LUX9132-XH
FOREVER
1 What are the product description of Forever's PC polymers?
LUX1932C-XH Polycarbonate (PC) resin is a highly versatile, non-filled, injection moldable grade, suitable for various applications. This non-chlorinated, non-brominated flame retardant PC has an impressive UL-94 V0 rating at 1.5 mm, making it ideal for superior fire safety. Additionally, this grade has excellent flow properties and is UV stabilized, providing extraordinary weathering resistance. LEXAN LUX9430C comes in a range of diffusion colors, making it suitable for applications that require effective light diffusion.
General | |||||
Form | Resin Pellets | ||||
Feature | F1
Non-Chlorinated |
| Non-Brominated & Non- Chlorinated Flame | ||
| |||||
Uses |
|
| |||
Physical | Value | Test Method | |||
Density / Specific Gravity |
1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion |
| UL 746C | |||
Mechanical | Value | Test Method | |||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 85 J/m | ASTM D256 | |||
Notched Izod Impact Strength notched;23 °C notched;-30 °C |
10 kJ/m² 9 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C -30 °C |
10 kJ/m² 9 kJ/m² | ISO 179 1eA |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
54 MPa 57 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
80 % 73 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2400 MPa 2300 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
103 MPa 96 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2400 MPa 2400 MPa |
ASTM D790 ISO 178 |
Thermal | Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 0.4 mm |
V-0 V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm |
850 °C 850 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm |
960 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50
|
136 °C 139 °C
|
ASTM D1525 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
130 °C 120 °C | ASTM D648 |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Value | Test Method |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |
1 What are the product description of Forever's PC polymers?
LUX1932C-XH Polycarbonate (PC) resin is a highly versatile, non-filled, injection moldable grade, suitable for various applications. This non-chlorinated, non-brominated flame retardant PC has an impressive UL-94 V0 rating at 1.5 mm, making it ideal for superior fire safety. Additionally, this grade has excellent flow properties and is UV stabilized, providing extraordinary weathering resistance. LEXAN LUX9430C comes in a range of diffusion colors, making it suitable for applications that require effective light diffusion.
General | |||||
Form | Resin Pellets | ||||
Feature | F1
Non-Chlorinated |
| Non-Brominated & Non- Chlorinated Flame | ||
| |||||
Uses |
|
| |||
Physical | Value | Test Method | |||
Density / Specific Gravity |
1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 | |||
Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | |||
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | |||
UV light, water exposure/immersion |
| UL 746C | |||
Mechanical | Value | Test Method | |||
Izod Impact, Notched 23 °C -30 °C |
100 J/m 85 J/m | ASTM D256 | |||
Notched Izod Impact Strength notched;23 °C notched;-30 °C |
10 kJ/m² 9 kJ/m² | ISO 180/1A |
Charpy Impact, V-Notched 23 °C -30 °C |
10 kJ/m² 9 kJ/m² | ISO 179 1eA |
Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
54 MPa 57 MPa |
ASTM D638 ISO 527 |
Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
80 % 73 % |
ASTM D638 ISO 527 |
Tensile Modulus 50 mm/min 1 mm/min |
2400 MPa 2300 MPa |
ASTM D638 ISO 527 |
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
103 MPa 96 MPa |
ASTM D790 ISO 178 |
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2400 MPa 2400 MPa |
ASTM D790 ISO 178 |
Thermal | Value | Test Method |
UL Recognized ≥ 1.5 mm ≥ 0.4 mm |
V-0 V-2 | UL 94 |
Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm |
850 °C 850 °C | IEC 60695-2-13 |
Glow Wire Flammability Index 3 mm 1.5 mm |
960 °C 960 °C | IEC 60695-2-12 |
Vicat Softening Temperature Rate B/50 Rate B/50
|
136 °C 139 °C
|
ASTM D1525 ISO 306 |
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
130 °C 120 °C | ASTM D648 |
Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
Relative Temp Index, Elec | 130 °C | UL 746B |
Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
Electrical | Value | Test Method |
Comparative Tracking Index, CTI | PLC 3 | UL 746A |
Processing | Nominal Value | |
Drying Temperature<Injection> | 120 °C | |
Drying Time<Injection> | 3 - 4 hrs | |
Drying Time, Cumulative<Injection> | 48 hrs | |
Maximum Moisture Content<Injection> | 0.02 % | |
Melt Temperature<Injection> | 280 - 305 °C | |
Nozzle Temperature<Injection> | 275 - 300 °C | |
Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
Mold Temperature<Injection> | 70 - 95 °C | |
Back Pressure<Injection> | 0.3 - 0.7 MPa | |
Screw Speed<Injection> | 40 - 70 rpm | |
Shot To Cylinder Size<Injection> | 40 - 60 % | |
Vent Depth<Injection> | 0.025 - 0.076 mm |