C3650-XH
FOREVER
Forever's flame retardant PC/ABS blend - the perfect solution for those who require both safety and performance.
Our blend is designed using non-brominated and non-chlorinated flame retardant systems, ensuring the highest level of safety for your application.
It offers an exceptional combination of high impact strength and excellent extrusion and thermoforming characteristics, making it ideal for a wide range of uses. Additionally, it is halogen free according to DIN VDE 0472/815, making it an excellent choice for cable channels.
General | ||||
Form |
| |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.20 g/cm³ 1.18 g/cm³ |
ASTM D792 ISO 1183 | ||
Water Absorption at Saturation | 0.60 % | ASTM D570 | ||
Linear Mold Shrinkage, Flow(Thickness; 3.2 | mm) | 0.4 - 0.6 % | ||
Melt Flow(5 kg;260 °C) | 8.5 g/10min | ASTM D1238 | ||
Melt Volume Rate, MVR(5 kg;260 °C) | 8.0 cm³/10 min | ISO 1133 | ||
Hardness, Rockwell R | 124 | ISO 2039-2 | ||
Ball Indentation Hardness(H 358/30) | 113 MPa | ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Break
50 mm/min |
50.0 MPa 55.0 MPa 51.0 MPa |
ISO 527 ISO 527 ASTM D638-1 | ||
Tensile Strength, Yield
50 mm/min |
55.0 MPa 65.0 MPa 64.0 MPa |
ISO 527 ISO 527 ASTM D638-1 | ||
Elongation at Break 50 mm/min |
35 % > = 50 % 55 % |
ASTM D638-1 ISO 527 ISO 527 | ||
Elongation at Yield
50 mm/min |
3.0 % 4.5 % 4.9 % |
ISO 527 ISO 527 ASTM D638-1 |
Tensile Modulus |
2600 MPa |
ISO 527 |
2860 MPa | ASTM D638 | |
Flexural Yield Strength
1.3 mm/min;50 mm;span |
100 MPa 101 MPa |
ISO 178 ASTM D790 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2680 MPa 2700 MPa | ASTM D790 ISO 178 |
Izod Impact, Notched(Temperature; 23 °C) | 694 J/m | ASTM D256 |
Izod Impact, Notched, ISO Temperature; 23 °C;80x10x4 mm Temperature; -30 °C;80x10x4 mm Temperature; 0 °C;80x10x4 mm |
45.0 kJ/m² 13.0 kJ/m² 15.0 kJ/m² | ISO 180/1A |
Charpy Impact, Notched Temperature; 23 °C Temperature; -30 °C |
48 kJ/m² 13 kJ/m² | ISO 179 1eA |
Dart Drop, Total Energy(Temperature; 23 °C) | 64.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
CTE, Flow Temperature; -40 - 40 °C 23 - 60 °C |
72.0 µm/m-°C 80.0 µm/m-°C |
ASTM E831 ISO 11359-2 |
CLTE, Transverse Temperature; -40 - 40 °C 23 - 60 °C |
72.0 µm/m-°C 80.0 µm/m-°C |
ASTM E831 ISO 11359-2 |
Thermal Conductivity | 0.200 W/m-K | ISO 8302 |
Deflection Temperature | ||
Pressure; 0.46 MPa;Edgew;120*10*4;sp=100mm 0 | 102 °C | ISO 75/Be |
Thickness; 3.2 mm;Pressure; 0.46 MPa | 100 °C | ASTM D648 |
Thickness; 3.2 mm;Pressure; 1.8 MPa | 88.0 °C | ASTM D648 |
Pressure; 1.8 MPa;Edgew;120*10*4;sp=100mm 0 | 91.0 °C | ISO 75/Ae |
Vicat Softening Point | ||
Rate B/50 | 108 °C | ISO 306 |
Rate B/120 | 110 °C | ISO 306 |
Rate B/50 | 110 °C | ASTM D1525 |
UL RTI, Electrical | 60.0 °C | UL 746B |
UL RTI, Mechanical with Impact | 60.0 °C | UL 746B |
UL RTI, Mechanical without Impact | 60.0 °C | UL 746B |
Flammability, UL94 Thickness; 1.49 mm Thickness; 2.48 mm |
V-0 5VB | UL 94 |
Oxygen Index | 37 % | ISO 4589 |
Forever's flame retardant PC/ABS blend - the perfect solution for those who require both safety and performance.
