200 A TC-I-10-XH
Forever
200 A TC-I-10-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.
General | ||
Form | ||
Feature | Thermally
| |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.51 g/cm³ | ASTM D792 |
Mechanical | Nominal Value | Test Method |
Tensile Strength, Break | 75.8 MPa | ASTM D638 |
Elongation at Break | 2.0 % | ASTM D638 |
Tensile Modulus | 6890 MPa | ASTM D638 |
Flexural Strength | 131 MPa | ASTM D790 |
Flexural Modulus | 6890 MPa | ASTM D790 |
Izod Impact, Notched(Thickness; 3.2 mm) | 26.7 J/m | ASTM D256 |
Izod Impact, Unnotched(Thickness; 3.2 mm) | 427 J/m | ASTM D4812 |
Thermal | Nominal Value | Test Method |
Thermal conductivity through plane(through-plane) | 0.500 W/m-K | ASTM E1530 |
Thermal conductivity in plane(in-plane) | 1.10 W/m-K | ASTM E1461 |
Deflection Temperature(Pressure; 1.8 MPa) | 171 °C | ASTM D648 |
Electrical | Nominal Value | Test Method |
Surface Resistivity per Square | > = 1.00e+14 Ohms | ASTM D257 |
Dielectric Strength(In Oil;Short Term) | 15.1 kV/mm | ASTM D149 |
Processing | Nominal Value | |
Melt Temperature | 243 - 279 °C | |
Mold Temperature | 54.4 - 93.3 °C | |
Drying Temperature(Time 2 hr) | 82.2 °C | |
Moisture Content | 0.20 % | |
Dew Point | -17.8 °C | |
Injection Pressure | 68.9 - 103 MPa | |
200 A TC-I-10-XH type PA6 resin can make strong, hard parts. Isotropic shrinkage properties. Inherently flame retardant. Application areas: Automotive industry, textile machinery, instruments and precision engineering. Typical parts: Electrical and electronic industry parts.
General | ||
Form | ||
Feature | Thermally
| |
Physical | Nominal Value | Test Method |
Density / Specific Gravity | 1.51 g/cm³ | ASTM D792 |
Mechanical | Nominal Value | Test Method |
Tensile Strength, Break | 75.8 MPa | ASTM D638 |
Elongation at Break | 2.0 % | ASTM D638 |
Tensile Modulus | 6890 MPa | ASTM D638 |
Flexural Strength | 131 MPa | ASTM D790 |
Flexural Modulus | 6890 MPa | ASTM D790 |
Izod Impact, Notched(Thickness; 3.2 mm) | 26.7 J/m | ASTM D256 |
Izod Impact, Unnotched(Thickness; 3.2 mm) | 427 J/m | ASTM D4812 |
Thermal | Nominal Value | Test Method |
Thermal conductivity through plane(through-plane) | 0.500 W/m-K | ASTM E1530 |
Thermal conductivity in plane(in-plane) | 1.10 W/m-K | ASTM E1461 |
Deflection Temperature(Pressure; 1.8 MPa) | 171 °C | ASTM D648 |
Electrical | Nominal Value | Test Method |
Surface Resistivity per Square | > = 1.00e+14 Ohms | ASTM D257 |
Dielectric Strength(In Oil;Short Term) | 15.1 kV/mm | ASTM D149 |
Processing | Nominal Value | |
Melt Temperature | 243 - 279 °C | |
Mold Temperature | 54.4 - 93.3 °C | |
Drying Temperature(Time 2 hr) | 82.2 °C | |
Moisture Content | 0.20 % | |
Dew Point | -17.8 °C | |
Injection Pressure | 68.9 - 103 MPa | |
Resin Pellets