S223-KG7-XH
Forever
S223-KG7-XH can maintain strong strength and stiffness at higher temperatures. PA66 plastic still has hygroscopicity after molding, and its degree mainly depends on the material composition, wall thickness, and environmental conditions.
General |
Form |
Filler |
Feature |
Usage |
Physical Nominal Value Test Method |
Density, dry 1.41 g/cm³ ISO 1183 |
Dry: Molding Shrinkage, Across Flow 1.0 % ISO 294-4 |
Dry: Molding Shrinkage, Flow 0.20 % ISO 294-4 |
Dry: Water Absorption, Saturation(23 °C) 5.5 % ISO 62 |
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.5 % ISO 62 |
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 11500 MPa | ISO 527-2 |
Condition: Tensile Modulus | 7550 MPa | ISO 527-2 |
Dry: Tensile Stress, Break | 210 MPa | ISO 527-2 |
Condition: Tensile Stress, Break | 140 MPa | ISO 527-2 |
Dry: Tensile Strain, Break | 3.5 % | ISO 527-2 |
Condition: Tensile Strain, Break | 5.8 % | ISO 527-2 |
Dry: Flexural Modulus | 9400 MPa | ISO 178 |
Dry: Flexural Stress | 270 MPa | ISO 178 |
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 14 kJ/m² | ISO 179 1eA |
Condition: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 18 kJ/m² | ISO 179 1eA |
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
74 kJ/m² 89 kJ/m² | ISO 179 1eU |
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
74 kJ/m² 95 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
260 °C 247 °C |
ISO 75-2/B ISO 75-2/A |
Dry: Melting Temperature(10 °C/min) | 260 °C | ISO 11357-3 |
Dry: CLTE, Flow | 2.0E-5 cm/cm/°C | ISO 11359-2 |
Dry: CLTE, Transverse | 6.0E-5 cm/cm/°C | ISO 11359-2 |
S223-KG7-XH can maintain strong strength and stiffness at higher temperatures. PA66 plastic still has hygroscopicity after molding, and its degree mainly depends on the material composition, wall thickness, and environmental conditions.
General |
Form |
Filler |
Feature |
Usage |
Physical Nominal Value Test Method |
Density, dry 1.41 g/cm³ ISO 1183 |
Dry: Molding Shrinkage, Across Flow 1.0 % ISO 294-4 |
Dry: Molding Shrinkage, Flow 0.20 % ISO 294-4 |
Dry: Water Absorption, Saturation(23 °C) 5.5 % ISO 62 |
Dry: Water Absorption, Equilibrium(50% RH;23 °C) 1.5 % ISO 62 |
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus | 11500 MPa | ISO 527-2 |
Condition: Tensile Modulus | 7550 MPa | ISO 527-2 |
Dry: Tensile Stress, Break | 210 MPa | ISO 527-2 |
Condition: Tensile Stress, Break | 140 MPa | ISO 527-2 |
Dry: Tensile Strain, Break | 3.5 % | ISO 527-2 |
Condition: Tensile Strain, Break | 5.8 % | ISO 527-2 |
Dry: Flexural Modulus | 9400 MPa | ISO 178 |
Dry: Flexural Stress | 270 MPa | ISO 178 |
Dry: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 14 kJ/m² | ISO 179 1eA |
Condition: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 18 kJ/m² | ISO 179 1eA |
Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
74 kJ/m² 89 kJ/m² | ISO 179 1eU |
Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
74 kJ/m² 95 kJ/m² | ISO 179 1eU |
Thermal | Nominal Value | Test Method |
Dry: Heat Deflection Temperature, Unannealed 0.45 MPa 1.8 MPa |
260 °C 247 °C |
ISO 75-2/B ISO 75-2/A |
Dry: Melting Temperature(10 °C/min) | 260 °C | ISO 11357-3 |
Dry: CLTE, Flow | 2.0E-5 cm/cm/°C | ISO 11359-2 |
Dry: CLTE, Transverse | 6.0E-5 cm/cm/°C | ISO 11359-2 |
Resin Pellets