PA66-G30
Forever
PA66-G30-XH is a reinforced Polyamide 66 (Nylon 66) material, incorporating a 30% glass fiber filler. Notable characteristics of PA66-G30-XH include its flame retardant properties, excellent aesthetics, dimensional stability, resistance to high temperatures, and high strength. This material finds common use in various applications such as appliances, electrical/electronic components, engineering/industrial parts, and tools.
General | |
Form | |
Filler | |
Feature | |
Uses |
Power Mechanical Parts |
Physical Nominal Value Test Method | |
Density / Specific Gravity 1.36 g/cm³ ISO 1183 | |
Molding Shrinkage, Across Flow 0.90 % ISO 2577 | |
Molding Shrinkage, Flow 0.30 % ISO 2577 | |
Water Absorption, Equilibrium(50% RH;23 °C) 1.8 % ISO 62 | |
Ash Content 30 % ISO 3451-1 | |
Mechanical Nominal Value Test Method | |
Tensile Stress 185 MPa ISO 527-2/10 | |
Tensile Strain, Break 3.0 % ISO 527-2/10 | |
Flexural Modulus(2 mm/min) 8200 MPa ISO 178 | |
Flexural Stress(2 mm/min) 270 MPa ISO 178 | |
Notched Izod Impact Strength(23 °C) 14 kJ/m² ISO 180 | |
Thermal Nominal Value Test Method | |
Heat Deflection Temperature, Unannealed | |
0.45 MPa 255 °C ISO 75-2/B | |
1.8 MPa 250 °C ISO 75-2/A | |
Flame Rating HB UL 94 | |
Electrical Nominal Value Test Method | |
Volume Resistivity 1.0e+15 ohms ·cm IEC 60093 | |
Processing | Nominal Value |
Drying Temperature - Desiccant Dryer<Injection> | 90 - 110 °C |
Drying Time - Desiccant Dryer<Injection> | 4.0 - 6.0 hr |
Rear Temperature<Injection> | 260 - 275 °C |
Middle Temperature<injection> | 270 - 280 °C |
Front Temperature<Injection> | 280 - 290 °C |
Processing Temp, Melt<Injection> | 270 - 290 °C |
Mold Temperature<Injection> | 50 - 120 °C |
Injection Rate<Injection> | Moderate-Fast |
PA66-G30-XH is a reinforced Polyamide 66 (Nylon 66) material, incorporating a 30% glass fiber filler. Notable characteristics of PA66-G30-XH include its flame retardant properties, excellent aesthetics, dimensional stability, resistance to high temperatures, and high strength. This material finds common use in various applications such as appliances, electrical/electronic components, engineering/industrial parts, and tools.
General | |
Form | |
Filler | |
Feature | |
Uses |
Power Mechanical Parts |
Physical Nominal Value Test Method | |
Density / Specific Gravity 1.36 g/cm³ ISO 1183 | |
Molding Shrinkage, Across Flow 0.90 % ISO 2577 | |
Molding Shrinkage, Flow 0.30 % ISO 2577 | |
Water Absorption, Equilibrium(50% RH;23 °C) 1.8 % ISO 62 | |
Ash Content 30 % ISO 3451-1 | |
Mechanical Nominal Value Test Method | |
Tensile Stress 185 MPa ISO 527-2/10 | |
Tensile Strain, Break 3.0 % ISO 527-2/10 | |
Flexural Modulus(2 mm/min) 8200 MPa ISO 178 | |
Flexural Stress(2 mm/min) 270 MPa ISO 178 | |
Notched Izod Impact Strength(23 °C) 14 kJ/m² ISO 180 | |
Thermal Nominal Value Test Method | |
Heat Deflection Temperature, Unannealed | |
0.45 MPa 255 °C ISO 75-2/B | |
1.8 MPa 250 °C ISO 75-2/A | |
Flame Rating HB UL 94 | |
Electrical Nominal Value Test Method | |
Volume Resistivity 1.0e+15 ohms ·cm IEC 60093 | |
Processing | Nominal Value |
Drying Temperature - Desiccant Dryer<Injection> | 90 - 110 °C |
Drying Time - Desiccant Dryer<Injection> | 4.0 - 6.0 hr |
Rear Temperature<Injection> | 260 - 275 °C |
Middle Temperature<injection> | 270 - 280 °C |
Front Temperature<Injection> | 280 - 290 °C |
Processing Temp, Melt<Injection> | 270 - 290 °C |
Mold Temperature<Injection> | 50 - 120 °C |
Injection Rate<Injection> | Moderate-Fast |
Resin Pellets