C2950HF-XH
Forever
Non-chlorinated and non-brominated flame retardant PC/ABS provides a well-rounded combination of impact resistance, heat resistance, and improved flow for a wide range of applications.
General | |||
Form |
| ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.18 g/cm³ | ASTM D792 | |
Water Absorption(Time 24 hr) | 0.10 % | ASTM D570 | |
Moisture Absorption at Equilibrium | 0.40 % | ASTM D570 | |
Linear Mold Shrinkage, Flow(Thickness; 3.2 mm) | 0.4 - 0.6 % | ||
Linear Mold Shrinkage, Transverse(Thickness; 3.2 mm) | 0.4 - 0.6 % | ||
Melt Flow(2.16 kg;260 °C) | 22 g/10min | ASTM D1238 | |
Hardness, Rockwell R | 121 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength, Yield(50 mm/min) | 64.0 MPa | ASTM D638-1 | |
Elongation at Break(50 mm/min) | 40 % | ASTM D638-1 | |
Elongation at Yield(50 mm/min) | 5.0 % | ASTM D638-1 | |
Flexural Yield Strength | 96.0 MPa | ASTM D790 | |
Flexural Modulus | 2580 MPa | ASTM D790 | |
Izod Impact, Notched(Temperature; 23 °C) | 453 J/m | ASTM D256 | |
Dart Drop, Total Energy(Peak Energy) | 54.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
CTE, Flow(Temperature; -30 - 30 °C) | 72.0 µm/m-°C | ASTM D696 |
CLTE, Transverse(Temperature; -30 - 30 °C) | 72.0 µm/m-°C | ASTM D696 |
Thermal Conductivity | 0.200 W/m-K | ASTM C177 |
Deflection Temperature Thickness; 6.4 mm;Pressure; 0.46 MPa Thickness; 3.2 mm;Pressure; 1.8 MPa Thickness; 6.4 mm;Pressure; 1.8 MPa |
101 °C 87.0 °C 93.0 °C | ASTM D648 |
Vicat Softening Point(Rate B/50) | 112 °C | ASTM D1525 |
UL RTI, Electrical | 85.0 °C | UL 746B |
UL RTI, Mechanical with Impact | 85.0 °C | UL 746B |
UL RTI, Mechanical without Impact | 85.0 °C | UL 746B |
Flammability, UL94 Thickness; 0.76 mm Thickness; 1.49 mm Thickness; 2.48 mm 3.4 mm |
V-2 V-0 5VB 5VA | UL 94 |
Oxygen Index | 30 % | ASTM D2863 |
Hot Wire Ignition, HWI | 30 - 60 sec | UL 746A |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.60e+17 ohms ·cm | ASTM D257 |
Surface Resistance | > = 1.00e+16 Ohms | ASTM D257 |
Dielectric Constant Frequency; 1.0e+6 Hz Frequency; 50 - 60 Hz |
2.7 2.8 | ASTM D150 |
Dielectric Strength(Thickness; 3.2 mm;In Oil) | 24.3 kV/mm | ASTM D149 |
Dissipation Factor Frequency; 50 - 60 Hz Frequency; 1.0e+6 Hz |
0.0052 0.0071 | ASTM D150 |
Arc Resistance(Tungsten) | 60 - 120 sec | ASTM D495 |
Comparative Tracking Index | 250 - 400 V | UL 746A |
High Amp Arc Ignition, HAI | > = 120 arcs | UL 746A |
High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | UL 746A |
Processing | Nominal Value |
Injection Molding | |
Drying Temperature | 80 - 90 °C |
Drying Time | 3 - 4 hrs |
Drying Time, Cumulative | 8 hrs |
Maximum Moisture Content | 0.04 % |
Melt Temperature | 245 - 275 °C |
Nozzle Temperature | 245 - 275 °C |
Front - Zone 3 Temperature | 245 - 275 °C |
Middle - Zone 2 Temperature | 220 - 265 °C |
Rear - Zone 1 Temperature | 220 - 255 °C |
Mold Temperature | 60 - 80 °C |
Back Pressure | 0.3 - 0.7 MPa |
Screw Speed | 40 - 70 rpm |
Shot to Cylinder Size | 30 - 80 % |
Vent Depth | 0.038 - 0.076 mm |
Non-chlorinated and non-brominated flame retardant PC/ABS provides a well-rounded combination of impact resistance, heat resistance, and improved flow for a wide range of applications.
