PX13012-XH
Forever
PX13012-XH compound is a specialized Nylon 6 resin that has been enhanced with a unique thermal filler. This grade of resin boasts additional features such as high thermal conductivity, excellent electrical insulation properties, and is also non-brominated and non-chlorinated, making it a safe flame retardant material.
General | |||||
Form |
| ||||
Feature | Thermally Conductive | Non-Brominated & Non- Chlorinated Flame
| Non-Chlorinated Electrically Isolative | ||
Usage |
|
| |||
Physical | Nominal Value | Test Method | |||
Mold Shrinkage, Flow | |||||
24 hrs | 0.55 % | ASTM D955 | |||
24 hrs | 0.55 % | ISO 294 | |||
Mold Shrinkage, XFlow | |||||
24 hrs | 0.65 % | ASTM D955 | |||
24 hrs | 0.65 % | ISO 294 | |||
Density / Specific Gravity | 1.68 g/cm³ | ISO 1183 | |||
Water Absorption(24 hrs;23 °C) | 0.23 % | ISO 62-1 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 152 J/m | ASTM D4812 |
80*10*4;23 °C | 9 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 15 J/m | ASTM D256 |
80*10*4;23 °C | 3 kJ/m² | ISO 180/1A |
Tensile Stress, Yield(5 mm/min;Type I) | 68 MPa | ASTM D638 |
Tensile Strain, Break | ||
5 mm/min;Type I | 1.2 % | ASTM D638 |
5 mm/min | 1.1 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.0E+04 MPa | ASTM D638 |
1 mm/min | 1.3E+04 MPa | ISO 527 |
Flexural Stress, break(1.3 mm/min;50 mm;span) | 119 MPa | ASTM D790 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 1.2E+04 MPa | ASTM D790 |
2 mm/min | 1.2E+04 MPa | ISO 178 |
Tensile Stress, Break(5 mm/min) | 75 MPa | ISO 527 |
Flexural Stress, Yield(2 mm/min) | 105 MPa | ISO 178 |
Thermal Nominal Value | Test Method | |||
UL Recognized(≥ 0.8 mm) V-0 | UL 94 | |||
Glow Wire Ignition Temperature [GWIT] 0.8 mm 1.6 mm 3 mm |
750 °C 775 °C 800 °C | IEC 60695-2-13 | ||
Glow Wire Flammability Index 0.8 mm 1.6 mm 3 mm |
960 °C 960 °C 960 °C | IEC 60695-2-12 | ||
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) 203 °C | ASTM D648 | |||
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 137 °C | ASTM D648 | ||
CTE, Flow -40 - 40 °C -30°C to 80°C |
3.3E-05 3.9E-05 |
1/°C 1/°C |
ASTM E831 ISO 11359-2 | |
CTE, XFlow -40 - 40 °C -30°C to 80°C |
4.4E-05 1/°C 5.5e-05 1/°C |
ASTM E831 ISO 11359-2 | ||
Thermal conductivity through plane(60*60*3mm plaque) 1.2 W/m-K | ISO 22007-2 | |||
Thermal conductivity in plane(60*60*3mm plaque) 5.5 W/m-K | ISO 22007-2 | |||
Ball Pressure Test(165°C +/- 2°C) PASSES | IEC 60695-10-2 | |||
HDT/Bf(0.45) 203 °C | ISO 75/Bf | |||
HDT/Af(1.8) 160 °C | ISO 75/Af | |||
Relative Temp Index, Elec 130 °C | UL 746B | |||
Relative Temp Index, Mechanical with Impact 100 °C | UL 746B | |||
Relative Temp Index, Mechanical without Impact 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 4.0E+14 ohms | ASTM D257 |
Dielectric Strength, in Oil(1.6 mm) | 7.2 kV/mm | ASTM D149 |
Dielectric Strength(1.6 mm) | 6.1 kV/mm | IEC 60243-1 |
Comparative Tracking Index, CTI | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |
Hot-wire Ignition, HWI( ≥ 0.8 mm) | PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.25 % | |
Minimum Moisture Content<Injection> | 0.15 % | |
Melt Temperature<Injection> | 270 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
Mold Temperature<Injection> | 85 - 100 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 20 - 60 rpm |
PX13012-XH compound is a specialized Nylon 6 resin that has been enhanced with a unique thermal filler. This grade of resin boasts additional features such as high thermal conductivity, excellent electrical insulation properties, and is also non-brominated and non-chlorinated, making it a safe flame retardant material.
