Density / Specific Gravity |
1.31 1.31 g/cm³ |
ASTM D792 ISO 1183 |
Melt Flow Rate[MFR](250 °C;2.16 kgf) | 23 g/10min | ASTM D1238 |
Water Absorption(23 °C;saturated) | 0.16 % | ISO 62-1 |
Moisture Absorption(50% RH;23 °C) | 0.07 % | ISO 62 |
Melt Volume Rate, MVR(2.16 kg;MVR at 250 °C) | 21 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 50 J/m | ASTM D256 |
-30 °C | 46 J/m | ASTM D256 |
80*10*4;23 °C | 4 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 2 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 61 J | ASTM D3763 |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 5 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 56 MPa | ASTM D638 |
50 mm/min | 55 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 29 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 3.2 % | ASTM D638 |
50 mm/min | 3 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2550 MPa | ASTM D638 |
1 mm/min | 2550 MPa | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 140 % | ASTM D638 |
50 mm/min | 130 % | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 84 MPa | ASTM D790 |
2 mm/min | 80 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2560 MPa | ASTM D790 |
2 mm/min | 2430 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 48 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 7.8E-05 1/°C | ASTM E831 |
-40 - 40 °C | 7.8E-05 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 8.1e-05 1/°C | ASTM E831 |
-40 - 40 °C | 8.1e-05 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 133 °C | ISO 75/Bf |
Vicat Softening Temperature(Rate B/120) | 168 °C | ISO 306 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 12 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 245 - 260 °C | |
Nozzle Temperature<Injection> | 240 - 255 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 260 °C | |
Middle, Zone 2 Temperature<Injection> | 240 - 255 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 250 °C | |
Mold Temperature<Injection> | 50 - 75 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 50 - 100 rpm | |
Shot To Cylinder Size<Injection> | 40 - 80 % | |
Vent Depth <Injection> | 0.013 - 0.025 mm |
Resin Pellets