Availability: | |
---|---|
Quantity: | |
CS9610-XH
Forever
CS9610-XH is a type of Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend that is suitable for injection molding. It is designed to have low smoke emission and is free from chlorinated or brominated flame retardants. This grade exhibits excellent mechanical strength and impact resistance. Moreover, it has achieved a UL94 V0@2.0mm and 5VB@2.0mm flame rating, indicating its high flame retardancy.
General | ||||||
Form |
| |||||
Feature | Aeroplane Application
Non-Chlorinated |
| Non-Brominated & Non- Chlorinated Flame Retardant | |||
Usage | Electrical |
| ||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.2 | ASTM D792 | ||||
Melt Flow Rate[MFR](260 | °C;5 | kgf) | 15 g/10min | ASTM D1238 | ||
Melt Volume Rate, MVR(5 kg;MVR at 260 °C) | 12 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched(23 °C) | 800 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 72 J | ASTM D3763 |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
45 kJ/m² 15 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
45 kJ/m² 15 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 64 MPa | ASTM D638 |
50 mm/min | 62 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 62 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 5 % | ASTM D638 |
50 mm/min | 4.8 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 55 % | ASTM D638 |
50 mm/min | > 45 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2600 MPa | ASTM D638 |
1 mm/min | 2400 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 98 MPa | ASTM D790 |
2 mm/min | 98 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2440 MPa | ASTM D790 |
2 mm/min | 2500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2 mm ≥ 2 mm |
5VB V-0 | UL 94 |
NBS Smoke Density, Flaming, Dmax | 225 | ASTM E662 |
NBS Smoke Density, Flaming Ds 1.5 min Ds 4 min |
40 150 | ASTM E662 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
118 °C 105 °C | ASTM D648 |
Vicat Softening Temperature Rate B/50 Rate B/120 |
124 °C 127 °C | ISO 306 |
HDT/Af(1.8) | 106 °C | ISO 75/Af |
Relative Temp Index, Elec | 90 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 90 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 90 °C | UL 746B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 90 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 270 - 300 °C | |
Nozzle Temperature<Injection> | 265 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 265 - 300 °C | |
Middle, Zone 2 Temperature<Injection> | 260 - 300 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 300 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 90 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |
CS9610-XH is a type of Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend that is suitable for injection molding. It is designed to have low smoke emission and is free from chlorinated or brominated flame retardants. This grade exhibits excellent mechanical strength and impact resistance. Moreover, it has achieved a UL94 V0@2.0mm and 5VB@2.0mm flame rating, indicating its high flame retardancy.
General | ||||||
Form |
| |||||
Feature | Aeroplane Application
Non-Chlorinated |
| Non-Brominated & Non- Chlorinated Flame Retardant | |||
Usage | Electrical |
| ||||
Physical | Nominal Value | Test Method | ||||
Density / Specific Gravity | 1.2 | ASTM D792 | ||||
Melt Flow Rate[MFR](260 | °C;5 | kgf) | 15 g/10min | ASTM D1238 | ||
Melt Volume Rate, MVR(5 kg;MVR at 260 °C) | 12 cm³/10 min | ISO 1133 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched(23 °C) | 800 J/m | ASTM D256 |
Instrumented Dart Impact, Total Energy(23 °C) | 72 J | ASTM D3763 |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
45 kJ/m² 15 kJ/m² | ISO 180/1A |
C harpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp =62mm 0 -30 °C;Edgew;80*10*3;sp =62mm 0 |
45 kJ/m² 15 kJ/m² | ISO 179 1eA |
Tensile Stress, Yield | ||
50 mm/min;Type I | 64 MPa | ASTM D638 |
50 mm/min | 62 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 62 MPa | ASTM D638 |
50 mm/min | 50 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 5 % | ASTM D638 |
50 mm/min | 4.8 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 55 % | ASTM D638 |
50 mm/min | > 45 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 2600 MPa | ASTM D638 |
1 mm/min | 2400 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 98 MPa | ASTM D790 |
2 mm/min | 98 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2440 MPa | ASTM D790 |
2 mm/min | 2500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2 mm ≥ 2 mm |
5VB V-0 | UL 94 |
NBS Smoke Density, Flaming, Dmax | 225 | ASTM E662 |
NBS Smoke Density, Flaming Ds 1.5 min Ds 4 min |
40 150 | ASTM E662 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
118 °C 105 °C | ASTM D648 |
Vicat Softening Temperature Rate B/50 Rate B/120 |
124 °C 127 °C | ISO 306 |
HDT/Af(1.8) | 106 °C | ISO 75/Af |
Relative Temp Index, Elec | 90 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 90 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 90 °C | UL 746B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 90 °C | |
Drying Time<Injection> | 4 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 270 - 300 °C | |
Nozzle Temperature<Injection> | 265 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 265 - 300 °C | |
Middle, Zone 2 Temperature<Injection> | 260 - 300 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 300 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 90 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |