Flame Retardant Injection Extruded Grade PC Plastic Native Particles

Form                                        Resin Pellets

Filler                                          15 % Stainless Steel Fiber

Electrically Conductive

Emi/Rfi Shielding

High Impact

Feature

Non-Brominated & 

Non-Chlorinated Flame Retardant

Non-Chlorinated

Uses

Consumer

Electrical

Packaging

Industria

Physical

Nominal Value

Test Method

Mold Shrinkage, Flow(24 hrs)

0.4 - 0.7 %

ISO 294

Mold Shrinkage, XFlow(24 hrs)

0.5 %

ISO 294

Density / Specific Gravity

1.29 g/cm³

ISO 1183

Mechanical

Nominal Value

Test Method

Izod Impact, Unnotched

23 °C

1790 J/m

ASTM D4812

80*10*4;23 °C

85 kJ/m²

ISO 180/1U

Izod Impact, Notched

23 °C

124 J/m

ASTM D256

80*10*4;23 °C

14 kJ/m²

ISO 180/1A

Tensile Stress, Yield

57 MPa

ISO 527

Tensile Stress, Break

55 MPa

ISO 527

Tensile Strain, Yield

3.8 %

ISO 527

Tensile Strain, Break

4 - 8 %

ISO 527

Tensile Modulus(1 mm/min)

2800 MPa

ISO 527

Flexural Stress

80 MPa

ISO 178

Flexural Modulus

2600 MPa

ISO 178

CTE, Flow(-40 - 40 °C)

5.6E-05 1/°C

ISO 11359-2

CTE, XFlow(-40 - 40 °C)

6.7e-05 1/°C

ISO 11359-2

HDT/Bf(0.45)

136 °C

ISO 75/Bf

HDT/Af(1.8)

125 °C

ISO 75/Af

Electrical

Nominal Value

Test Method

Volume Resistivity

1.0E+04 ohms ·cm

ASTM D257

Surface Resistivity

100 - 1.0E+04 ohms

ASTM D257

Shielding Effectivness @ 3Mm

40 - 55 dB

SABIC Method

Processing

Nominal Value

Drying Temperature<Injection>

120 °C

Drying Time<Injection>

4 hrs

Maximum Moisture Content<Injection>

0.02 %

Melt Temperature<Injection>

305 - 325 °C

Front, Zone 3 Temperature<Injection>

320 - 330 °C

Middle, Zone 2 Temperature<Injection>

310 - 320 °C

Rear, Zone 1 Temperature<Injection>

295 - 305 °C

Mold Temperature<Injection>

95 - 120 °C

Back Pressure<Injection>

0.2 - 0.3 MPa

Screw Speed <Injection>

30 - 60 rpm