F136-E1-XH
Forever
F136-E1-XH has a low melting point and a wide process temperature range. It has better impact resistance and solubility than PA66, but also stronger moisture absorption.
General | ||
Form | ||
Feature |
| |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.13 g/cm³ | ISO 1183 |
Viscosity Number | 245 cm³/g | ISO 307 |
Melt Viscosity(260 °C) | 2.25E+6 mPa · s | Internal Method |
Mechanical | Nominal Value | Test Method |
Coefficient of Friction, Dynamic | 0.80 | ISO 8295 |
Coefficient of Friction, Static | 1.4 | ISO 8295 |
Film Thickness - Tested | 50 µm | |
Tensile Modulus(50 mm/min) | 465 MPa | Internal Method |
Tensile Stress - MD, Yield | 34.0 MPa | ISO 527-3 |
Tensile Stress - MD, Break | 94.0 MPa | ISO 527-3 |
Tensile Elongation, Break, MD | 350 % | ISO 527-3 |
Trouser Tear - Parallel | 32.0 | ISO 6383-1 |
Thermal | Nominal Value | Test Method |
CLTE, Flow | 9.0E-5 cm/cm/°C | ISO 11359-2 |
Specific Heat Capacity | 1550 J/kg/°C | |
Average Specific Heat Capacity(20 - 150 °C) | 2250 J/kg/°C | |
Optical | Nominal Value | Test Method |
Clarity | 85 % | Internal Method |
Processing | Nominal Value |
Cylinder Zone 1 Temp. <Extrusion> | 270 °C |
Cylinder Zone 2 Temp. <Extrusion> | 270 °C |
Cylinder Zone 3 Temp. <Extrusion> | 270 °C |
Cylinder Zone 4 Temp. <Extrusion> | 270 °C |
Die Temperature<Extrusion> | 270 °C |
Chill Roll Temperature<Extrusion> | 110 °C |
F136-E1-XH has a low melting point and a wide process temperature range. It has better impact resistance and solubility than PA66, but also stronger moisture absorption.
General | ||
Form | ||
Feature |
| |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.13 g/cm³ | ISO 1183 |
Viscosity Number | 245 cm³/g | ISO 307 |
Melt Viscosity(260 °C) | 2.25E+6 mPa · s | Internal Method |
Mechanical | Nominal Value | Test Method |
Coefficient of Friction, Dynamic | 0.80 | ISO 8295 |
Coefficient of Friction, Static | 1.4 | ISO 8295 |
Film Thickness - Tested | 50 µm | |
Tensile Modulus(50 mm/min) | 465 MPa | Internal Method |
Tensile Stress - MD, Yield | 34.0 MPa | ISO 527-3 |
Tensile Stress - MD, Break | 94.0 MPa | ISO 527-3 |
Tensile Elongation, Break, MD | 350 % | ISO 527-3 |
Trouser Tear - Parallel | 32.0 | ISO 6383-1 |
Thermal | Nominal Value | Test Method |
CLTE, Flow | 9.0E-5 cm/cm/°C | ISO 11359-2 |
Specific Heat Capacity | 1550 J/kg/°C | |
Average Specific Heat Capacity(20 - 150 °C) | 2250 J/kg/°C | |
Optical | Nominal Value | Test Method |
Clarity | 85 % | Internal Method |
Processing | Nominal Value |
Cylinder Zone 1 Temp. <Extrusion> | 270 °C |
Cylinder Zone 2 Temp. <Extrusion> | 270 °C |
Cylinder Zone 3 Temp. <Extrusion> | 270 °C |
Cylinder Zone 4 Temp. <Extrusion> | 270 °C |
Die Temperature<Extrusion> | 270 °C |
Chill Roll Temperature<Extrusion> | 110 °C |
Resin Pellets