| Technical Data Sheet | Glass Fiber Enhanced | Heat Resistance | Flame Retardant | Hight Gloss | Transparent | Weather Resistance | |||||
| Items | Method | Unite | 200G10 | 200G20 | 200G30 | 200G40 | 200HR | 200V30 | 200HG | 200T | 200WR |
| Physical Property | |||||||||||
| Specific Gravity | ASTM D792 | − | 1.1 | 1.18 | 1.25 | 1.37 | 1.05 | 1.18 | 1.04 | 1.08 | 1.07 |
| Water Absorption | ASTM D570 | % | 0.17 | 0.17 | 0.16 | 0.2 | 0.17 | 0.17 | 0.17 | 0.17 | 0.17 |
| Molding Shrinkage | ASTM D955 | % | 0.3/0.5 | 0.2/0.4 | 0.1/0.3 | 0.1/0.3 | 0.4/0.7 | 0.5/0.7 | 0.5/0.7 | 0.5/0.7 | 0.5/0.7 |
| Melt Flow Index(220℃,10kg) | ASTM 1238 | g/10min | 22 | 20 | 18 | 16 | 20 | 5 | 25 | 20 | 25 |
| Glass Fiber Content | − | % | 10 | 20 | 30 | 40 | − | − | − | − | − |
| Mechanical Property | |||||||||||
| Tensile Strength(50mm/min) | ASTM D638 | MPa | 55 | 75 | 95 | 75 | 45 | 40 | 45 | 50 | 45 |
| Elongation tensile Stretch(50mm/min) | ASTM D638 | % | 8 | 6 | 3.5 | 3.5 | 20 | 15 | 20 | 20 | 20 |
| Flexural Strength(10mm/min) | ASTM D790 | MPa | 80 | 100 | 130 | 100 | 65 | 60 | 65 | 85 | 65 |
| Flexural Modulus(10mm/min) | ASTM D790 | MPa | 3500 | 4800 | 7000 | 7500 | 2300 | 2200 | 2200 | 2500 | 2200 |
| Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 8 | 8.5 | 9 | 8 | 18 | 20 | 20 | 15 | 20 |
| Thermal Property | |||||||||||
| Heat Deflection Temperature(1.8MPa) | ASTM D648 | ℃ | 88 | 93 | 100 | 110 | 110 | 80 | 85 | 85 | 85 |
| Flammability | UL94 | 1.5mm | − | − | − | − | − | V1 | − | − | − |
| Flammability | UL94 | 3.0mm | HB | HB | HB | HB | HB | V0 | HB | HB | HB |
| Electrical Property | |||||||||||
| Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | |||||||||
| CTI(23℃) | IEC60112 | V | |||||||||
| Surface Resistivity | IEC 60093 | Ω | |||||||||
| Volume Resistivity | ICE 60093 | Ω.cm | |||||||||
| Technical Data Sheet | Glass Fiber Enhanced | Heat Resistance | Flame Retardant | Hight Gloss | Transparent | Weather Resistance | |||||
| Items | Method | Unite | 200G10 | 200G20 | 200G30 | 200G40 | 200HR | 200V30 | 200HG | 200T | 200WR |
| Physical Property | |||||||||||
| Specific Gravity | ASTM D792 | − | 1.1 | 1.18 | 1.25 | 1.37 | 1.05 | 1.18 | 1.04 | 1.08 | 1.07 |
| Water Absorption | ASTM D570 | % | 0.17 | 0.17 | 0.16 | 0.2 | 0.17 | 0.17 | 0.17 | 0.17 | 0.17 |
| Molding Shrinkage | ASTM D955 | % | 0.3/0.5 | 0.2/0.4 | 0.1/0.3 | 0.1/0.3 | 0.4/0.7 | 0.5/0.7 | 0.5/0.7 | 0.5/0.7 | 0.5/0.7 |
| Melt Flow Index(220℃,10kg) | ASTM 1238 | g/10min | 22 | 20 | 18 | 16 | 20 | 5 | 25 | 20 | 25 |
| Glass Fiber Content | − | % | 10 | 20 | 30 | 40 | − | − | − | − | − |
| Mechanical Property | |||||||||||
| Tensile Strength(50mm/min) | ASTM D638 | MPa | 55 | 75 | 95 | 75 | 45 | 40 | 45 | 50 | 45 |
| Elongation tensile Stretch(50mm/min) | ASTM D638 | % | 8 | 6 | 3.5 | 3.5 | 20 | 15 | 20 | 20 | 20 |
| Flexural Strength(10mm/min) | ASTM D790 | MPa | 80 | 100 | 130 | 100 | 65 | 60 | 65 | 85 | 65 |
| Flexural Modulus(10mm/min) | ASTM D790 | MPa | 3500 | 4800 | 7000 | 7500 | 2300 | 2200 | 2200 | 2500 | 2200 |
| Notched impact strength(23℃) | ASTM D256 | KJ/m2 | 8 | 8.5 | 9 | 8 | 18 | 20 | 20 | 15 | 20 |
| Thermal Property | |||||||||||
| Heat Deflection Temperature(1.8MPa) | ASTM D648 | ℃ | 88 | 93 | 100 | 110 | 110 | 80 | 85 | 85 | 85 |
| Flammability | UL94 | 1.5mm | − | − | − | − | − | V1 | − | − | − |
| Flammability | UL94 | 3.0mm | HB | HB | HB | HB | HB | V0 | HB | HB | HB |
| Electrical Property | |||||||||||
| Dielectric Strength(3mm) | IEC 60243-1 | MV/mm | |||||||||
| CTI(23℃) | IEC60112 | V | |||||||||
| Surface Resistivity | IEC 60093 | Ω | |||||||||
| Volume Resistivity | ICE 60093 | Ω.cm | |||||||||