Availability: | |
---|---|
Quantity: | |
MN-3600H-XH
FOREVER
Product Description | |||
PC alloy grade | |||
General | |||
Form | Resin Pellets | ||
Feature Non-Brominated Good Thermal | |||
Uses | Battery Cases | Electrical Engineering | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ISO 1183 | |
Melt Volume-Flow Rate, MVR(280 °C;2.16 kg) | 18 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Across Flow(4 mm) | 0.50 - 0.70 % | Internal Method | |
Molding Shrinkage, Flow(4 mm) | 0.50 - 0.70 % | Internal Method | |
Water Absorption(24 hr;23 °C) | 0.22 % | ISO 62 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2350 MPa | ISO 527-2/1 | |
Tensile Stress, Yield | 60.0 MPa | ISO 527-2/50 | |
Tensile Stress, Break | 50.0 MPa | ISO 527-2/50 | |
Tensile Strain, Yield | 7.0 % | ISO 527-2/50 | |
Tensile Strain, Break | 100 % | ISO 527-2/50 | |
Flexural Modulus(2 mm/min) | 2300 MPa | ISO 178 | |
Flexural Stress(2 mm/min) | 95.0 MPa | ISO 178 | |
Charpy Notched Impact Strength(23 °C) | 45 kJ/m² | ISO 179 | |
Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
125 °C 112 °C |
ISO 75-2/B ISO 75-2/A |
CLTE, Flow | 7.0E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
RTI Elec(1.5 mm) | 95.0 °C | UL 746 |
RTI Imp(1.5 mm) | 95.0 °C | UL 746 |
RTI Str(1.5 mm) | 95.0 °C | UL 746 |
Flame Rating 0.45 mm 1 mm 1.5 mm 2 mm 3 mm |
HB V-1 V-0 5VB 5VA | UL 94 |
Glow Wire Flammability Index 1 mm 1.5 mm 2 mm 3 mm |
960 °C 930 °C 960 °C 930 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 2 mm 3 mm |
875 °C 825 °C 825 °C 825 °C | IEC 60695-2-13 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |
Product Description | |||
PC alloy grade | |||
General | |||
Form | Resin Pellets | ||
Feature Non-Brominated Good Thermal | |||
Uses | Battery Cases | Electrical Engineering | |
Physical | Nominal Value | Test Method | |
Density / Specific Gravity | 1.19 g/cm³ | ISO 1183 | |
Melt Volume-Flow Rate, MVR(280 °C;2.16 kg) | 18 cm³/10 min | ISO 1133 | |
Molding Shrinkage, Across Flow(4 mm) | 0.50 - 0.70 % | Internal Method | |
Molding Shrinkage, Flow(4 mm) | 0.50 - 0.70 % | Internal Method | |
Water Absorption(24 hr;23 °C) | 0.22 % | ISO 62 | |
Mechanical | Nominal Value | Test Method | |
Tensile Modulus | 2350 MPa | ISO 527-2/1 | |
Tensile Stress, Yield | 60.0 MPa | ISO 527-2/50 | |
Tensile Stress, Break | 50.0 MPa | ISO 527-2/50 | |
Tensile Strain, Yield | 7.0 % | ISO 527-2/50 | |
Tensile Strain, Break | 100 % | ISO 527-2/50 | |
Flexural Modulus(2 mm/min) | 2300 MPa | ISO 178 | |
Flexural Stress(2 mm/min) | 95.0 MPa | ISO 178 | |
Charpy Notched Impact Strength(23 °C) | 45 kJ/m² | ISO 179 | |
Charpy Unnotched Impact Strength(23 °C) | No Break | ISO 179 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
125 °C 112 °C |
ISO 75-2/B ISO 75-2/A |
CLTE, Flow | 7.0E-5 cm/cm/°C | ISO 11359-2 |
CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
RTI Elec(1.5 mm) | 95.0 °C | UL 746 |
RTI Imp(1.5 mm) | 95.0 °C | UL 746 |
RTI Str(1.5 mm) | 95.0 °C | UL 746 |
Flame Rating 0.45 mm 1 mm 1.5 mm 2 mm 3 mm |
HB V-1 V-0 5VB 5VA | UL 94 |
Glow Wire Flammability Index 1 mm 1.5 mm 2 mm 3 mm |
960 °C 930 °C 960 °C 930 °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature [GWIT] 1 mm 1.5 mm 2 mm 3 mm |
875 °C 825 °C 825 °C 825 °C | IEC 60695-2-13 |
Electrical | Nominal Value | Test Method |
Surface Resistivity | > 1.0E+15 Ohms | IEC 60093 |