General | |||||
Form |
| ||||
Feature | Thermally Conductive | Non-Brominated & Non- Chlorinated Flame
| Non-Chlorinated Electrically Isolative | ||
Usage |
|
| |||
Physical | Nominal Value | Test Method | |||
Mold Shrinkage, Flow | |||||
24 hrs | 0.55 % | ASTM D955 | |||
24 hrs | 0.55 % | ISO 294 | |||
Mold Shrinkage, XFlow | |||||
24 hrs | 0.65 % | ASTM D955 | |||
24 hrs | 0.65 % | ISO 294 | |||
Density / Specific Gravity | 1.68 g/cm³ | ISO 1183 | |||
Water Absorption(24 hrs;23 °C) | 0.23 % | ISO 62-1 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 152 J/m | ASTM D4812 |
80*10*4;23 °C | 9 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 15 J/m | ASTM D256 |
80*10*4;23 °C | 3 kJ/m² | ISO 180/1A |
Tensile Stress, Yield(5 mm/min;Type I) | 68 MPa | ASTM D638 |
Tensile Strain, Break | ||
5 mm/min;Type I | 1.2 % | ASTM D638 |
5 mm/min | 1.1 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.0E+04 MPa | ASTM D638 |
1 mm/min | 1.3E+04 MPa | ISO 527 |
Flexural Stress, break(1.3 mm/min;50 mm;span) | 119 MPa | ASTM D790 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 1.2E+04 MPa | ASTM D790 |
2 mm/min | 1.2E+04 MPa | ISO 178 |
Tensile Stress, Break(5 mm/min) | 75 MPa | ISO 527 |
Flexural Stress, Yield(2 mm/min) | 105 MPa | ISO 178 |
Thermal Nominal Value | Test Method | |||
UL Recognized(≥ 0.8 mm) V-0 | UL 94 | |||
Glow Wire Ignition Temperature [GWIT] 0.8 mm 1.6 mm 3 mm |
750 °C 775 °C 800 °C | IEC 60695-2-13 | ||
Glow Wire Flammability Index 0.8 mm 1.6 mm 3 mm |
960 °C 960 °C 960 °C | IEC 60695-2-12 | ||
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) 203 °C | ASTM D648 | |||
Heat Deflection Temperature[HDT], Unannealed(3.2 mm;1.82 MPa) | 137 °C | ASTM D648 | ||
CTE, Flow -40 - 40 °C -30°C to 80°C |
3.3E-05 3.9E-05 |
1/°C 1/°C |
ASTM E831 ISO 11359-2 | |
CTE, XFlow -40 - 40 °C -30°C to 80°C |
4.4E-05 1/°C 5.5e-05 1/°C |
ASTM E831 ISO 11359-2 | ||
Thermal conductivity through plane(60*60*3mm plaque) 1.2 W/m-K | ISO 22007-2 | |||
Thermal conductivity in plane(60*60*3mm plaque) 5.5 W/m-K | ISO 22007-2 | |||
Ball Pressure Test(165°C +/- 2°C) PASSES | IEC 60695-10-2 | |||
HDT/Bf(0.45) 203 °C | ISO 75/Bf | |||
HDT/Af(1.8) 160 °C | ISO 75/Af | |||
Relative Temp Index, Elec 130 °C | UL 746B | |||
Relative Temp Index, Mechanical with Impact 100 °C | UL 746B | |||
Relative Temp Index, Mechanical without Impact 130 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Surface Resistivity | 4.0E+14 ohms | ASTM D257 |
Dielectric Strength, in Oil(1.6 mm) | 7.2 kV/mm | ASTM D149 |
Dielectric Strength(1.6 mm) | 6.1 kV/mm | IEC 60243-1 |
Comparative Tracking Index, CTI | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |
Hot-wire Ignition, HWI( ≥ 0.8 mm) | PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.25 % | |
Minimum Moisture Content<Injection> | 0.15 % | |
Melt Temperature<Injection> | 270 - 295 °C | |
Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
Mold Temperature<Injection> | 85 - 100 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 20 - 60 rpm |