Our blend is designed using non-brominated and non-chlorinated flame retardant systems, ensuring the highest level of safety for your application.
It offers an exceptional combination of high impact strength and excellent extrusion and thermoforming characteristics, making it ideal for a wide range of uses. Additionally, it is halogen free according to DIN VDE 0472/815, making it an excellent choice for cable channels.
General | ||||
Form |
| |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.20 g/cm³ 1.18 g/cm³ |
ASTM D792 ISO 1183 | ||
Water Absorption at Saturation | 0.60 % | ASTM D570 | ||
Linear Mold Shrinkage, Flow(Thickness; 3.2 | mm) | 0.4 - 0.6 % | ||
Melt Flow(5 kg;260 °C) | 8.5 g/10min | ASTM D1238 | ||
Melt Volume Rate, MVR(5 kg;260 °C) | 8.0 cm³/10 min | ISO 1133 | ||
Hardness, Rockwell R | 124 | ISO 2039-2 | ||
Ball Indentation Hardness(H 358/30) | 113 MPa | ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Break
50 mm/min |
50.0 MPa 55.0 MPa 51.0 MPa |
ISO 527 ISO 527 ASTM D638-1 | ||
Tensile Strength, Yield
50 mm/min |
55.0 MPa 65.0 MPa 64.0 MPa |
ISO 527 ISO 527 ASTM D638-1 | ||
Elongation at Break 50 mm/min |
35 % > = 50 % 55 % |
ASTM D638-1 ISO 527 ISO 527 | ||
Elongation at Yield
50 mm/min |
3.0 % 4.5 % 4.9 % |
ISO 527 ISO 527 ASTM D638-1 |
Tensile Modulus |
2600 MPa |
ISO 527 |
2860 MPa | ASTM D638 | |
Flexural Yield Strength
1.3 mm/min;50 mm;span |
100 MPa 101 MPa |
ISO 178 ASTM D790 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2680 MPa 2700 MPa | ASTM D790 ISO 178 |
Izod Impact, Notched(Temperature; 23 °C) | 694 J/m | ASTM D256 |
Izod Impact, Notched, ISO Temperature; 23 °C;80x10x4 mm Temperature; -30 °C;80x10x4 mm Temperature; 0 °C;80x10x4 mm |
45.0 kJ/m² 13.0 kJ/m² 15.0 kJ/m² | ISO 180/1A |
Charpy Impact, Notched Temperature; 23 °C Temperature; -30 °C |
48 kJ/m² 13 kJ/m² | ISO 179 1eA |
Dart Drop, Total Energy(Temperature; 23 °C) | 64.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
CTE, Flow Temperature; -40 - 40 °C 23 - 60 °C |
72.0 µm/m-°C 80.0 µm/m-°C |
ASTM E831 ISO 11359-2 |
CLTE, Transverse Temperature; -40 - 40 °C 23 - 60 °C |
72.0 µm/m-°C 80.0 µm/m-°C |
ASTM E831 ISO 11359-2 |
Thermal Conductivity | 0.200 W/m-K | ISO 8302 |
Deflection Temperature | ||
Pressure; 0.46 MPa;Edgew;120*10*4;sp=100mm 0 | 102 °C | ISO 75/Be |
Thickness; 3.2 mm;Pressure; 0.46 MPa | 100 °C | ASTM D648 |
Thickness; 3.2 mm;Pressure; 1.8 MPa | 88.0 °C | ASTM D648 |
Pressure; 1.8 MPa;Edgew;120*10*4;sp=100mm 0 | 91.0 °C | ISO 75/Ae |
Vicat Softening Point | ||
Rate B/50 | 108 °C | ISO 306 |
Rate B/120 | 110 °C | ISO 306 |
Rate B/50 | 110 °C | ASTM D1525 |
UL RTI, Electrical | 60.0 °C | UL 746B |
UL RTI, Mechanical with Impact | 60.0 °C | UL 746B |
UL RTI, Mechanical without Impact | 60.0 °C | UL 746B |
Flammability, UL94 Thickness; 1.49 mm Thickness; 2.48 mm |
V-0 5VB | UL 94 |
Oxygen Index | 37 % | ISO 4589 |