MS003-XH compound is composed of a Polypropylene (PP) resin with 15% stainless steel fiber. This grade offers additional features such as electrical conductivity and EMI/RFI shielding.
General | |||
Form | |||
Filler | |||
Feature | |||
Usage |
|
|
|
Physical Nominal Value | Test Method | ||
Density / Specific Gravity 1.01 g/cm³ 1.01 g/cm³ |
ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow | |||
24 hrs 1.2 % | ASTM D955 | ||
24 hrs 1.2 % | ISO 294 | ||
Mold Shrinkage, XFlow | |||
24 hrs 1.3 % | ASTM D955 | ||
24 hrs 1.3 % | ISO 294 | ||
Water Absorption(24 hrs;23 °C) 0.03 % | ISO 62-1 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 1226 J/m | ASTM D4812 |
80*10*4;23 °C | 80 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 267 J/m | ASTM D256 |
80*10*4;23 °C | 25 kJ/m² | ISO 180/1A |
Multiaxial Impact | 22 J | ISO 6603 |
Tensile Stress, Yield | ||
19 MPa | ASTM D638 | |
21 MPa | ISO 527 | |
Tensile Stress, Break | ||
15 MPa | ASTM D638 | |
15 MPa | ISO 527 | |
Tensile Strain, Yield | ||
6.2 % | ASTM D638 | |
5.2 % | ISO 527 | |
Tensile Strain, Break | ||
88.4 % | ASTM D638 | |
72 % | ISO 527 | |
Tensile Modulus | ||
50 mm/min | 1190 MPa | ASTM D638 |
1 mm/min | 1300 MPa | ISO 527 |
Flexural Stress | ||
27 MPa | ASTM D790 | |
32 MPa | ISO 178 | |
Flexural Modulus | ||
1190 MPa | ASTM D790 | |
1500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
92 °C 53 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 1.0E-04 1/°C | ASTM E831 |
-40 - 40 °C | 1.4E-04 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 9.7E-05 1/°C | ASTM E831 |
-40 - 40 °C | 1.7E-04 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 95 °C | ISO 75/Bf |
HDT/Af(1.8) | 56 °C | ISO 75/Af |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0E+04 ohms ·cm | ASTM D257 |
Surface Resistivity | 1000 ohms | ASTM D257 |
Static Decay(5000V to <50V) | < 0.01 Seconds | FTMS101B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Melt Temperature<Injection> | 230 - 250 °C | |
Front, Zone 3 Temperature<Injection> | 260 - 270 °C | |
Middle, Zone 2 Temperature<Injection> | 230 - 245 °C | |
Rear, Zone 1 Temperature<Injection> | 205 - 215 °C | |
Mold Temperature<Injection> | 30 - 55 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 25 - 50 rpm |
MS003-XH compound is composed of a Polypropylene (PP) resin with 15% stainless steel fiber. This grade offers additional features such as electrical conductivity and EMI/RFI shielding.
General | |||
Form | |||
Filler | |||
Feature | |||
Usage |
|
|
|
Physical Nominal Value | Test Method | ||
Density / Specific Gravity 1.01 g/cm³ 1.01 g/cm³ |
ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow | |||
24 hrs 1.2 % | ASTM D955 | ||
24 hrs 1.2 % | ISO 294 | ||
Mold Shrinkage, XFlow | |||
24 hrs 1.3 % | ASTM D955 | ||
24 hrs 1.3 % | ISO 294 | ||
Water Absorption(24 hrs;23 °C) 0.03 % | ISO 62-1 |
Mechanical | Nominal Value | Test Method |
Izod Impact, Unnotched | ||
23 °C | 1226 J/m | ASTM D4812 |
80*10*4;23 °C | 80 kJ/m² | ISO 180/1U |
Izod Impact, Notched | ||
23 °C | 267 J/m | ASTM D256 |
80*10*4;23 °C | 25 kJ/m² | ISO 180/1A |
Multiaxial Impact | 22 J | ISO 6603 |
Tensile Stress, Yield | ||
19 MPa | ASTM D638 | |
21 MPa | ISO 527 | |
Tensile Stress, Break | ||
15 MPa | ASTM D638 | |
15 MPa | ISO 527 | |
Tensile Strain, Yield | ||
6.2 % | ASTM D638 | |
5.2 % | ISO 527 | |
Tensile Strain, Break | ||
88.4 % | ASTM D638 | |
72 % | ISO 527 | |
Tensile Modulus | ||
50 mm/min | 1190 MPa | ASTM D638 |
1 mm/min | 1300 MPa | ISO 527 |
Flexural Stress | ||
27 MPa | ASTM D790 | |
32 MPa | ISO 178 | |
Flexural Modulus | ||
1190 MPa | ASTM D790 | |
1500 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
92 °C 53 °C | ASTM D648 |
CTE, Flow | ||
-40 - 40 °C | 1.0E-04 1/°C | ASTM E831 |
-40 - 40 °C | 1.4E-04 1/°C | ISO 11359-2 |
CTE, XFlow | ||
-40 - 40 °C | 9.7E-05 1/°C | ASTM E831 |
-40 - 40 °C | 1.7E-04 1/°C | ISO 11359-2 |
HDT/Bf(0.45) | 95 °C | ISO 75/Bf |
HDT/Af(1.8) | 56 °C | ISO 75/Af |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1.0E+04 ohms ·cm | ASTM D257 |
Surface Resistivity | 1000 ohms | ASTM D257 |
Static Decay(5000V to <50V) | < 0.01 Seconds | FTMS101B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 °C | |
Drying Time<Injection> | 4 hrs | |
Melt Temperature<Injection> | 230 - 250 °C | |
Front, Zone 3 Temperature<Injection> | 260 - 270 °C | |
Middle, Zone 2 Temperature<Injection> | 230 - 245 °C | |
Rear, Zone 1 Temperature<Injection> | 205 - 215 °C | |
Mold Temperature<Injection> | 30 - 55 °C | |
Back Pressure<Injection> | 0.2 - 0.3 MPa | |
Screw Speed <Injection> | 25 - 50 rpm |