Multi Functional PC/ABS Blend Raw Materials, Containing Stainless Steel Fibers And Glass Fibers.

Form

Resin Pellets

Feature

Electrically Conductive

 Emi/Rfi Shielding

Non-Brominated & Non- Chlorinated Flame Retardant

Usage

Consumer

Electrical

 Packaging

 Industria

Physical

Nominal Value

Test Method

Density / Specific Gravity

1.46 g/cm³

1.46 g/cm³

ASTM D792

ISO 1183

Moisture Absorption

23 °C;50% RH/24 hrs

0.08 %

ASTM D570

50% RH;23 °C

0.04 %

ISO 62

Izod Impact, Unnotched

23 °C

350 J/m

ASTM D4812

-30 °C

330 J/m

ASTM D4812

80*10*4;23 °C

21 kJ/m²

ISO 180/1U

80*10*4;-30 °C

21 kJ/m²

ISO 180/1U

Izod Impact, Notched

23 °C

60 J/m

ASTM D256

-30 °C

44 J/m

ASTM D256

80*10*4;23 °C

6 kJ/m²

ISO 180/1A

80*10*4;-30 °C

5 kJ/m²

ISO 180/1A

Multiaxial Impact

4 J

ISO 6603

Instrumented Dart Impact, Total Energy(23 °C)

11 J

ASTM D3763

C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0)

7 kJ/m²

ISO 179 1eA

Tensile Stress, Break

5 mm/min;Type I

60 MPa

ASTM D638

5 mm/min

62 MPa

ISO 527

Tensile Strain, Break

5 mm/min;Type I

1.8 %

ASTM D638

5 mm/min

1.8 %

ISO 527

Tensile Modulus

50 mm/min

6000 MPa

ASTM D638

1 mm/min

5800 MPa

ISO 527

Flexural Stress, Yield

1.3 mm/min;50 mm;span

90 MPa

ASTM D790

2 mm/min

105 MPa

ISO 178

Flexural Stress, break(1.3 mm/min;50 mm;span)

90 MPa

ASTM D790

Flexural Modulus(1.3 mm/min;50 mm;span)

5300 MPa

ASTM D790

Flexural Strain, Break(2 mm/min)

2.8 %

ISO 178

UL Recognized(1.5 mm)

V-0

UL 94

Vicat Softening Temperature

Rate A/50

101 °C

ASTM D1525

Rate B/50

105 °C

ASTM D1525

Rate A/50

102 °C

ISO 306

Rate B/120

105 °C

ISO 306

Heat Deflection Temperature[HDT], Unannealed

3.2 mm;1.82 MPa

1.82 MPa;6.4 mm

94 °C

96 °C

ASTM D648

CTE, Flow

-40 - 40 °C

3.1E-05 1/°C

ASTM E831

23°C to 60°C

2.9E-05 1/°C

ISO 11359-2

CTE, XFlow

-40 - 40 °C

5.8E-05 1/°C

ASTM E831

23°C to 60°C

7.4E-05 1/°C

ISO 11359-2

HDT/Af(1.8)

96 °C

ISO 75/Af

Relative Temp Index, Elec

60 °C

UL 746B

Relative Temp Index, Mechanical with Impact

60 °C

UL 746B

Relative Temp Index, Mechanical without Impact

60 °C

UL 746B

Electrical

Nominal Value

Test Method

Volume Resistivity

1.0E+04 - 1.0E+06 ohms ·cm

ASTM D257

Surface Resistivity

1000 - 1.0E+06 ohms

ASTM D257

Static Decay(5000V to <50V)

< 0.01 Seconds

FTMS101B

Drying Temperature<Injection>

85 - 90 °C

Drying Time<Injection>

3 - 4 hrs

Maximum Moisture Content<Injection>

0.04 %

Melt Temperature<Injection>

270 - 300 °C

Nozzle Temperature<Injection>

265 - 300 °C

Front, Zone 3 Temperature<Injection>

265 - 300 °C

Middle, Zone 2 Temperature<Injection>

260 - 300 °C

Rear, Zone 1 Temperature<Injection>

260 - 300 °C

Mold Temperature<Injection>

60 - 100 °C

Back Pressure<Injection>

4 MPa

Screw Speed <Injection>

30 - 100 rpm