Availability: | |
---|---|
Quantity: | |
1760E-XH
FOREVER
1760E-XH is a high-performance 11% glass reinforced PCPBT alloy that provides excellent impact and chemical resistance. Particularly suitable for automotive exterior applications, it has exceptional physical property retention, even in extreme conditions.
This version of the 1760-XH resin delivers higher flow, making it easy to process. Whether it's for exterior moldings or other demanding applications requiring high-performance materials, the 1760E-XH is an excellent choice for its durability and superior performance properties.
General | |||
Form | Resin Pellets | ||
Filler | 11 % Glass Fiber | ||
Feature Chemical Resistant Ductile Excellent Processability | |||
Automotive Rail | Automotive Exterior Electrical | Automotive Interior | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.30 g/cm³ | ||
Melt Mass-Flow Rate, MFR(250 °C;5 kg) 15 g/10min ASTM D1238 | |||
Melt Volume-Flow Rate, MVR(265 °C;5 kg) 27 cm³/10 min ISO 1133 | |||
Molding Shrinkage, Across Flow(3.2 mm) 0.40 - 0.60 % Internal Method | |||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.60 % Internal Method | |||
Water Absorption, Saturation(23 °C) | 0.50 % | ISO 62 | |
Water Absorption, Equilibrium(50% RH;23 °C) 0.15 % ISO 62 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 5310 MPa 4800 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
5 mm/min;Type I | 84.0 MPa 84.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Strength, Break | ||
5 mm/min;Type I | 84.0 MPa 84.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Yield | ||
5 mm/min;Type I | 3.0 % 3.0 % | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Break | ||
5 mm/min;Type I | 3.0 % 3.0 % | ASTM D4812;ISO 180/1U ISO 527-2/5 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min | 3910 MPa 4010 MPa | ASTM D790 ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 133 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 131 MPa | ASTM D790 |
Charpy Notched Impact Strength(23 °C) | 12 kJ/m² | ISO 179 1eA |
Notched Izod Impact | ||
-30 °C | 60 J/m | ASTM D256 |
23 °C | 63 J/m | ASTM D256 |
-30 °C | 3.0 kJ/m² | ISO 180/1A |
23 °C | 3.0 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Energy at Peak -30 °C -20 °C | 3.00 J 4.00 J | ASTM D3763 |
Instrumented Dart Impact, Total Energy -30 °C 23 °C | 3.00 J 8.00 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 125 °C 116 °C 101 °C | ASTM D648 ASTM D648 ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 121 °C 135 °C 130 °C | ASTM D1525 ISO 306/B50 ISO 306/B120 |
CLTE, Flow(-40 - 40 °C) | 3.9E-5 cm/cm/°C | |
CLTE, Transverse -40 - 40 °C -40 °C | 7.6E-5 cm/cm/°C 7.6E-5 cm/cm/°C | ASTM E831 ISO 11359-2 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 110 °C | |
Drying Time<Injection> | 4.0 - 6.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 50 - 80 % | |
Rear Temperature<Injection> | 250 - 270 °C | |
Middle Temperature<injection> | 255 - 275 °C | |
Front Temperature<Injection> | 260 - 280 °C | |
Nozzle Temperature<Injection> | 255 - 275 °C | |
Processing Temp, Melt<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 65 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.600 MPa | |
Screw Speed<Injection> | 50 - 80 rpm | |
Vent Depth<Injection> | 0.013 - 0.020 mm | |
Injection, Drying Time, Cumulative<Injection> | 8 hrs |
1760E-XH is a high-performance 11% glass reinforced PCPBT alloy that provides excellent impact and chemical resistance. Particularly suitable for automotive exterior applications, it has exceptional physical property retention, even in extreme conditions.
This version of the 1760-XH resin delivers higher flow, making it easy to process. Whether it's for exterior moldings or other demanding applications requiring high-performance materials, the 1760E-XH is an excellent choice for its durability and superior performance properties.
General | |||
Form | Resin Pellets | ||
Filler | 11 % Glass Fiber | ||
Feature Chemical Resistant Ductile Excellent Processability | |||
Automotive Rail | Automotive Exterior Electrical | Automotive Interior | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.30 g/cm³ | ||
Melt Mass-Flow Rate, MFR(250 °C;5 kg) 15 g/10min ASTM D1238 | |||
Melt Volume-Flow Rate, MVR(265 °C;5 kg) 27 cm³/10 min ISO 1133 | |||
Molding Shrinkage, Across Flow(3.2 mm) 0.40 - 0.60 % Internal Method | |||
Molding Shrinkage, Flow(3.2 mm) 0.40 - 0.60 % Internal Method | |||
Water Absorption, Saturation(23 °C) | 0.50 % | ISO 62 | |
Water Absorption, Equilibrium(50% RH;23 °C) 0.15 % ISO 62 |
Mechanical | Nominal Value | Test Method |
Tensile Modulus | ||
5 mm/min | 5310 MPa 4800 MPa | ASTM D638 ISO 527-2/1 |
Tensile Strength, Yield | ||
5 mm/min;Type I | 84.0 MPa 84.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Strength, Break | ||
5 mm/min;Type I | 84.0 MPa 84.0 MPa | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Yield | ||
5 mm/min;Type I | 3.0 % 3.0 % | ASTM D638 ISO 527-2/5 |
Tensile Elongation, Break | ||
5 mm/min;Type I | 3.0 % 3.0 % | ASTM D4812;ISO 180/1U ISO 527-2/5 |
Flexural Modulus 1.3 mm/min;50 mm;Span 2 mm/min | 3910 MPa 4010 MPa | ASTM D790 ISO 178 |
Flexural Stress, at Yield(2 mm/min) | 133 MPa | ISO 178 |
Flexural Stress, Yield(1.3 mm/min;50 mm;Span) | 131 MPa | ASTM D790 |
Charpy Notched Impact Strength(23 °C) | 12 kJ/m² | ISO 179 1eA |
Notched Izod Impact | ||
-30 °C | 60 J/m | ASTM D256 |
23 °C | 63 J/m | ASTM D256 |
-30 °C | 3.0 kJ/m² | ISO 180/1A |
23 °C | 3.0 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Energy at Peak -30 °C -20 °C | 3.00 J 4.00 J | ASTM D3763 |
Instrumented Dart Impact, Total Energy -30 °C 23 °C | 3.00 J 8.00 J | ASTM D3763 |
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 1.8 MPa;3.2 mm 1.8 MPa;6.4 mm 80*10*4 mm;1.8 MPa;4 mm;64 mm;Span | 125 °C 116 °C 101 °C | ASTM D648 ASTM D648 ISO 75-2/Af |
Vicat Softening Temperature | ||
50 °C/h;50 N;Rate A;Loading 2 | 121 °C 135 °C 130 °C | ASTM D1525 ISO 306/B50 ISO 306/B120 |
CLTE, Flow(-40 - 40 °C) | 3.9E-5 cm/cm/°C | |
CLTE, Transverse -40 - 40 °C -40 °C | 7.6E-5 cm/cm/°C 7.6E-5 cm/cm/°C | ASTM E831 ISO 11359-2 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 110 °C | |
Drying Time<Injection> | 4.0 - 6.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 50 - 80 % | |
Rear Temperature<Injection> | 250 - 270 °C | |
Middle Temperature<injection> | 255 - 275 °C | |
Front Temperature<Injection> | 260 - 280 °C | |
Nozzle Temperature<Injection> | 255 - 275 °C | |
Processing Temp, Melt<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 65 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.600 MPa | |
Screw Speed<Injection> | 50 - 80 rpm | |
Vent Depth<Injection> | 0.013 - 0.020 mm | |
Injection, Drying Time, Cumulative<Injection> | 8 hrs |