DF0041VI-XH
Forever
LNP THERMOCOMP DF0041VI-XH compound is a material made from Polycarbonate resin mixed with 20% glass fiber. It has several additional benefits, such as enhanced surface for plating and improved mechanical performance, making it ideal for Laser Direct Structuring (LDS) applications. It is also a non-brominated and non-chlorinated flame retardant, and has a wide range of processing capabilities.
General | |||
Form | Resin Pellets | ||
Filler | 20% Glass Fiber | ||
Feature | Good Hardness
Lds | Non-Brominated & Non- Chlorinated Flame Retardant
Structural | Non-Chlorinated Structural
Circuit Solution |
Usage |
Electrical Building and Construction | ||
Physical | Nominal Value | Test Method | |
Melt Flow Rate[MFR] 300 °C;2.16 kgf 300 °C;1.2 kgf |
17 g/10min 10 g/10min | ASTM D1238 | |
Density / Specific Gravity | 1.4 g/cm³ | ASTM D792 | |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 80 J/m | ASTM D256 |
80*10*4;23 °C | 8 kJ/m² | ISO 180/1A |
Izod Impact, Unnotched | ||
23 °C | 450 J/m | ASTM D4812 |
80*10*4;23 °C | 26 kJ/m² | ISO 180/1U |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 8 kJ/m² | ISO 179 1eA |
C harpy Impact, Unnotched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 30 kJ/m² | ISO 179 1eU |
Tensile Stress, Break | ||
5 mm/min;Type I | 85 MPa | ASTM D638 |
5 mm/min | 86 MPa | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 2.5 % | ASTM D638 |
5 mm/min | 2.5 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 7000 MPa | ASTM D638 |
1 mm/min | 6900 MPa | ISO 527 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 6000 MPa | ASTM D790 |
2 mm/min | 6400 MPa | ISO 178 |
Flexural Strength | ||
1.3 mm/min;50 mm;span | 125 MPa | ASTM D790 |
2 mm/min | 130 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
124 °C 118 °C | ASTM D648 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 110 - 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Melt Temperature<Injection> | 290 - 310 °C | |
Nozzle Temperature<Injection> | 285 - 310 °C | |
Front, Zone 3 Temperature<Injection> | 285 - 310 °C | |
Middle, Zone 2 Temperature<Injection> | 285 - 310 °C | |
Rear, Zone 1 Temperature<Injection> | 285 - 310 °C | |
Mold Temperature<Injection> | 100 - 130 °C | |
Back Pressure<Injection> | 0.1 - 0.3 MPa | |
Screw Speed <Injection> | 50 - 150 rpm |
LNP THERMOCOMP DF0041VI-XH compound is a material made from Polycarbonate resin mixed with 20% glass fiber. It has several additional benefits, such as enhanced surface for plating and improved mechanical performance, making it ideal for Laser Direct Structuring (LDS) applications. It is also a non-brominated and non-chlorinated flame retardant, and has a wide range of processing capabilities.
General | |||
Form | Resin Pellets | ||
Filler | 20% Glass Fiber | ||
Feature | Good Hardness
Lds | Non-Brominated & Non- Chlorinated Flame Retardant
Structural | Non-Chlorinated Structural
Circuit Solution |
Usage |
Electrical Building and Construction | ||
Physical | Nominal Value | Test Method | |
Melt Flow Rate[MFR] 300 °C;2.16 kgf 300 °C;1.2 kgf |
17 g/10min 10 g/10min | ASTM D1238 | |
Density / Specific Gravity | 1.4 g/cm³ | ASTM D792 | |
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 80 J/m | ASTM D256 |
80*10*4;23 °C | 8 kJ/m² | ISO 180/1A |
Izod Impact, Unnotched | ||
23 °C | 450 J/m | ASTM D4812 |
80*10*4;23 °C | 26 kJ/m² | ISO 180/1U |
C harpy Impact, V-Notched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 8 kJ/m² | ISO 179 1eA |
C harpy Impact, Unnotched(23 °C;Edgew;80*10*4;sp =62 mm 0) | 30 kJ/m² | ISO 179 1eU |
Tensile Stress, Break | ||
5 mm/min;Type I | 85 MPa | ASTM D638 |
5 mm/min | 86 MPa | ISO 527 |
Tensile Strain, Break | ||
5 mm/min;Type I | 2.5 % | ASTM D638 |
5 mm/min | 2.5 % | ISO 527 |
Tensile Modulus | ||
5 mm/min | 7000 MPa | ASTM D638 |
1 mm/min | 6900 MPa | ISO 527 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 6000 MPa | ASTM D790 |
2 mm/min | 6400 MPa | ISO 178 |
Flexural Strength | ||
1.3 mm/min;50 mm;span | 125 MPa | ASTM D790 |
2 mm/min | 130 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
124 °C 118 °C | ASTM D648 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 110 - 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Melt Temperature<Injection> | 290 - 310 °C | |
Nozzle Temperature<Injection> | 285 - 310 °C | |
Front, Zone 3 Temperature<Injection> | 285 - 310 °C | |
Middle, Zone 2 Temperature<Injection> | 285 - 310 °C | |
Rear, Zone 1 Temperature<Injection> | 285 - 310 °C | |
Mold Temperature<Injection> | 100 - 130 °C | |
Back Pressure<Injection> | 0.1 - 0.3 MPa | |
Screw Speed <Injection> | 50 - 150 rpm |