PA6 GF60-03-XH
Forever
PA6 GF60-03-XH is a type of composite tape made up of 60% E-glass by weight and polyamide 6 (nylon 6). This tape is reinforced with continuous fibers in one direction, making it strong and lightweight. It has impressive toughness and can resist impacts effectively. This material is particularly suitable for applications in industries such as manufacturing, automotive, and sporting goods where strength, toughness, and cost are important factors to consider. Additionally, it is easy to process. The tape is available in both natural and black colors, and there may be options for different widths and thicknesses.
General |
Form |
Filler |
Feature |
Usage |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.69 g/cm³ ISO 1183 |
Mechanical Nominal Value Test Method |
Tensile Modulus, Tape(0°) 29700 MPa ASTM D3039M |
Tensile Strength, Tape(0°) 679 MPa ASTM D3039M |
Tensile Elongation, Break, Tape(0°) 2.4 % ASTM D3039M |
Flexural Modulus, Tape(0°) 32100 MPa ASTM D790 |
Flexural Strength, Tape(0°) 752 MPa ASTM D790 |
Flexural Elongation, Break, Tape(0°) 3.12 ASTM D790 |
Thermal Nominal Value Test Method |
Glass Transition Temperature(10 °C;min) 57.0 °C ISO 11357-2 |
Melting Point(10 °C/min) 220 °C ISO 11357-3 |
PA6 GF60-03-XH is a type of composite tape made up of 60% E-glass by weight and polyamide 6 (nylon 6). This tape is reinforced with continuous fibers in one direction, making it strong and lightweight. It has impressive toughness and can resist impacts effectively. This material is particularly suitable for applications in industries such as manufacturing, automotive, and sporting goods where strength, toughness, and cost are important factors to consider. Additionally, it is easy to process. The tape is available in both natural and black colors, and there may be options for different widths and thicknesses.
General |
Form |
Filler |
Feature |
Usage |
Physical Nominal Value Test Method |
Density / Specific Gravity 1.69 g/cm³ ISO 1183 |
Mechanical Nominal Value Test Method |
Tensile Modulus, Tape(0°) 29700 MPa ASTM D3039M |
Tensile Strength, Tape(0°) 679 MPa ASTM D3039M |
Tensile Elongation, Break, Tape(0°) 2.4 % ASTM D3039M |
Flexural Modulus, Tape(0°) 32100 MPa ASTM D790 |
Flexural Strength, Tape(0°) 752 MPa ASTM D790 |
Flexural Elongation, Break, Tape(0°) 3.12 ASTM D790 |
Thermal Nominal Value Test Method |
Glass Transition Temperature(10 °C;min) 57.0 °C ISO 11357-2 |
Melting Point(10 °C/min) 220 °C ISO 11357-3 |