LUX7632C-XH
FOREVER
LUX7632C-XH Polycarbonate (PC) resin is a high-performance, non-filled extrudable grade that delivers excellent mechanical and thermal properties.
This product is designed to meet demanding applications, offering outstanding flame retardancy, weatherability, and low smoke generation. It has been developed using a non-chlorinated and non-brominated formula, making it an eco-friendly solution for manufacturers.
The UL-94 V0 rating at 1.0mm and 5VA rating at 3.0mm ensure superior flame retardancy, while the F1 rating for UV stabilization provides added weathering resistance. The material is available in diffusion colors, making it a preferred choice for lighting and electrical applications.
Overall, LUX7632C-XH is a versatile and reliable material that is ideal for applications that require excellent durability, dimensional stability, and weather resistance.
General | |||||
Form | Resin | Pellets | |||
Feature | F1 | Non-Brominated & Non-
| |||
Uses |
| ||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity |
1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Mold Shrinkage, Flow(3.2 mm) | 0.55 - 0.75 % | SABIC Method | |||
Mold Shrinkage, XFlow(3.2 mm) | 0.6 - 0.8 % | SABIC Method | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 5 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.14 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 5 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion |
| UL 746C | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched | ASTM D4812 | ||||
23 °C | NB J/m | ||||
-30 °C | NB J/m | ||||
Izod Impact, Notched | ASTM D256 | ||||
23 °C | 100 J/m | ||||
-30 °C | 85 J/m | ||||
Instrumented Dart Impact, Total Energy(23 °C) | 66 J | ASTM D3763 | |||
Unnotched Izod Impact Strength | ISO 180/1U | ||||
unnotched;80*10*3;23 °C 0 | NB kJ/m² | ||||
unnotched;80*10*3;-30 °C 0 | NB kJ/m² |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 9 kJ/m² | ISO 179 1eA |
Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
68 MPa 67 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
52 MPa 52 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
6 % 6 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
51 % 23 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2500 MPa 2400 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
106 MPa 103 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2400 MPa 2500 MPa |
ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 3 mm ≥ 1 mm ≥ 0.4 mm |
5VA V-0 V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1 mm |
850 °C 875 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1 mm |
960 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 137 °C 139 °C |
ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
131 °C 120 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C |
6.6E-05 1/°C 7.2e-05 1/°C |
ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C |
7.0E-05 1/°C 7.6E-05 1/°C |
ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp=100mm; 0.45 Mpa) | 131 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 120 °C | ISO 75/Ae |
Relative Temp Index, Elec | 125 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Dielectric Constant, Dk(1.1e+9 Hz) | 2.79 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 5.8E-03 | ASTM ES 7-83 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm |
PLC 2 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 290 - 310 °C | |
Nozzle Temperature<Injection> | 280 - 305 °C | |
Front, Zone 3 Temperature<Injection> | 290 - 310 °C | |
Middle, Zone 2 Temperature<Injection> | 275 - 300 °C | |
Rear, Zone 1 Temperature<Injection> | 265 - 290 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
LUX7632C-XH Polycarbonate (PC) resin is a high-performance, non-filled extrudable grade that delivers excellent mechanical and thermal properties.
This product is designed to meet demanding applications, offering outstanding flame retardancy, weatherability, and low smoke generation. It has been developed using a non-chlorinated and non-brominated formula, making it an eco-friendly solution for manufacturers.
The UL-94 V0 rating at 1.0mm and 5VA rating at 3.0mm ensure superior flame retardancy, while the F1 rating for UV stabilization provides added weathering resistance. The material is available in diffusion colors, making it a preferred choice for lighting and electrical applications.
Overall, LUX7632C-XH is a versatile and reliable material that is ideal for applications that require excellent durability, dimensional stability, and weather resistance.
General | |||||
Form | Resin | Pellets | |||
Feature | F1 | Non-Brominated & Non-
| |||
Uses |
| ||||
Physical | Nominal Value | Test Method | |||
Density / Specific Gravity |
1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Mold Shrinkage, Flow(3.2 mm) | 0.55 - 0.75 % | SABIC Method | |||
Mold Shrinkage, XFlow(3.2 mm) | 0.6 - 0.8 % | SABIC Method | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 5 g/10min | ASTM D1238 | |||
Water Absorption(23 °C;saturated) | 0.14 % | ISO 62-1 | |||
Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 5 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion |
| UL 746C | |||
Mechanical | Nominal Value | Test Method | |||
Izod Impact, Unnotched | ASTM D4812 | ||||
23 °C | NB J/m | ||||
-30 °C | NB J/m | ||||
Izod Impact, Notched | ASTM D256 | ||||
23 °C | 100 J/m | ||||
-30 °C | 85 J/m | ||||
Instrumented Dart Impact, Total Energy(23 °C) | 66 J | ASTM D3763 | |||
Unnotched Izod Impact Strength | ISO 180/1U | ||||
unnotched;80*10*3;23 °C 0 | NB kJ/m² | ||||
unnotched;80*10*3;-30 °C 0 | NB kJ/m² |
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 9 kJ/m² | ISO 179 1eA |
Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² NB kJ/m² | ISO 179 1eU |
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
68 MPa 67 MPa |
ASTM D638 ISO 527 |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
52 MPa 52 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
6 % 6 % |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
51 % 23 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2500 MPa 2400 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
106 MPa 103 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2400 MPa 2500 MPa |
ASTM D790 ISO 178 |
Thermal | Nominal Value | Test Method |
UL Recognized ≥ 3 mm ≥ 1 mm ≥ 0.4 mm |
5VA V-0 V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1 mm |
850 °C 875 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1 mm |
960 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 137 °C 139 °C |
ASTM D1525 ISO 306 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
131 °C 120 °C | ASTM D648 |
CTE, Flow -40 - 40 °C 23°C to 80°C |
6.6E-05 1/°C 7.2e-05 1/°C |
ASTM E831 ISO 11359-2 |
CTE, XFlow -40 - 40 °C 23°C to 80°C |
7.0E-05 1/°C 7.6E-05 1/°C |
ASTM E831 ISO 11359-2 |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
HDT/Be(Edgew;120*10*4;sp=100mm; 0.45 Mpa) | 131 °C | ISO 75/Be |
Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 120 °C | ISO 75/Ae |
Relative Temp Index, Elec | 125 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 125 °C | UL 746B |
Electrical | Nominal Value | Test Method |
Dielectric Constant, Dk(1.1e+9 Hz) | 2.79 | ASTM ES 7-83 |
Dissipation Factor, Df(1.1e+9 Hz) | 5.8E-03 | ASTM ES 7-83 |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Hot-wire Ignition, HWI ≥ 3 mm ≥ 1 mm |
PLC 2 PLC 3 | UL 746A |
High Amp Arc Ignition, HAI(≥ 1 mm) | PLC 0 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 290 - 310 °C | |
Nozzle Temperature<Injection> | 280 - 305 °C | |
Front, Zone 3 Temperature<Injection> | 290 - 310 °C | |
Middle, Zone 2 Temperature<Injection> | 275 - 300 °C | |
Rear, Zone 1 Temperature<Injection> | 265 - 290 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |