MD231U-XH
Forever
MD231U-XH is a polypropylene compound with 20% mineral fillers, designed specifically for injection molding. This material offers exceptional mechanical properties and a moderate melt flow rate. It finds applications in various industries, including air ducts, air filters, air conditioning parts, and automotive components located under the bonnet.
General | ||||
Form | Resin Pellets | |||
Filler | 20 % Mineral | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.05 g/cm³ | ISO 1183 | ||
Melt Flow 2.16 kg;230 °C 5 kg;230 °C |
6.0 g/10min 27.5 g/10min | ISO 1133 | ||
Ball Indentation Hardness | 80.6 MPa | ISO 2039 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(50 mm/min) | 36.0 MPa | ISO 527-2 | ||
Elongation at Yield(50 mm/min) | 10 % | ISO 527-2 | ||
Flexural Modulus | 2700 MPa | ISO 178 | ||
C harpy Impact Unnotched Temperature; -20 °C Temperature; 23 °C |
13.7 kJ/m² 42 kJ/m² | ISO 179 1eU | ||
C harpy Impact, Notched Temperature; -20 °C Temperature; 23 °C |
1.2 kJ/m² 3 kJ/m² | ISO 179 1eA | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
125 °C 70.0 °C | ISO 75-2 | ||
Processing | Nominal Value |
Processing Temperature | 220 - 260 °C |
Feed Temperature | 40.0 - 80.0 °C |
Mold Temperature | 30.0 - 50.0 °C |
Injection Velocity | 100 - 200 mm/sec |
Hold Pressure | 30.0 - 60.0 MPa |
MD231U-XH is a polypropylene compound with 20% mineral fillers, designed specifically for injection molding. This material offers exceptional mechanical properties and a moderate melt flow rate. It finds applications in various industries, including air ducts, air filters, air conditioning parts, and automotive components located under the bonnet.
General | ||||
Form | Resin Pellets | |||
Filler | 20 % Mineral | |||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.05 g/cm³ | ISO 1183 | ||
Melt Flow 2.16 kg;230 °C 5 kg;230 °C |
6.0 g/10min 27.5 g/10min | ISO 1133 | ||
Ball Indentation Hardness | 80.6 MPa | ISO 2039 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(50 mm/min) | 36.0 MPa | ISO 527-2 | ||
Elongation at Yield(50 mm/min) | 10 % | ISO 527-2 | ||
Flexural Modulus | 2700 MPa | ISO 178 | ||
C harpy Impact Unnotched Temperature; -20 °C Temperature; 23 °C |
13.7 kJ/m² 42 kJ/m² | ISO 179 1eU | ||
C harpy Impact, Notched Temperature; -20 °C Temperature; 23 °C |
1.2 kJ/m² 3 kJ/m² | ISO 179 1eA | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Pressure; 0.46 MPa Pressure; 1.8 MPa |
125 °C 70.0 °C | ISO 75-2 | ||
Processing | Nominal Value |
Processing Temperature | 220 - 260 °C |
Feed Temperature | 40.0 - 80.0 °C |
Mold Temperature | 30.0 - 50.0 °C |
Injection Velocity | 100 - 200 mm/sec |
Hold Pressure | 30.0 - 60.0 MPa |