HCX1640-XH
FOREVER
HCX1640-XH Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend - the perfect solution for medical and pharmaceutical industries.
This biocompatible grade is meticulously designed to meet the strict requirements of ISO10993 and USP Class VI for unparalleled safety in medical devices and pharmaceutical applications. With improved heat resistance, flow, and impact balance, this PC/ABS blend is engineered to provide exceptional performance and reliability in challenging applications.
Experience the superior quality of HCX1640-XH, the ultimate choice for your medical device and pharmaceutical needs.
General | ||||
Form |
| |||
Feature | ||||
Uses |
|
| Mass Transportation | |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.15 1.15 g/cm³ |
ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.6 % | SABIC Method | ||
Melt Flow Rate[MFR](260 °C;5 kgf) | 19 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.4 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | ||
Melt Volume Rate, MVR(5 kg;MVR at 260 °C) | 18 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C |
550 J/m 300 J/m 40 kJ/m² 20 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A | ||
Izod Impact, Double-Gated(23 °C) | 150 J/m | SABIC Method | ||
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 | ||
Izod Impact, Unnotched | ISO 180/1U | |||
80*10*4;23 °C | NB kJ/m² | |||
80*10*4;-30 °C | NB kJ/m² | |||
Charpy Impact, V-Notched | ISO 179 1eA | |||
23 °C;Edgew;80*10*4;sp=62 mm 0 | 40 kJ/m² | |||
-30 °C;Edgew;80*10*4;sp=62 mm 0 | 20 kJ/m² | |||
Charpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp=62 mm 0 -30 °C;Edgew;80*10*4;sp=62 mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
55 MPa 55 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
50 MPa 50 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
5 % 5 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
> 50 % > 50 % |
ASTM D638 ISO 527 |
Tensile Modulus 5 mm/min 1 mm/min |
2400 MPa 2400 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
85 MPa 85 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2300 MPa 2300 MPa |
ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature | ||
Rate B/50 | 130 °C | ASTM D1525 |
Rate B/50 | 130 °C | ISO 306 |
Rate B/120 | 132 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
122 °C 108 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C |
7.0E-05 1/°C 7.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C |
7.0E-05 1/°C 7.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
HDT/Af(1.8) | 108 °C | ISO 75/Af |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 110 °C | |
Drying Time<Injection> | 2 - 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 260 - 290 °C | |
Nozzle Temperature<Injection> | 240 - 280 °C | |
Front, Zone 3 Temperature<Injection> | 250 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 250 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 260 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 90 °C |
HCX1640-XH Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend - the perfect solution for medical and pharmaceutical industries.
This biocompatible grade is meticulously designed to meet the strict requirements of ISO10993 and USP Class VI for unparalleled safety in medical devices and pharmaceutical applications. With improved heat resistance, flow, and impact balance, this PC/ABS blend is engineered to provide exceptional performance and reliability in challenging applications.
Experience the superior quality of HCX1640-XH, the ultimate choice for your medical device and pharmaceutical needs.
General | ||||
Form |
| |||
Feature | ||||
Uses |
|
| Mass Transportation | |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.15 1.15 g/cm³ |
ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.6 % | SABIC Method | ||
Melt Flow Rate[MFR](260 °C;5 kgf) | 19 g/10min | ASTM D1238 | ||
Water Absorption(23 °C;saturated) | 0.4 % | ISO 62-1 | ||
Moisture Absorption(50% RH;23 °C) | 0.1 % | ISO 62 | ||
Melt Volume Rate, MVR(5 kg;MVR at 260 °C) | 18 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method | ||
Izod Impact, Notched 23 °C -30 °C 80*10*4;23 °C 80*10*4;-30 °C |
550 J/m 300 J/m 40 kJ/m² 20 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A | ||
Izod Impact, Double-Gated(23 °C) | 150 J/m | SABIC Method | ||
Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 | ||
Izod Impact, Unnotched | ISO 180/1U | |||
80*10*4;23 °C | NB kJ/m² | |||
80*10*4;-30 °C | NB kJ/m² | |||
Charpy Impact, V-Notched | ISO 179 1eA | |||
23 °C;Edgew;80*10*4;sp=62 mm 0 | 40 kJ/m² | |||
-30 °C;Edgew;80*10*4;sp=62 mm 0 | 20 kJ/m² | |||
Charpy Impact, Unnotched 23 °C;Edgew;80*10*4;sp=62 mm 0 -30 °C;Edgew;80*10*4;sp=62 mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
55 MPa 55 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
50 MPa 50 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
5 % 5 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
> 50 % > 50 % |
ASTM D638 ISO 527 |
Tensile Modulus 5 mm/min 1 mm/min |
2400 MPa 2400 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
85 MPa 85 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2300 MPa 2300 MPa |
ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
Vicat Softening Temperature | ||
Rate B/50 | 130 °C | ASTM D1525 |
Rate B/50 | 130 °C | ISO 306 |
Rate B/120 | 132 °C | ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
122 °C 108 °C | ASTM D648 |
CTE, Flow -40 - 40 °C -40 - 40 °C |
7.0E-05 1/°C 7.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C -40 - 40 °C |
7.0E-05 1/°C 7.0E-05 1/°C |
ASTM E831 ISO 11359-2 |
HDT/Af(1.8) | 108 °C | ISO 75/Af |
Processing | Nominal Value | |
Drying Temperature<Injection> | 100 - 110 °C | |
Drying Time<Injection> | 2 - 4 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 260 - 290 °C | |
Nozzle Temperature<Injection> | 240 - 280 °C | |
Front, Zone 3 Temperature<Injection> | 250 - 290 °C | |
Middle, Zone 2 Temperature<Injection> | 250 - 290 °C | |
Rear, Zone 1 Temperature<Injection> | 230 - 260 °C | |
Hopper Temperature<Injection> | 60 - 80 °C | |
Mold Temperature<Injection> | 60 - 90 °C |