MC8100-XH
Forever
MC8100-XH, a modified plastic, has better properties than pure PC and ABS, such as improved impact resistance, heat resistance, and hardness. Easy for injection molding, extrusion, and blow molding processing.
General | ||
Form | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.13 g/cm³ | ASTM D792 |
Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.70 % | Internal Method |
Water Absorption(24 hr) | 0.10 % | ASTM D570 |
Water Absorption, Equilibrium(23 °C) | 0.40 % | ASTM D570 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus(50 mm/min) | 2060 MPa | ASTM D638 |
Tensile Strength, Yield(50 mm/min;Type I) | 52.0 MPa | ASTM D638 |
Tensile Elongation, Yield(50 mm/min;Type I) | 5.0 % | ASTM D638 |
Tensile Elongation, Break(50 mm/min;Type I) | 100 % | ASTM D638 |
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2060 MPa | ASTM D790 |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 77.0 MPa | ASTM D790 |
Notched Izod Impact -30 °C 23 °C | 430 J/m 530 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy -30 °C 23 °C | 47.0 J 54.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm | 123 °C 104 °C | ASTM D648 |
CLTE, Flow(-40 - 40 °C) | 8.1E-5 cm/cm/°C | ASTM E831 |
Thermal Conductivity | 0.20 W/m-K | ASTM C177 |
Processing | Nominal Value |
Drying Temperature<Extrusion Blow Molding> | 100 - 110 °C |
Drying Time | 3 - 4 hrs |
Drying Time, Cumulative<Extrusion Blow Molding> | 24 hrs |
Minimum Moisture Content<Extrusion Blow Molding> | 0.04 % |
Maximum Moisture Content<Extrusion Blow Molding> | 0.04 - 0.05 % |
Melt Temperature, Parison | 245 - 260 °C |
Barrel - Zone 1 Temperature<Extrusion Blow Molding> | 240 - 250 °C |
Barrel - Zone 2 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
Barrel - Zone 3 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
Barrel - Zone 4 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
Adapter - Zone 5 Temperature<Extrusion Blow Molding> | 245 - 260 °C |
Head - Zone 6 - Top Temperature<Extrusion Blow Molding> | 245 - 260 °C |
Head - Zone 7 - Bottom Temperature<Extrusion Blow Molding> | 245 - 260 °C |
Screw Speed <Extrusion Blow Molding> | 20 - 50 rpm |
Extruder Feed Zone Temperature<Extrusion Blow Molding> | 60 - 80 °C |
Mold Temperature<Extrusion Blow Molding> | 40 - 90 °C |
Die Temperature<Extrusion Blow Molding> | 250 - 265 °C |
MC8100-XH, a modified plastic, has better properties than pure PC and ABS, such as improved impact resistance, heat resistance, and hardness. Easy for injection molding, extrusion, and blow molding processing.
General | ||
Form | ||
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.13 g/cm³ | ASTM D792 |
Molding Shrinkage, Flow(3.2 mm) | 0.40 - 0.70 % | Internal Method |
Water Absorption(24 hr) | 0.10 % | ASTM D570 |
Water Absorption, Equilibrium(23 °C) | 0.40 % | ASTM D570 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus(50 mm/min) | 2060 MPa | ASTM D638 |
Tensile Strength, Yield(50 mm/min;Type I) | 52.0 MPa | ASTM D638 |
Tensile Elongation, Yield(50 mm/min;Type I) | 5.0 % | ASTM D638 |
Tensile Elongation, Break(50 mm/min;Type I) | 100 % | ASTM D638 |
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2060 MPa | ASTM D790 |
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 77.0 MPa | ASTM D790 |
Notched Izod Impact -30 °C 23 °C | 430 J/m 530 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy -30 °C 23 °C | 47.0 J 54.0 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm | 123 °C 104 °C | ASTM D648 |
CLTE, Flow(-40 - 40 °C) | 8.1E-5 cm/cm/°C | ASTM E831 |
Thermal Conductivity | 0.20 W/m-K | ASTM C177 |
Processing | Nominal Value |
Drying Temperature<Extrusion Blow Molding> | 100 - 110 °C |
Drying Time | 3 - 4 hrs |
Drying Time, Cumulative<Extrusion Blow Molding> | 24 hrs |
Minimum Moisture Content<Extrusion Blow Molding> | 0.04 % |
Maximum Moisture Content<Extrusion Blow Molding> | 0.04 - 0.05 % |
Melt Temperature, Parison | 245 - 260 °C |
Barrel - Zone 1 Temperature<Extrusion Blow Molding> | 240 - 250 °C |
Barrel - Zone 2 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
Barrel - Zone 3 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
Barrel - Zone 4 Temperature<Extrusion Blow Molding> | 240 - 255 °C |
Adapter - Zone 5 Temperature<Extrusion Blow Molding> | 245 - 260 °C |
Head - Zone 6 - Top Temperature<Extrusion Blow Molding> | 245 - 260 °C |
Head - Zone 7 - Bottom Temperature<Extrusion Blow Molding> | 245 - 260 °C |
Screw Speed <Extrusion Blow Molding> | 20 - 50 rpm |
Extruder Feed Zone Temperature<Extrusion Blow Molding> | 60 - 80 °C |
Mold Temperature<Extrusion Blow Molding> | 40 - 90 °C |
Die Temperature<Extrusion Blow Molding> | 250 - 265 °C |
Resin Pellets