HF1110R-XH
Forever
HF1110-XH is a high flow grade polymer with an easy mold release version. It is specifically designed for applications that require thin wall lighting lenses, data storage components, and safety eyewear lenses.
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability | |||
| ||||
Usage | Electronic Displays |
|
| |
Automotive Exterior
| Automotive Interior
| Constraction | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 25 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(50 mm/min;Type I) | 62.0 MPa | ASTM D638 | ||
Tensile Strength, Break(50 mm/min;Type I) | 65.0 MPa | ASTM D638 | ||
Tensile Elongation, Break(50 mm/min;Type I) | 120 % | ASTM D638 | ||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2300 MPa | ASTM D790 | ||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 93.0 MPa | ASTM D790 | ||
Notched Izod Impact(23 °C) | 640 J/m | ASTM D256 | ||
Instrumented Dart Impact, Energy at Peak(23 °C) | 54.0 J | ASTM D3763 | ||
Tensile Impact Strength(Type S) | 378 kJ/m² | ASTM D1822 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed(1.8 MPa;3.2 mm) | 126 °C | ASTM D648 | ||
RTI Elec | 130 °C | UL 746 | ||
RTI Imp | 130 °C | UL 746 | ||
RTI Str | 130 °C | UL 746 | ||
Flame Rating(1.1 mm) | V-2 | UL 94 | ||
Electrical | Nominal Value | Test Method |
Comparative Tracking Index[CTI] | PLC 2 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 |
High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746 |
Hot-wire Ignition, HWI | PLC 2 | UL 746 |
Optical | Nominal Value | Test Method |
Transmittance (2.5e+3 µm) | 88.0 % | ASTM D1003 |
Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 250 - 270 °C | |
Middle Temperature<injection> | 260 - 280 °C | |
Front Temperature<Injection> | 270 - 295 °C | |
Nozzle Temperature<Injection> | 265 - 290 °C | |
Processing Temp, Melt<Injection> | 270 - 295 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.025 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 48 hrs |
HF1110-XH is a high flow grade polymer with an easy mold release version. It is specifically designed for applications that require thin wall lighting lenses, data storage components, and safety eyewear lenses.
General | ||||
Form | Resin Pellets | |||
Feature | Excellent Processability | |||
| ||||
Usage | Electronic Displays |
|
| |
Automotive Exterior
| Automotive Interior
| Constraction | ||
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity | 1.20 g/cm³ | ASTM D792 | ||
Melt Mass-Flow Rate, MFR(300 °C;1.2 kg) | 25 g/10min | ASTM D1238 | ||
Molding Shrinkage, Flow(3.2 mm) | 0.50 - 0.70 % | Internal Method | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Strength, Yield(50 mm/min;Type I) | 62.0 MPa | ASTM D638 | ||
Tensile Strength, Break(50 mm/min;Type I) | 65.0 MPa | ASTM D638 | ||
Tensile Elongation, Break(50 mm/min;Type I) | 120 % | ASTM D638 | ||
Flexural Modulus(1.3 mm/min;50 mm;Span) | 2300 MPa | ASTM D790 | ||
Flexural Strength, Yield(1.3 mm/min;50 mm;Span) | 93.0 MPa | ASTM D790 | ||
Notched Izod Impact(23 °C) | 640 J/m | ASTM D256 | ||
Instrumented Dart Impact, Energy at Peak(23 °C) | 54.0 J | ASTM D3763 | ||
Tensile Impact Strength(Type S) | 378 kJ/m² | ASTM D1822 | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed(1.8 MPa;3.2 mm) | 126 °C | ASTM D648 | ||
RTI Elec | 130 °C | UL 746 | ||
RTI Imp | 130 °C | UL 746 | ||
RTI Str | 130 °C | UL 746 | ||
Flame Rating(1.1 mm) | V-2 | UL 94 | ||
Electrical | Nominal Value | Test Method |
Comparative Tracking Index[CTI] | PLC 2 | UL 746 |
High Amp Arc Ignition, HAI, Surface | PLC 1 | UL 746 |
High Voltage Arc Tracking Rate, HVTR | PLC 2 | UL 746 |
Hot-wire Ignition, HWI | PLC 2 | UL 746 |
Optical | Nominal Value | Test Method |
Transmittance (2.5e+3 µm) | 88.0 % | ASTM D1003 |
Haze(2.5e+3 µm) | 1.00 % | ASTM D1003 |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3.0 - 4.0 hr | |
Suggested Max Moisture<Injection> | 0.020 % | |
Suggested Shot Size<Injection> | 40 - 60 % | |
Rear Temperature<Injection> | 250 - 270 °C | |
Middle Temperature<injection> | 260 - 280 °C | |
Front Temperature<Injection> | 270 - 295 °C | |
Nozzle Temperature<Injection> | 265 - 290 °C | |
Processing Temp, Melt<Injection> | 270 - 295 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.300 - 0.700 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Vent Depth <Injection> | 0.025 - 0.076 mm | |
Drying Time, Cumulative<Injection> | 48 hrs |