B3ZG6 BK30564-XH
Forever
B3ZG6 BK30564-XH is a high-performance PA6 grade for injection molding, featuring impact modification, pigmented black color, and a 30% glass fiber reinforcement. This grade is specifically designed for industrial applications requiring excellent impact strength and rigidity. Typical applications for B3ZG6 BK30564-XH include automotive airbag housings and half-shells used in suitcases.
General | ||||
Form | Resin Pellets | |||
Filler | 30 % Glass Fiber | |||
Usage |
|
| ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.33 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 25 cm³/10 min | ISO 1133 | ||
Water Absorption, Saturation(23 °C) | 6.2 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 2.0 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus(23 °C) | 8800 MPa | ISO 527-2 | ||
Tensile Stress, Break(23 °C) | 150 MPa | ISO 527-2 | ||
Tensile Strain, Break(23 °C) | 3.2 % | ISO 527-2 | ||
Flexural Modulus(23 °C) | 7900 MPa | ISO 178 | ||
C harpy Notched Impact Strength | ISO 179 | |||
-30 °C | 8.0 kJ/m² | |||
23 °C | 15 kJ/m² | |||
Notched Izod Impact Strength | ISO 180 | |||
-30 °C | 8.0 kJ/m² | |||
23 °C | 16 kJ/m² | |||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature, Unannealed(1.8 MPa) | 205 °C | ISO 75-2/A | ||
Melting Temperature, DSC | 220 °C | ISO 3146 | ||
Processing | Nominal Value |
Drying Temperature<Injection> | 80 °C |
Drying Time<Injection> | 2.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.080 % |
Rear Temperature<Injection> | 245 - 275 °C |
Middle Temperature<injection> | 260 - 285 °C |
Front Temperature<Injection> | 270 - 295 °C |
Nozzle Temperature<Injection> | 270 - 295 °C |
Processing Temp, Melt<Injection> | 270 - 295 °C |
Mold Temperature<Injection> | 80 - 95 °C |
Injection Pressure<Injection> | 3.50 - 12.5 MPa |
Injection Rate<Injection> | Fast |
B3ZG6 BK30564-XH is a high-performance PA6 grade for injection molding, featuring impact modification, pigmented black color, and a 30% glass fiber reinforcement. This grade is specifically designed for industrial applications requiring excellent impact strength and rigidity. Typical applications for B3ZG6 BK30564-XH include automotive airbag housings and half-shells used in suitcases.
General | ||||
Form | Resin Pellets | |||
Filler | 30 % Glass Fiber | |||
Usage |
|
| ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.33 g/cm³ | ISO 1183 | ||
Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 25 cm³/10 min | ISO 1133 | ||
Water Absorption, Saturation(23 °C) | 6.2 % | ISO 62 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 2.0 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Modulus(23 °C) | 8800 MPa | ISO 527-2 | ||
Tensile Stress, Break(23 °C) | 150 MPa | ISO 527-2 | ||
Tensile Strain, Break(23 °C) | 3.2 % | ISO 527-2 | ||
Flexural Modulus(23 °C) | 7900 MPa | ISO 178 | ||
C harpy Notched Impact Strength | ISO 179 | |||
-30 °C | 8.0 kJ/m² | |||
23 °C | 15 kJ/m² | |||
Notched Izod Impact Strength | ISO 180 | |||
-30 °C | 8.0 kJ/m² | |||
23 °C | 16 kJ/m² | |||
Thermal | Nominal Value | Test Method | ||
Heat Deflection Temperature, Unannealed(1.8 MPa) | 205 °C | ISO 75-2/A | ||
Melting Temperature, DSC | 220 °C | ISO 3146 | ||
Processing | Nominal Value |
Drying Temperature<Injection> | 80 °C |
Drying Time<Injection> | 2.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.080 % |
Rear Temperature<Injection> | 245 - 275 °C |
Middle Temperature<injection> | 260 - 285 °C |
Front Temperature<Injection> | 270 - 295 °C |
Nozzle Temperature<Injection> | 270 - 295 °C |
Processing Temp, Melt<Injection> | 270 - 295 °C |
Mold Temperature<Injection> | 80 - 95 °C |
Injection Pressure<Injection> | 3.50 - 12.5 MPa |
Injection Rate<Injection> | Fast |
Industrial Applications