XE 5026 (BG-30 H)-XH
XE 5026 (BG-30 H)-XH is a high-performance Polyamide 6 (Nylon 6) material, specifically designed for injection molding applications. It is formulated with 30% glass fiber reinforcement to enhance its mechanical properties. This grade, known as XE 5026 (BG-30 H)-XH, is available in various regions such as Africa & Middle East, Asia Pacific, Europe, Latin America, and North America. It possesses important attributes including being flame rated, RoHS compliant, and featuring a heat stabilizer, ensuring its suitability for a wide range of applications. Some typical applications include automotive components, household appliances, and electrical/electronic parts.
General | ||
Form | ||
Filler | ||
Feature | ||
Uses |
| |
Physical Nominal Value Test Method | ||
Density, dry 1.35 g/cm³ ISO 1183 | ||
Dry: Molding Shrinkage, Across Flow 0.60 % ISO 294-4 | ||
Dry: Molding Shrinkage, Flow 0.10 % ISO 294-4 | ||
Dry: Water Absorption, Saturation(23 °C) 7.0 % ISO 62 | ||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 2.0 % ISO 62 | ||
Dry: Ball Indentation Hardness 210 MPa ISO 2039-1 | ||
Condition: Ball Indentation Hardness 100 MPa ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 9500 MPa | ISO 527-2 |
Condition: Tensile Modulus | 6000 MPa | ISO 527-2 |
Dry: Tensile Stress, Break | 180 MPa | ISO 527-2 |
Condition: Tensile Stress, Break | 100 MPa | ISO 527-2 |
Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 |
Condition: Tensile Strain, Break | 7.0 % | ISO 527-2 |
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
9.0 kJ/m² 11 kJ/m² | ISO 179 1eA |
Condition: Charpy Notched Impact Strength -30 °C 23 °C |
8.0 kJ/m² 20 kJ/m² | ISO 179 1eA |
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
70 kJ/m² 80 kJ/m² | ISO 179 1eU |
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
60 kJ/m² 90 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 1.8 MPa 8 MPa |
205 °C 135 °C |
ISO 75-2/A ISO 75-2/C |
Dry: Continuous Use Temperature, Long Term | 120 - 135 °C | ISO 2578 |
Dry: Continuous Use Temperature, Short time | 200 °C | Internal Method |
Dry: Melting Temperature(10 °C;min) | 222 °C | ISO 11357-3 |
Dry: Flammability Classification(0.8 mm) | HB | IEC 60695-11- 10;IEC 60695-11- 20 |
Electrical | Nominal Value | Test Method |
Condition: Surface resistivity | 1.0E+12 ohms | IEC 60093 |
Dry: Volume Resistivity | 1.0e+14 ohms ·cm | IEC 60093 |
Condition: Volume resistivity | 1.0E+13 ohms ·cm | IEC 60093 |
Dry: Electric Strength | 40 kV/mm | IEC 60243-1 |
Condition: Electric Strength | 37 kV/mm | IEC 60243-1 |
Condition: Comparative Tracking Index | 500 V | IEC 60112 |
XE 5026 (BG-30 H)-XH is a high-performance Polyamide 6 (Nylon 6) material, specifically designed for injection molding applications. It is formulated with 30% glass fiber reinforcement to enhance its mechanical properties. This grade, known as XE 5026 (BG-30 H)-XH, is available in various regions such as Africa & Middle East, Asia Pacific, Europe, Latin America, and North America. It possesses important attributes including being flame rated, RoHS compliant, and featuring a heat stabilizer, ensuring its suitability for a wide range of applications. Some typical applications include automotive components, household appliances, and electrical/electronic parts.
General | ||
Form | ||
Filler | ||
Feature | ||
Uses |
| |
Physical Nominal Value Test Method | ||
Density, dry 1.35 g/cm³ ISO 1183 | ||
Dry: Molding Shrinkage, Across Flow 0.60 % ISO 294-4 | ||
Dry: Molding Shrinkage, Flow 0.10 % ISO 294-4 | ||
Dry: Water Absorption, Saturation(23 °C) 7.0 % ISO 62 | ||
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 2.0 % ISO 62 | ||
Dry: Ball Indentation Hardness 210 MPa ISO 2039-1 | ||
Condition: Ball Indentation Hardness 100 MPa ISO 2039-1 | ||
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 9500 MPa | ISO 527-2 |
Condition: Tensile Modulus | 6000 MPa | ISO 527-2 |
Dry: Tensile Stress, Break | 180 MPa | ISO 527-2 |
Condition: Tensile Stress, Break | 100 MPa | ISO 527-2 |
Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 |
Condition: Tensile Strain, Break | 7.0 % | ISO 527-2 |
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
9.0 kJ/m² 11 kJ/m² | ISO 179 1eA |
Condition: Charpy Notched Impact Strength -30 °C 23 °C |
8.0 kJ/m² 20 kJ/m² | ISO 179 1eA |
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
70 kJ/m² 80 kJ/m² | ISO 179 1eU |
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
60 kJ/m² 90 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 1.8 MPa 8 MPa |
205 °C 135 °C |
ISO 75-2/A ISO 75-2/C |
Dry: Continuous Use Temperature, Long Term | 120 - 135 °C | ISO 2578 |
Dry: Continuous Use Temperature, Short time | 200 °C | Internal Method |
Dry: Melting Temperature(10 °C;min) | 222 °C | ISO 11357-3 |
Dry: Flammability Classification(0.8 mm) | HB | IEC 60695-11- 10;IEC 60695-11- 20 |
Electrical | Nominal Value | Test Method |
Condition: Surface resistivity | 1.0E+12 ohms | IEC 60093 |
Dry: Volume Resistivity | 1.0e+14 ohms ·cm | IEC 60093 |
Condition: Volume resistivity | 1.0E+13 ohms ·cm | IEC 60093 |
Dry: Electric Strength | 40 kV/mm | IEC 60243-1 |
Condition: Electric Strength | 37 kV/mm | IEC 60243-1 |
Condition: Comparative Tracking Index | 500 V | IEC 60112 |