PA6 with 30%GF Reinforced Natural Recycled PA6 Resin Engineering Plastics High Impact Polyamide

Form                                        Resin Pellets

Filler                                        30 % Glass Fiber

 High Impact                      Easy Release                         Excellent Mechanical

Feature

High Mechanical Strength

Automotive Industry      

(interior And Body Parts)

Physical                                                                                Nominal Value                                       Test Method

Density / Specific Gravity                                                     1.37 g/cm³                                             ISO 1183

Water Absorption(23 0 ℃)                                                  6.7 %                                                     ISO 62

Melt Volume Rate, MVR                                                       50 cm³/10 min                                      ISO 1133

Mechanical                                                                            Nominal Value                                     Test Method

Tensile Modulus                                                                   9500 MPa                                              ISO 527

Flexural Modulus                                                                  8500 MPa                                              ISO 178

Flexural Strength                                                                  270 MPa                                                 ISO 178

C harpy Impact Strength, Unnotched                                  95 kJ/m²                                                 ISO 179

C harpy Impact Strength, Notched(23 ℃)                            10 kJ/m²                                                ISO 179

Thermal                                                                                 Nominal Value                                      Test Method

Deflection Temperature Under Load, ISO                                                                                        ISO 75

1.8 MPa                                                                            210 °C

0.45 MPa                                                                             220 °C

CLTE, Transverse                                                                  0.25E-4 - 0.7E-4 /K                               ISO 11359

UL temperature rating                                                          HB                                                           UL 94

Melting Point(DSC)

220 °C

Processing

Nominal Value

Melt Temperature Range

270 - 290 °C

Mold temperature range

80 - 100 °C