LUX2619-XH
FOREVER
1 What is the light diffusion polycarbonate?
Diffusion PC resins is a transparent PC(polycarbonate) plastic adding a certain ratio of light diffusion agents and other additives through a special process polymerization of a light and opaque light diffusion material particles.
With the rapid development of the LED industry in the past years, LED lighting has been fully popularized and accepted by people, as a key material for LED lighting PC light diffusion plastics are also constantly developing
and improving.
Product Description | |||||
Introducing the latest addition to our range of polycarbonate resins - LUX2619-XH. This extrusion grade resin boasts a UL94 V-0 rating at 1.5 mm, making it an excellent choice for applications that require high flammability ratings. Moreover, LUX2619-XH has been specifically formulated for superior light reflectivity, ensuring maximum luminance in applications where clarity is key. With its outstanding mechanical properties and easy processing, LUX2619-XH is a versatile material that is ideal for a wide range of industrial and commercial applications. | |||||
General | |||||
Form | Resin | Pellets | |||
Feature | High | Reflection | |||
Uses |
| ||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.34 g/cm³ | ASTM D792;ISO 1183 | |||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.5 g/10min | ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) | 0.80 - 1.0 % | Internal Method | |||
Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | |||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.15 % | ISO 62 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Yield(50 mm/min;Type I) | 57.0 MPa | ASTM D638 | |||
Tensile Strength, Break(50 mm/min;Type I) | 50.0 MPa | ASTM D638 | |||
Tensile Elongation, Yield(50 mm/min;Type I) | 6.0 % | ASTM D638 | |||
Tensile Elongation, Break(50 mm/min;Type I) | 74 % | ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2730 MPa | ASTM D790 | |||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 97.0 MPa | ASTM D790 | |||
Notched Izod Impact -30 °C 23 °C |
140 J/m 640 J/m | ASTM D256 | |||
Unnotched Izod Impact(23 °C) | 2100 J/m | ASTM D4812 | |||
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
141 °C 129 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 147 °C | ASTM D1525 |
CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 6.4E-5 cm/cm/°C | ASTM E831 |
Flame Rating(1.5 mm) | V-2 | UL 94 |
Glow Wire Flammability Index(1 - 3 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
875 °C 850 °C | IEC 60695-2-13 |
1 What is the light diffusion polycarbonate?
Diffusion PC resins is a transparent PC(polycarbonate) plastic adding a certain ratio of light diffusion agents and other additives through a special process polymerization of a light and opaque light diffusion material particles.
With the rapid development of the LED industry in the past years, LED lighting has been fully popularized and accepted by people, as a key material for LED lighting PC light diffusion plastics are also constantly developing
and improving.
Product Description | |||||
Introducing the latest addition to our range of polycarbonate resins - LUX2619-XH. This extrusion grade resin boasts a UL94 V-0 rating at 1.5 mm, making it an excellent choice for applications that require high flammability ratings. Moreover, LUX2619-XH has been specifically formulated for superior light reflectivity, ensuring maximum luminance in applications where clarity is key. With its outstanding mechanical properties and easy processing, LUX2619-XH is a versatile material that is ideal for a wide range of industrial and commercial applications. | |||||
General | |||||
Form | Resin | Pellets | |||
Feature | High | Reflection | |||
Uses |
| ||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity | 1.34 g/cm³ | ASTM D792;ISO 1183 | |||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 7.5 g/10min | ASTM D1238 | |||
Molding Shrinkage, Flow(3.2 mm) | 0.80 - 1.0 % | Internal Method | |||
Water Absorption, Saturation(23 °C) | 0.35 % | ISO 62 | |||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.15 % | ISO 62 | |||
Mechanical | Nominal Value | Test Method | |||
Tensile Strength, Yield(50 mm/min;Type I) | 57.0 MPa | ASTM D638 | |||
Tensile Strength, Break(50 mm/min;Type I) | 50.0 MPa | ASTM D638 | |||
Tensile Elongation, Yield(50 mm/min;Type I) | 6.0 % | ASTM D638 | |||
Tensile Elongation, Break(50 mm/min;Type I) | 74 % | ASTM D638 | |||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2730 MPa | ASTM D790 | |||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 97.0 MPa | ASTM D790 | |||
Notched Izod Impact -30 °C 23 °C |
140 J/m 640 J/m | ASTM D256 | |||
Unnotched Izod Impact(23 °C) | 2100 J/m | ASTM D4812 | |||
Thermal | Nominal Value | Test Method |
Deflection Temperature Under Load, Unannealed 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
141 °C 129 °C | ASTM D648 |
Vicat Softening Temperature(50 °C/h;50 N;Rate A;Loading 2) | 147 °C | ASTM D1525 |
CLTE, Flow(-40 - 40 °C) | 6.1E-5 cm/cm/°C | ASTM E831 |
CLTE, Transverse(-40 - 40 °C) | 6.4E-5 cm/cm/°C | ASTM E831 |
Flame Rating(1.5 mm) | V-2 | UL 94 |
Glow Wire Flammability Index(1 - 3 mm) | 960 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 3 mm |
875 °C 850 °C | IEC 60695-2-13 |
Lighting Applications