FXC630SK-XH
Forever
FXC630SK-XH is a thermoplastic plastic made by combining polycarbonate and ABS. It combines the excellent properties of both materials, including the formability of ABS material and the mechanical properties, impact strength, temperature resistance, and UV resistance of PC. It can be widely used in automotive internal parts, business machines, communication equipment, household appliances, and lighting equipment.
General | ||||
Form |
| |||
Usage |
|
|
| |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 | mm) | 0.3 - 0.5 % | SABIC Method | |
Melt Flow Rate[MFR](260 | °C;2.16 kgf) | 13.5 g/10min | ASTM D1238 | |
Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C) | 14 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 213 J/m | ASTM D256 |
80*10*4;23 °C | 14 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 47 J | ASTM D3763 |
Tensile Stress, Yield | ||
50 mm/min;Type I | 59 MPa | ASTM D638 |
50 mm/min | 60 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 46 MPa | ASTM D638 |
50 mm/min | 45 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 4 % | ASTM D638 |
50 mm/min | 3 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 20 % | ASTM D638 |
50 mm/min | 7 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 3100 MPa | ASTM D638 |
1 mm/min | 2800 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 94 MPa | ASTM D790 |
2 mm/min | 90 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2680 MPa | ASTM D790 |
2 mm/min | 2600 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2 mm ≥ 1.5 mm ≥ 1.2 mm ≥ 1 mm |
5VB V-0 V-1 V-2 | UL 94 |
Vicat Softening Temperature Rate B/50 Rate B/120 |
98 °C 95 °C |
ASTM D1525 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
90 °C 82 °C | ASTM D648 |
CTE, Flow(-40 - 40 °C) | 7.2e-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 7.2e-05 1/°C | ASTM E831 |
Relative Temp Index, Elec | 60 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 60 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 60 °C | UL 746B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 8 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 275 °C | |
Middle, Zone 2 Temperature<Injection> | 220 - 265 °C | |
Rear, Zone 1 Temperature<Injection> | 220 - 255 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 30 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |
FXC630SK-XH is a thermoplastic plastic made by combining polycarbonate and ABS. It combines the excellent properties of both materials, including the formability of ABS material and the mechanical properties, impact strength, temperature resistance, and UV resistance of PC. It can be widely used in automotive internal parts, business machines, communication equipment, household appliances, and lighting equipment.
General | ||||
Form |
| |||
Usage |
|
|
| |
Physical | Nominal Value | Test Method | ||
Density / Specific Gravity |
1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 | ||
Mold Shrinkage, Flow(3.2 | mm) | 0.3 - 0.5 % | SABIC Method | |
Melt Flow Rate[MFR](260 | °C;2.16 kgf) | 13.5 g/10min | ASTM D1238 | |
Melt Volume Rate, MVR(2.16 kg;MVR at 260 °C) | 14 cm³/10 min | ISO 1133 | ||
Mechanical | Nominal Value | Test Method |
Izod Impact, Notched | ||
23 °C | 213 J/m | ASTM D256 |
80*10*4;23 °C | 14 kJ/m² | ISO 180/1A |
Instrumented Dart Impact, Total Energy(23 °C) | 47 J | ASTM D3763 |
Tensile Stress, Yield | ||
50 mm/min;Type I | 59 MPa | ASTM D638 |
50 mm/min | 60 MPa | ISO 527 |
Tensile Stress, Break | ||
50 mm/min;Type I | 46 MPa | ASTM D638 |
50 mm/min | 45 MPa | ISO 527 |
Tensile Strain, Yield | ||
50 mm/min;Type I | 4 % | ASTM D638 |
50 mm/min | 3 % | ISO 527 |
Tensile Strain, Break | ||
50 mm/min;Type I | 20 % | ASTM D638 |
50 mm/min | 7 % | ISO 527 |
Tensile Modulus | ||
50 mm/min | 3100 MPa | ASTM D638 |
1 mm/min | 2800 MPa | ISO 527 |
Flexural Stress, Yield | ||
1.3 mm/min;50 mm;span | 94 MPa | ASTM D790 |
2 mm/min | 90 MPa | ISO 178 |
Flexural Modulus | ||
1.3 mm/min;50 mm;span | 2680 MPa | ASTM D790 |
2 mm/min | 2600 MPa | ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 2 mm ≥ 1.5 mm ≥ 1.2 mm ≥ 1 mm |
5VB V-0 V-1 V-2 | UL 94 |
Vicat Softening Temperature Rate B/50 Rate B/120 |
98 °C 95 °C |
ASTM D1525 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
90 °C 82 °C | ASTM D648 |
CTE, Flow(-40 - 40 °C) | 7.2e-05 1/°C | ASTM E831 |
CTE, XFlow(-40 - 40 °C) | 7.2e-05 1/°C | ASTM E831 |
Relative Temp Index, Elec | 60 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 60 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 60 °C | UL 746B |
Processing | Nominal Value | |
Drying Temperature<Injection> | 80 - 90 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 8 hrs | |
Maximum Moisture Content<Injection> | 0.04 % | |
Melt Temperature<Injection> | 245 - 275 °C | |
Nozzle Temperature<Injection> | 245 - 275 °C | |
Front, Zone 3 Temperature<Injection> | 245 - 275 °C | |
Middle, Zone 2 Temperature<Injection> | 220 - 265 °C | |
Rear, Zone 1 Temperature<Injection> | 220 - 255 °C | |
Mold Temperature<Injection> | 60 - 80 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed <Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 30 - 80 % | |
Vent Depth <Injection> | 0.038 - 0.076 mm |