General | |||
Form |
| ||
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.18 g/cm³ | ASTM D792 | |
Water Absorption(Time 24 hr) | 0.10 % | ASTM D570 | |
Moisture Absorption at Equilibrium | 0.40 % | ASTM D570 | |
Linear Mold Shrinkage, Flow(Thickness; 3.2 mm) | 0.4 - 0.6 % | ||
Linear Mold Shrinkage, Transverse(Thickness; 3.2 mm) | 0.4 - 0.6 % | ||
Melt Flow(2.16 kg;260 °C) | 22 g/10min | ASTM D1238 | |
Hardness, Rockwell R | 121 | ASTM D785 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength, Yield(50 mm/min) | 64.0 MPa | ASTM D638-1 | |
Elongation at Break(50 mm/min) | 40 % | ASTM D638-1 | |
Elongation at Yield(50 mm/min) | 5.0 % | ASTM D638-1 | |
Flexural Yield Strength | 96.0 MPa | ASTM D790 | |
Flexural Modulus | 2580 MPa | ASTM D790 | |
Izod Impact, Notched(Temperature; 23 °C) | 453 J/m | ASTM D256 | |
Dart Drop, Total Energy(Peak Energy) | 54.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
CTE, Flow(Temperature; -30 - 30 °C) | 72.0 µm/m-°C | ASTM D696 |
CLTE, Transverse(Temperature; -30 - 30 °C) | 72.0 µm/m-°C | ASTM D696 |
Thermal Conductivity | 0.200 W/m-K | ASTM C177 |
Deflection Temperature Thickness; 6.4 mm;Pressure; 0.46 MPa Thickness; 3.2 mm;Pressure; 1.8 MPa Thickness; 6.4 mm;Pressure; 1.8 MPa |
101 °C 87.0 °C 93.0 °C | ASTM D648 |
Vicat Softening Point(Rate B/50) | 112 °C | ASTM D1525 |
UL RTI, Electrical | 85.0 °C | UL 746B |
UL RTI, Mechanical with Impact | 85.0 °C | UL 746B |
UL RTI, Mechanical without Impact | 85.0 °C | UL 746B |
Flammability, UL94 Thickness; 0.76 mm Thickness; 1.49 mm Thickness; 2.48 mm 3.4 mm |
V-2 V-0 5VB 5VA | UL 94 |
Oxygen Index | 30 % | ASTM D2863 |
Hot Wire Ignition, HWI | 30 - 60 sec | UL 746A |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.60e+17 ohms ·cm | ASTM D257 |
Surface Resistance | > = 1.00e+16 Ohms | ASTM D257 |
Dielectric Constant Frequency; 1.0e+6 Hz Frequency; 50 - 60 Hz |
2.7 2.8 | ASTM D150 |
Dielectric Strength(Thickness; 3.2 mm;In Oil) | 24.3 kV/mm | ASTM D149 |
Dissipation Factor Frequency; 50 - 60 Hz Frequency; 1.0e+6 Hz |
0.0052 0.0071 | ASTM D150 |
Arc Resistance(Tungsten) | 60 - 120 sec | ASTM D495 |
Comparative Tracking Index | 250 - 400 V | UL 746A |
High Amp Arc Ignition, HAI | > = 120 arcs | UL 746A |
High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | UL 746A |
Processing | Nominal Value |
Injection Molding | |
Drying Temperature | 80 - 90 °C |
Drying Time | 3 - 4 hrs |
Drying Time, Cumulative | 8 hrs |
Maximum Moisture Content | 0.04 % |
Melt Temperature | 245 - 275 °C |
Nozzle Temperature | 245 - 275 °C |
Front - Zone 3 Temperature | 245 - 275 °C |
Middle - Zone 2 Temperature | 220 - 265 °C |
Rear - Zone 1 Temperature | 220 - 255 °C |
Mold Temperature | 60 - 80 °C |
Back Pressure | 0.3 - 0.7 MPa |
Screw Speed | 40 - 70 rpm |
Shot to Cylinder Size | 30 - 80 % |
Vent Depth | 0.038 - 0.076 mm |