WF0061iQ-XH
Forever
The WF0061iQ-XH compound is made from Poly butylene terephthalate (PBT) resin using ELCRIN iQ upcycling technology, which incorporates a minimum of 25% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. This grade offers additional advantages such as being Non-Chlorinated, Non-Brominated Flame Retardant, having a UL94V0 and 5VA Flame Rating, and displaying excellent chemical resistance. It is an ideal option for various applications that require a more sustainable flame retardant (FR) and PBT solution.
General | ||||
Form | Resin Pellets | |||
Filler | 30 % Glass Fiber | |||
Feature | Good Hardness 25 % Pcr | Non-Brominated & Non- Chlorinated Flame Retardant | ||
Chemical Resistant Non-Chlorinated |
| |||
Uses |
|
| ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.56 1.56 g/cm³ | ASTM D792 ISO 1183 | ||
Water Absorption(23 °C;saturated) | 0.23 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.09 % | ISO 62 | ||
Melt Volume Rate, MVR(5 kg;MVR at 250 °C) | 16 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 570 J/m | ASTM D4812 |
80*10*4;23 °C | 37 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 72 J/m | ASTM D256 |
-30 °C | 55 J/m | ASTM D256 |
80*10*4;23 °C | 7 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 6 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 6 J | ASTM D3763 |
Tensile Stress, Yield | ||
5 mm/min;Type I | 105 MPa | ASTM D638 |
5 mm/min | 108 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 105 MPa | ASTM D638 |
5 mm/min | 108 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 2 % | ASTM D638 |
5 mm/min | 2 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 2 % | ASTM D638 |
5 mm/min | 2 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.1E+04 MPa | ASTM D638 |
1 mm/min | 1.1E+04 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 165 MPa | ASTM D790 |
2 mm/min | 175 MPa | ISO 178 |
Flexural Stress, break | ||
1.3 mm/min;50 mm;span | 165 MPa | ASTM D790 |
2 mm/min | 175 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 9600 MPa | ASTM D790 |
2 mm/min | 1.0E+04 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 0.8 mm ≥ 3 mm | V-0 5VB | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm 0.8 mm | 800 °C 775 °C 750 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 0.8 mm | 960 °C 960 °C 960 °C | IEC 60695-2-12 |
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm | 200 °C 214 °C | ASTM D648 |
CTE, Flow(-40 - 40 °C) | 2.4E-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 8.0e-05 1/°C | ASTM E831 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
Relative Temp Index, Elec | 75 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 75 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 75 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI ≥ 0.8 mm ≥ 3 mm | PLC 1 PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |
The WF0061iQ-XH compound is made from Poly butylene terephthalate (PBT) resin using ELCRIN iQ upcycling technology, which incorporates a minimum of 25% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. This grade offers additional advantages such as being Non-Chlorinated, Non-Brominated Flame Retardant, having a UL94V0 and 5VA Flame Rating, and displaying excellent chemical resistance. It is an ideal option for various applications that require a more sustainable flame retardant (FR) and PBT solution.
General | ||||
Form | Resin Pellets | |||
Filler | 30 % Glass Fiber | |||
Feature | Good Hardness 25 % Pcr | Non-Brominated & Non- Chlorinated Flame Retardant | ||
Chemical Resistant Non-Chlorinated |
| |||
Uses |
|
| ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.56 1.56 g/cm³ | ASTM D792 ISO 1183 | ||
Water Absorption(23 °C;saturated) | 0.23 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.09 % | ISO 62 | ||
Melt Volume Rate, MVR(5 kg;MVR at 250 °C) | 16 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 570 J/m | ASTM D4812 |
80*10*4;23 °C | 37 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 72 J/m | ASTM D256 |
-30 °C | 55 J/m | ASTM D256 |
80*10*4;23 °C | 7 kJ/m² | ISO 180/1A |
80*10*4;-30 °C | 6 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 6 J | ASTM D3763 |
Tensile Stress, Yield | ||
5 mm/min;Type I | 105 MPa | ASTM D638 |
5 mm/min | 108 MPa | ISO 527 |
Tensile Stress, Break | ||
5 mm/min;Type I | 105 MPa | ASTM D638 |
5 mm/min | 108 MPa | ISO 527 |
Tensile Strain, Yield | ||
5 mm/min;Type I | 2 % | ASTM D638 |
5 mm/min | 2 % | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 2 % | ASTM D638 |
5 mm/min | 2 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.1E+04 MPa | ASTM D638 |
1 mm/min | 1.1E+04 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 165 MPa | ASTM D790 |
2 mm/min | 175 MPa | ISO 178 |
Flexural Stress, break | ||
1.3 mm/min;50 mm;span | 165 MPa | ASTM D790 |
2 mm/min | 175 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 9600 MPa | ASTM D790 |
2 mm/min | 1.0E+04 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 0.8 mm ≥ 3 mm | V-0 5VB | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm 0.8 mm | 800 °C 775 °C 750 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm 0.8 mm | 960 °C 960 °C 960 °C | IEC 60695-2-12 |
Heat Deflection Temperature[HDT], Unannealed 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm | 200 °C 214 °C | ASTM D648 |
CTE, Flow(-40 - 40 °C) | 2.4E-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 8.0e-05 1/°C | ASTM E831 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
Relative Temp Index, Elec | 75 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 75 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 75 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Hot-wire Ignition, HWI ≥ 0.8 mm ≥ 3 mm | PLC 1 PLC 0 | UL 746A |
High Amp Arc Ignition, HAI( ≥ 0.8 mm) | PLC 0 | UL 746A |
Comparative Tracking Index | 600 V | IEC 60112 |