PX11313-XH
Forever
PX11313-XH compound, which is produced using Nylon 6 resin mixed with mineral and glass fiber. This compound offers several additional features, including thermally conductive properties, electrical insulation capabilities, and non-brominated, non-chlorinated flame retardancy.
General | |||||
Form | Resin Pellets | ||||
Feature | Thermally Conductive | Non-Brominated & Non- Chlorinated Flame Retardant | Non-Chlorinated Electrically Isolative | ||
Usage |
| Electrical | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.79 g/cm³ | ASTM D792 | |||
Mold Shrinkage, Flow(24 hrs) | 0.42 % | ASTM D955 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.58 % | ASTM D955 | |||
Water Absorption | |||||
24 hrs;23 °C | 0.04 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.04 % | ISO 62 | |||
UV light, water exposure/immersion | f2 | UL 746C | |||
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 326 J/m | ASTM D4812 |
80*10*4;23 °C | 23 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 30 J/m | ASTM D256 |
80*10*4;23 °C | 3 kJ/m² | ISO 180/1A |
Tensile Stress, Break | ||
5 mm/min;Type I | 98 MPa | ASTM D638 |
5 mm/min | 108 MPa | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 1.3 % | ASTM D638 |
5 mm/min | 1.3 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.3E+04 MPa | ASTM D638 |
1 mm/min | 1.3E+04 MPa | ISO 527 |
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 167 MPa | ASTM D790 |
Flexural Stress, break | ||
1.3 mm/min;50 mm;span | 176 MPa | ASTM D790 |
2 mm/min | 186 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 1.2E+04 MPa | ASTM D790 |
2 mm/min | 1.3E+04 MPa | ISO 178 |
Impact Strength | 2.4 - 27 kJ/m² | ISO R179 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 0.8 mm) | V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
750 °C 800 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1 mm |
960 °C 960 °C | IEC 60695-2-12 |
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) | 227 °C | ASTM D648 |
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 215 °C | ASTM D648 |
CTE, Flow(40°C to 120°C) | 4.1E-05 1/°C | ASTM E831 |
CTE, XFlow(40°C to 120°C) | 8.5E-05 1/°C | ASTM E831 |
Thermal conductivity through plane | ||
10*10*3mm sample | 1.4 W/m-K | ASTM E1461-07 |
?80*3mm discs | 0.9 W/m-K | ISO 22007-2 |
Thermal conductivity in plane | ||
25*0.4mm disc | 1.8 W/m-K | ASTM E1461-07 |
?80*3mm discs | 1.9 W/m-K | ISO 22007-2 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
HDT/Bf(0.45) | 228 °C | ISO 75/Bf |
HDT/Af(1.8) | 208 °C | ISO 75/Af |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 105 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 140 °C | UL 746B |
PX11313-XH compound, which is produced using Nylon 6 resin mixed with mineral and glass fiber. This compound offers several additional features, including thermally conductive properties, electrical insulation capabilities, and non-brominated, non-chlorinated flame retardancy.
General | |||||
Form | Resin Pellets | ||||
Feature | Thermally Conductive | Non-Brominated & Non- Chlorinated Flame Retardant | Non-Chlorinated Electrically Isolative | ||
Usage |
| Electrical | |||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.79 g/cm³ | ASTM D792 | |||
Mold Shrinkage, Flow(24 hrs) | 0.42 % | ASTM D955 | |||
Mold Shrinkage, XFlow(24 hrs) | 0.58 % | ASTM D955 | |||
Water Absorption | |||||
24 hrs;23 °C | 0.04 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.04 % | ISO 62 | |||
UV light, water exposure/immersion | f2 | UL 746C | |||
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 326 J/m | ASTM D4812 |
80*10*4;23 °C | 23 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 30 J/m | ASTM D256 |
80*10*4;23 °C | 3 kJ/m² | ISO 180/1A |
Tensile Stress, Break | ||
5 mm/min;Type I | 98 MPa | ASTM D638 |
5 mm/min | 108 MPa | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 1.3 % | ASTM D638 |
5 mm/min | 1.3 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 1.3E+04 MPa | ASTM D638 |
1 mm/min | 1.3E+04 MPa | ISO 527 |
Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 167 MPa | ASTM D790 |
Flexural Stress, break | ||
1.3 mm/min;50 mm;span | 176 MPa | ASTM D790 |
2 mm/min | 186 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 1.2E+04 MPa | ASTM D790 |
2 mm/min | 1.3E+04 MPa | ISO 178 |
Impact Strength | 2.4 - 27 kJ/m² | ISO R179 |
Thermal | Nominal Value | Test Method |
UL Recognized(≥ 0.8 mm) | V-0 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
750 °C 800 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1 mm |
960 °C 960 °C | IEC 60695-2-12 |
Heat Deflection Temperature[HDT](0.45 MPa;3.2 mm) | 227 °C | ASTM D648 |
Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 215 °C | ASTM D648 |
CTE, Flow(40°C to 120°C) | 4.1E-05 1/°C | ASTM E831 |
CTE, XFlow(40°C to 120°C) | 8.5E-05 1/°C | ASTM E831 |
Thermal conductivity through plane | ||
10*10*3mm sample | 1.4 W/m-K | ASTM E1461-07 |
?80*3mm discs | 0.9 W/m-K | ISO 22007-2 |
Thermal conductivity in plane | ||
25*0.4mm disc | 1.8 W/m-K | ASTM E1461-07 |
?80*3mm discs | 1.9 W/m-K | ISO 22007-2 |
Ball Pressure Test(125°C +/- 2°C) | PASSES | IEC 60695-10-2 |
HDT/Bf(0.45) | 228 °C | ISO 75/Bf |
HDT/Af(1.8) | 208 °C | ISO 75/Af |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 105 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 140 °C | UL 746B |